Engineering topics

Edmonds, Brian J.

Publications and source records attributed to Edmonds, Brian J..

7 records

NASA NTRS2010

The Effect of Composition on the Surface Finish of PS400: A New High Temperature Solid Lubricant Coating

A new composite, multi-constituent, solid lubricant coating, NASA PS400, developed for high temperature tribological applications, exhibits a smoother surface finish after grinding and polishing than its predecessors PS200 and PS300. In this paper, the baseline composition of PS400 is modified to investigate each individual constituent s role on the achievable surface finish through a series of coating deposition, grinding, and polishing experiments. Furthermore, to explore the limits of compositional tailoring for improved tribological performance, several PS400 coatings were doped with additional solid lubricants (graphite, MoS2 and BN) and tribologically tested. The test results clearly showed that, compared to PS300 coatings, PS400 achieves a smoother surface finish via a reduced lubricant content. Coatings prepared with higher than the baseline level (10 wt%) of lubricants exhibited higher final surface roughness than the earlier generation PS300 coatings. Reducing or eliminating the one or both lubricants (fluorides or silver) did not further improve the surface finish suggesting that the current composition of PS400 is near optimal with respect to surface finish. Lastly, attempts to improve the poor initial room temperature tribological behavior of PS400 via the addition of traditional solid lubricants were unsuccessful. Based upon this work and earlier results it is expected that future research will concentrate on developing methods to produce a lubricious glaze on the rubbing surface during break in to ensure that low friction and wear are rapidly achieved.

DellaCorte, Christopher↗

NASA NTRS2010

High-Temperature Solid Lubricant Coating

NASA PS400 is a solid lubricant coating invented for high-temperature tribological applications. This plasma-sprayed coating is a variant of the previously patented PS304 coating, and has been formulated to provide higher density, smoother surface finish, and better dimensional stability. This innovation is a new composite material that provides a means to reduce friction and wear in mechanical components. PS400 is a blend of a nickel-molybdenum binder, chrome oxide hardener, silver lubricant, and barium fluoride/calcium fluoride eutectic lubricant that can either be sprayed or deposited by other means, such as powder metallurgy. The resulting composite material is then finished by grinding and polishing to produce a smooth, self-lubricating surface.

DellaCorte, Christopher↗

NASA NTRS2002

Heat Treatment Used to Strengthen Enabling Coating Technology for Oil-Free Turbomachinery

The PS304 high-temperature solid lubricant coating is a key enabling technology for Oil- Free turbomachinery propulsion and power systems. Breakthroughs in the performance of advanced foil air bearings and improvements in computer-based finite element modeling techniques are the key technologies enabling the development of Oil-Free aircraft engines being pursued by the Oil-Free Turbomachinery team at the NASA Glenn Research Center. PS304 is a plasma spray coating applied to the surface of shafts operating against foil air bearings or in any other component requiring solid lubrication at high temperatures, where conventional materials such as graphite cannot function.

Edmonds, Brian J.↗

NASA NTRS2001

Thermal Processing Effects on the Adhesive Strength of PS304 High Temperature Solid Lubricant Coatings

In this paper the effects of post deposition heat treatments on the cohesive and adhesive strength properties of PS304, a plasma sprayed nickel-chrome based, high temperature solid lubricant coating deposited on stainless steel, are studied. Plasma spray deposited coating samples were exposed in air at temperatures from 432 to 650 C for up to 500 hr to promote residual stress relief, enhance particle to particle bonding and increase coating to substrate bond strength. Coating pull-off strength was measured using a commercial adhesion tester that utilizes 13 mm diameter aluminum pull studs attached to the coating surface with epoxy. Pull off force was automatically recorded and converted to coating pull off strength. As deposited coating samples were also tested as a baseline. The as-deposited (untreated) samples either delaminated at the coating-substrate interface or failed internally (cohesive failure) at about 17 MPa. Samples heat treated at temperatures above 540 C for 100 hr or at 600 C or above for more than 24 hr exhibited strengths above 31 MPa, nearly a two fold increase. Coating failure occurred inside the body of the coating (cohesive failure) for nearly all of the heat-treated samples and only occasionally at the coating substrate interface (adhesive failure). Metallographic analyses of heat-treated coatings indicate that the Nickel-Chromium binder in the PS304 appears to have segregated into two phases, a high nickel matrix phase and a high chromium precipitated phase. Analysis of the precipitates indicates the presence of silicon, a constituent of a flow enhancing additive in the commercial NiCr powder. The exact nature and structure of the precipitate phase is not known. This microstructural change is believed to be partially responsible for the coating strength increase. Diffusion bonding between particles may also be playing a role. Increasing the heat treatment temperature, exposure time or both accelerate the heat treatment process. Preliminary measurements indicate that the heat treatment also results in a one time, permanent coating thickness increase of about 3%. Based upon these results, the incorporation of a heat treatment prior to final finishing has been incorporated in the application process of this coating technology.

DellaCorte, Christopher↗

NASA NTRS1999

Self-Lubricating Composite Containing Chromium Oxide

A self lubricating. friction and wear reducing composite material useful over a wide temperature range of from cryogenic temperature up to about 900 C. contains 60 80 wt. % of particulate Cr2O3, dispersed in a metal binder of a metal alloy containing Cr and at least 50 wt. % of Ni, Cr or a mature of Ni and Cr. It also contains 5-20 wt. % of a fluoride of at least one Group I, Group II or rare earth metal and. optionally, 5-20 wt. % of a low temperature lubricant metal, such as Ag. Au, Pt, Pd, Rh and Cu. This composite exhibits less oxidation instability and less abrasiveness than composites containing chromium carbide, is readily applied using plasma spray and can be ground and polished with a silicon carbide abrasive.

Dellacorte, Christopher↗

NASA NTRS1988

Wear-Resistant, Thermally Conductive Coating

Process makes coating with unusual properties. Coating is copper or copper alloy with controlled dispersion of oxide or carbide particles. Process results in coating that has thermal expansion similar to base material, increased resistance to abrasion when hot, and high thermal conductivity. Coatings resistant to wear used in variety of applications ranging from earth-moving equipment to space vehicles.

Edmonds, Brian J.↗

NASA NTRS1988

Plasma Spraying Of Dense, Rough Bond Coats

Simple modification of plasma torch facilitates spraying of coarse powders. Shape of nozzle changed to obtain decrease in velocity of gas and consequent increase in time particles spend in flame before impact on substrate. Increased residence time allows melting of coarser powders, spraying of which results in rougher bond surfaces.

Miller, Robert A.↗