Characterization of Hanford LAW Phase 3 Glasses
This report provides analyses of glass compositions, wash solution compositions, and Product Consistency Test (PCT) leachate compositions for a series of simulated low-activity waste (LAW) glasses fabricated at the Pacific Northwest National Laboratory (PNNL). These data will be used in the development of improved property/composition models for LAW glass at Hanford. Chemical analyses were performed on a representative sample of each of the quenched and sulfur saturated glasses to allow for comparisons with the targeted compositions. For some of the quenched glasses, measured concentrations of Cr₂O₃, K₂O, Na₂O, P₂O₅, and ZrO₂ were below the targeted values. For some of the sulfur saturated glasses, the measured concentrations of Al₂O₃, Cl⁻, Cr₂O₃, F⁻, K₂O, Na₂O, P₂O₅, V₂O₅, and ZrO₂ were generally low relative to the targeted values. A comparison of the measured compositions of the quenched and sulfur saturated versions of the study glasses showed that the measured concentrations of Al₂O₃, Cl⁻, and F⁻ were lower for most of the sulfur saturated glasses. The measured Cr₂O₃ and K₂O concentrations were markedly lower for the sulfur saturated versions of the glasses as compared to the quenched versions, which may indicate that these elements partitioned to the soluble sulfur salts. A set of modified glasses was received from PNNL later in this study. Chemical analysis showed that these glasses generally met their targeted compositions. The measured SO₃ concentrations were higher for most of the sulfur saturated glasses relative to those of the quenched versions, as expected. Chemical analysis of the wash solutions that resulted from preparation of the sulfur saturated melts identified Cr, K, Na, P, S, and V as the major elements in solution. With the exception of sulfur, this may explain why the measured concentrations of these components in the study glasses were generally below the targeted values. PNNL performed PCTs on quenched and canister centerline cooled (CCC) versions of the study glasses, as well as the modified glasses. The leachates were sent to SRNL for chemical analysis. Minor scatter in the measured values among the triplicate samples for each glass was noted. Several of the study glasses, both quenched and CCC, have NCi values that are greater than the immobilized LAW constraint of 4 g/L for B, Na, and Si.