DOE OSTI2024

Effects of processing conditions on flash sintering of commercial ZrN

Flash sintering (FS) is a potentially rapid and low-cost manufacturing technique for advanced ceramics. There are still many unknowns about ceramic FS, especially for highly conductive high-temperature ceramics (HTC), which often display decreased bulk conductivity with increasing temperature. This study qualitatively characterizes the flash behavior of highly conductive HTC materials using zirconium nitride (ZrN) as an example. The effects of processing parameters (e.g., DC voltage/electrical field strength, voltage ramp rate, post-flash holding time, mechanical pressure, sample milling, and choice of electrode materials) on ZrN flash behavior are also qualitatively studied and linked to samples microstructure and hardness. It is observed that best densification was achieved using 5 min Spex-milled ZrN powder under 25 MPa of applied pressure and constant 8 V DC. The potential mechanism for ZrN FS and the similarity and difference from FS of conventional oxides like YSZ have been proposed based on experimental observations, and the directions for future research are also pointed out.

Flash Sintering↗
DOE OSTI2023

Reactive flash sintering of TiZrN and TiAlN ternary metal nitrides

Here, this study demonstrated the reactive flash sintering (RFS) for two powder mixtures: TiN-ZrN (both conducting) and AlN-TiN (TiN conducting but AlN insulating), targeting ternary metal nitrides (TMN) of Ti 0.5 Zr 0.5 N and Ti 0.5 Al 0.5 N, respectively. A constant volage and pressure (e.g., 8 V DC, ∼15 MPa) at room temperature triggered the flash (current density up to 27 A/mm 2 ) without pre-heating, and the entire RFS process finished in a few minutes. For TiZrN, the flash was instantaneous whereas for TiAlN, there was a long incubation before the flash followed by a quick and dramatic flash. Both conventional ex situ XRD and in situ synchrotron study had been carried out. They showed a uniform Ti 0.57 Zr 0.43 N solution formed in RFS and persisted upon cooling, while (Ti, Al) N solid solution formed at high temperature was not stable and likely went through a very quick phase separation in the cooling process. The final products from RFS had been characterized using SEM/EDS for microstructure. Both TiZrN and TiAlN were dense. Distribution of Ti, Zr, and N was uniform for TiZrN; for TiAlN, Ti and N distribution was uniform, while association of Al with oxygen was observed. TGA-DSC revealed the onset oxidation temperature for TiZrN was comparable to TiN and ZrN, while it was higher by ∼200 °C for TiAlN, likely due to the formation of Al 2 O 3 . In terms of mechanical properties such as hardness or fracture toughness, forming a single-phase solid solution (like TiZrN) does not offer obvious benefits. while large grain size from RFS seemed to be unfavorable. Future optimization of RFS condition and in-depth study by both experiments and simulation are needed to fully understand the composition-processing-structure-property relationships for such TMN from the reactive flash sintering process.

Flash Sintering↗
DOE OSTI2022

Electrical, thermal, and H 2 O and CO 2 poisoning behaviors of PrNi 0.5 Co 0.5 O 3-δ electrode for intermediate temperature protonic ceramic electrochemical cells

PrNi 0.5 Co 0.5 O 3-δ (PNC) exhibits adequate total electrical conductivity (~300 S/cm at 400–600 °C) and moisture has no significant effect on it. The thermal expansion coefficient of PNC is 17.6 × 10 –6 /K by dilatometry and 18.43 × 10 –6 /K by in situ XRD. PNC also demonstrates chemical stability against H 2 O and CO 2 . However, PNC symmetrical cell over proton-conducting BaZr 0.4 Ce 0.4 Y 0.1 Yb 0.1 O 3-δ (BZCYYb4411) electrolyte shows significant H 2 O and CO 2 poisoning when those are introduced into O 2 –N 2 mixture. In comparison, symmetrical cells with PNC electrode over the oxygen ion conducting Ce 0.9 Gd 0.1 O 2-δ (GDC) electrolyte show no H 2 O and CO 2 poisoning under similar conditions. Here, it is hypothesized that poisoning from H 2 O and CO 2 of the PNC proton conducting symmetrical cell is caused by their adsorption on the BZCYYb4411 electrolyte instead of PNC electrode. Such a hypothesis is supported by the H 2 O and CO 2 adsorption behaviors on PNC and BZCYYb4411 powder surfaces, as measured by temperature programmed desorption (TPD).

08 HYDROGEN↗
DOE OSTI2020

Synthesis and flash sintering of (Hf 1-x Zr x )B 2 solid solution powders

(Hf 1-x Zr x )B 2 solid solution powders were synthesized by two methods. First, solution-based processing of HfCl 4 , ZrCl 4 , sucrose, and H 3 BO 3 was conducted followed by heat treatment in Argon to carry out the carbothermal reduction (CTR) reaction to form the diboride powders. Alternatively, in the so-called borohydride reduction (BHR) method, HfCl 4 , ZrCl 4 and NaBH 4 were mixed in an Argon glove box followed by heat treatment in Argon at 700-1500°C. The synthesized powders were characterized by XRD, SEM, TEM, EDS, and TGA, and the influence of different parameters such as starting composition, heat treatment temperature and time on products characteristics were revealed. Both CTR and BHR solid solution powders were then consolidated within ~5 min in a homemade flash sintering (FS) setup. Here, the composition, microstructure, hardness, and thermal-oxidation properties of flash sintered ceramics were characterized, and the implication of this study and directions for future research were discussed.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Synthesis and Flash Sintering of (Hf1-xZrx)B2 Solid Solution Fine Powders

Fine powders of (Hf1-xZrx)B2 solid solution were synthesized by two methods. In the first one, solution-based processing of HfCl4, ZrCl4, sucrose and H3BO3 was carried out followed by heat treatment (e.g., at 1500 °C for 1 h) in Argon to achieve the carbothermal reduction (CTR) reaction to form the boride solid solution. In the second one, called boron hydride reduction (BHR) method, HfCl4, ZrCl4 and NaBH4 were directly mixed in a glove box followed by heat treatment in Argon at elevated temperatures from 700 to 1500 °C. In addition, the powders synthesized via both methods were flash sintered without sample preheating in a homemade setup. The synthesized powders as well as the flash sintered bulk ceramics were characterized using different techniques including XRD, SEM, EDS, TEM, TGA-DSC, and Vickers hardness test to reveal the inter-relationships between starting materials composition, processing conditions, and the resulting materials microstructure and physical/chemical properties.