On the role of geometrically necessary dislocations in void formation and growth in response to shock loading conditions in wrought and additively manufactured Ta

This study investigates the role of geometrically necessary dislocations (GNDs) and microstructure on void nucleation and growth in wrought and additively manufactured (AM) tantalum subjected to high-strain rate loading. Multi-modal 3D data was collected using TriBeam tomography to calculate GND densities and their spatial relationship to voids. A microstructural comparison between the wrought and AM samples identified distinct void shapes and locations, with intragranular voids and more spherical voids frequently observed in the AM dataset. Results indicate that voids preferentially form at both high-angle grain boundaries and low-angle subgrain boundaries, the latter of which are frequently observed in the AM material. Through a radial distribution analysis of all voids in the datasets, significant GND localization to near-void-surface regions was observed in both samples. 3D crystal plasticity simulations were employed to extend the experimental observations, revealing higher void growth rates in [111] oriented grains when compared to [001] grains. The simulations also suggest that GNDs can be generated as part of the void growth process, with more GND accumulation for growth in a [111] grain than a [001] grain. These findings provide valuable insights into the links between nanoscale void nucleation, mesoscale void growth, and microstructural effects in dynamically loaded tantalum.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Subgrain geometrically necessary dislocation density mapping in spalled Ta in three dimensions

Here, in this work, the intragranular distributions of the densities of geometrically necessary dislocations (GNDs) generated in a polycrystalline tantalum (Ta) sample loaded in shock compression to spall are investigated. The sample studied is a highly resolved three-dimensional (3D) map of the orientations, grain boundary morphology, and voids across a 0.276mm 3 (with sample dimensions of 688.5µm x 669µm x 600µm) region of the microstructure about the spall plane obtained by TriBeam tomography. We present a formulation for calculating the crystallographic screw and edge character GND densities at a material point within body centered cubic (BCC) crystals when provided any number of potential slip systems or modes. Combining the 3D characterization, GND formulation, and a sample containing ≈ 6000 grains, we sought statistically relevant correlations between GND density per grain with grain size, grain orientation, void formation, and proximity from the spall plane. We show that GND density per grain increases with decreasing distance from the spall plane. Most grains had heterogeneously distributed GND densities but were free of any detectable voids, at least within the ≈ 1.5µm resolution of the characterization technique. It is found that the GND density for most grains is insensitive to grain size and grain orientation. Only the fraction of grains with the highest GND densities tended to have a [001] parallel to shock-direction orientation. Intragranular 3D maps of GNDs reveals that grains that contain voids have high GND density concentrations in the intragranular region immediately surrounding the void. The local intragranular GND mapping also showed voids that are connected to grain boundaries preferred to grow into the grain with the larger size, regardless of orientation.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Scan strategies in EBM-printed IN718 and the physics of bulk 3D microstructure development

Three-dimensional (3D) characterization provides opportunities for understanding processing-structure relationships in additively manufactured (AM) materials. Bulk samples of Inconel 718 were fabricated via electron beam melting (EBM) in order to study microstructural development as a function of energy input and beam scan strategy. TriBeam tomography of bulk Inconel 718 microstructures built under steady-state growth conditions reveals the sensitivity of microstructure formation and evolution to machine process parameters. Here, samples manufactured using a narrow range of energy input per unit build area result in varied grain morphologies and crystallographic textures. Using TRUCHAS, a thermal simulation software, the thermal history of bulk scan strategies was predicted, and combined with a calibrated microstructure-processing map to accurately predict bulk grain morphologies. The solidification parameters and the 3D measured nucleation density are used to predict the transition between columnar and equiaxed grain morphologies, providing a process map to guide AM parameter choices to locally control as-printed microstructure. A two-dimensional metric for characterizing bulk grain morphology was also found to agree well with predictions from the process map calibrated by 3D data. Combined with 3D tomography and thermal modelling, the physics of structure development were understood at a new level of detail with respect to the competing processes of grain nucleation and epitaxial growth.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Boundary characterization using 3D mapping of geometrically necessary dislocations in AM Ta microstructure

Additive manufacturing (AM) of high strength metallic materials produces microstructures and defects that deviate substantially from those created through conventional manufacturing methods. It has recently been demonstrated that with application of extreme energy densities, a high-temperature refractory metal, tantalum (Ta), can be printed to a fully dense state with exceptionally low porosity. Here we employ a combination of three-dimensional electron backscattered diffraction (EBSD) TriBeam technology and crystallographic geometrically necessary dislocation (GND) theory to characterize the microstructure and defect boundaries of this unusual AM product. Two-dimensional (2D) EBSD and these three-dimensional (3D) measurements indicate that the microstructure of AM Ta is highly oriented <111> along the build direction, yet at the same time contains large crystallographic orientation gradients that span mm’s across the build. Crystallographic GND density analysis of the 3D microstructure reveals that highly misoriented subboundaries exist within this strongly textured microstructure that have large dislocation densities of 1×10 16 m –2 , just as large as those comprising the high-angle grain boundaries (HAGBs) in the same material. The 3D crystallographic GND density mapping reveals these subboundaries are part of a complex, finely spaced network that extends throughout the entire microstructure. Here, the orientation of these boundaries can be related to the scan strategy used during printing. TEM measurements corroborate an extremely high dislocation density at the microscale and indicate a cell-like dislocation network structure existing in the AM Ta at the sub-μm scale.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Recent Developments in Femtosecond Laser-Enabled TriBeam Systems

Streams of multimodal three-dimensional (3D) and four-dimensional (4D) data are revolutionizing our ability to design and predict the behavior of a broad array of advanced materials systems. Over the last 10 years, a new 3D imaging platform consisting of a femtosecond (fs) pulsed laser coupled with a focused ion beam scanning electron microscope (FIB SEM) has been developed by UC Santa Barbara in collaboration with Thermo Fisher Scientific (formerly FEI). The femtosecond-laser-enabled FIB SEM, called the TriBeam, has become one of the only 3D serial sectioning methods available that can gather millimeter-scaled multimodal datasets at sub-μm voxel resolutions; these length scales are critical for many materials problems. Multimodal chemical, crystallographic, and morphological information can be gathered rapidly on a layer-by-layer basis and reconstructed in 3D. Large (gigabyte to terabyte scale) 3D datasets have been generated for a broad array of materials systems, including metallic alloys, ceramics, biomaterials, polymer- and ceramic-matrix composites, and semiconductors. The research tasks conducted have resulted in a completely new design, operating with a dual-wavelength femtosecond-pulsed laser on a plasma focused ion beam (PFIB) platform.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Multimodal 3D characterization of voids in shock-loaded tantalum: Implications for ductile spallation mechanisms

Predicting the failure of crystalline materials at high strain rates requires knowledge of the underlying failure mechanisms and their dependence on microstructure. However, little experimental consensus exists on the underlying micromechanics of spallation. In this study, a 3D-EBSD characterization experiment is performed on tantalum prior to and after partial spallation by plate impact, which allowed for the statistical assessment of the microstructural neighborhoods surrounding incipient voids. In analyzing the resulting dataset containing 5884 grains and 467 voids, it is observed that the voids were roughly spherical and consistent in size throughout the spalled material. The voids mostly resided at quadruple points, at triple junctions, at grain boundaries, and within grains, in decreasing order of prevalence. Moreover, voids tended to form at grain boundaries with high degrees of plastic incompatibility, growing into the plastically soft grain but orienting primarily with or perpendicular to the loading direction. Here, the statistics from these analyses of 3D microstructural data support dynamic cavitation models for ductile spallation.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Microstructure-Based Estimation of Strength and Ductility Distributions for \(\alpha +\beta \) Titanium Alloys

Titanium alloys are processed to develop a wide range of microstructure configurations and therefore material properties. While these properties are typically measured experimentally, a framework for property prediction could greatly enhance alloy design and manufacturing. In this work, a microstructure-sensitive framework is presented for the prediction of strength and ductility as well as estimates of the bounds in variability for these properties. The framework explicitly considers distributions of microstructure via new approaches for instantiation of structure in synthetic samples. The parametric evaluation strategy, including the finite element simulation package FEpX, is used to create and test virtual polycrystalline samples to evaluate the variability bounds of mechanical properties in Ti-6Al-4V. Critical parameters for the property evaluation framework are provided by measurements of single crystal properties and advanced characterization of microstructure and slip system strengths in 2D and 3D. Property distributions for yield strength and ductility are presented, along with the validation and verification steps undertaken. Comparisons between strain localization and slip activity in virtual samples and in experimental grain-scale strain measurements are also discussed.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Slip delocalization and diffusion mediated carbide formation during fatigue of a nickel-base superalloy

Fatigue crack initiation at high temperatures occurs at microscopic fatigue shear bands that form near twin boundaries in polycrystalline nickel-base superalloys that contain minimal metallurgical defects. The associated dislocation sub-structure is complex and dependent on thermal and mechanical conditions. Here we show the formation of fine-scale carbide precipitates along these fatigue shear bands in a nickel-base superalloy during fatigue above 650 °C. The formation of carbide precipitates is studied using calculations of bulk and pipe diffusion. The contribution of pipe diffusion is observed to be critical in the formation of fine-scale carbides and occurs coincident with the delocalization of slip during fatigue.

36 MATERIALS SCIENCE↗