NASA NTRS2009

Initial Transient in Zn-doped InSb Grown in Microgravity

Three Zn-doped InSb crystals were directionally solidified under microgravity conditions at the International Space Station (ISS) Alpha. The distribution of the Zn was measured using SIMS. A short diffusion-controlled transient, typical for systems with k greater than 1 was demonstrated. Static pressure of approximately 4000 N/m2 was imposed on the melt, to prevent bubble formation and dewetting. Still, partial de-wetting has occurred in one experiment, and apparently has disturbed the diffusive transport of Zn in the melt.

Ostrogorsky, A G.↗

NASA NTRS2009

Dewetting and Segregation of Zn-Doped InSb in Microgravity Experiments

In directional solidification, dewetting is characterized by the lack of contact between the crystal and the crucible walls, due to the existence of a liquid meniscus at the level of the solid-liquid interface. This creates a gap of a few tens of micrometers between the crystal and the crucible. One of the immediate consequences of this phenomenon is the dramatic improvement of the quality of the crystal. This improvement is partly due to the modification of the solid-liquid interface curvature and partly to the absence of sticking and spurious nucleation at the crystal-crucible interface. Dewetting has been, commonly observed during the growth of semiconductors in crucibles under microgravity conditions where it appears to be very stable: the gap between the crystal and the crucible remains constant along several centimetres of growth. The physical models of the phenomenon are well established and they predict that dewetting should not occur in microgravity, if sufficient static pressure is imposed on the melt, pushing it towards the crucible. We present the results of InSb(Zn) solidification experiments conducted at the International Space Station (ISS) where, in spite of a spring exerting a pressure on the liquid, partial dewetting did occur. This surprising result is discussed in terms of force exerted .by the spring on the liquid and of possibility that the spring did not work properly. Furthermore, it appears that the segregation of the Zn was not affected by the occurrence of the dewetting. The data suggest that there was no significant interference of convection with segregation of Zn in InSb.

Ostrogorsky, A. G.↗

NASA NTRS2004

Te-and Zn-Doped InSb Crystals Grown in Microgravity

In 2002, within the SUBSA (Solidification Using a Baffle in Sealed Ampoules) investigation, seven doped InSb crystals were grown in microgravity at the International Space Station. The key goals of the SUBSA investigation are: (a) to clarify the origin of the melt convection in space laboratories; (b) to reduce melt convection to the level which allows reproducible diffusion-controlled segregation; (e) to explore the submerged baffle process and liquid encapsulation in microgravity. 30 crystal growth experiments were conducted in the ground unit, to optimize the design of flight ampoules and to test the transparent SUBSA furnace developed by TecMasters Inc. The specially designed furnace, allowed observation of the crystal growth process (melting, seeding, motion of the solid-liquid interface, etc.). In the summer of 2002, eight crystal growth experiments were conducted in the Microgravity Science Glovebox (MSG) facility at the ISS. Four Te-doped (k = 0.5) and three Zn-doped (k2.9) crystals were grown on undoped seeds. In one experiment, we were not able to seed and grow. The seven grown crystals were sectioned and analyzed using SIMS. The design of the SUBSA ampoules, the segregation data and the video images obtained during the SUBSA flight experiments will be presented and discussed.

Ostrogorsky, A. G.↗

NASA NTRS2001

Space- and Ground-Based Crystal Growth Using a Baffle (CGB)

The composition of semiconductor crystals produced in space by conventional melt-growth processes (directional solidification and zone melting) is affected by minute levels of residual micro-acceleration, which causes natural convection. The residual acceleration has random magnitude, direction and frequency. Therefore, the velocity field in the melt is apriori unpredictable. As a result, the composition of the crystals grown in space can not be predicted and reproduced. The method for directional solidification with a submerged heater or a baffle was developed under NASA sponsorship. The disk-shaped baffle acts as a partition, creating a small melt zone at the solid-liquid interface. As a result, in ground based experiment the level of buoyancy-driven convection at the interface is significantly reduced. In several experiments with Te-doped GaSb, nearly diffusion controlled segregation was achieved.

Ostrogorsky, A. G.↗