El Atwani, Osman

Publications and source records attributed to El Atwani, Osman.

16 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2026

Thermal Stability and Ion Irradiation Response of Refined Grained V – 4Cr – 4Ti

Since the 1960’s, there has been interest in V-4Cr-4Ti and similar alloys as candidates for low activation structural materials for advanced nuclear reactors. V-4Cr-4Ti was produced using arc melting and subsequently subjected to large strain extrusion machining to produce a multimodal microstructure largely composed of nanocrystalline and ultrafine grain sizes. In-situ thermal stability of the multimodal V-4Cr-4Ti to 800 °C shows the formation of vanadium carbides with negligible grain growth. In-situ dual-beam 16 KeV He+ and 1 MeV Kr2+ ion irradiation performed at 700 °C to a final dose of ~5 displacements per atom show the formation of small He cavities well distributed throughout the system, with preferential clustering at grain boundaries. This work provides insight into how the increased fraction of grain boundaries affect the simultaneous dual beam ion irradiation response of multimodal V – 4 wt.% Cr – 4 wt.% Ti at elevated temperatures. Analysis of the cavities reveal an areal density of 0.024±0.007 cavities/nm2 and swelling of 0.236% after the dual-beam ion irradiation. Nanoindentation shows a ~50% increase in hardening after the ion irradiation at 700 °C.

TEM↗
DOE OSTI2025

Utilizing machine learning to predict tensile ductility and yield strength of CoNiV-based multi-principal elements alloys

This study explores the use of machine learning (ML) as a computational tool to accelerate the design of multi-principal element alloys (MPEAs) with improved tensile elongation. An ML model was trained using available experimental data from the literature along with theoretically derived features to predict yield strength (YS) and ductility. A subset of ML-predicted compositions—CoNiVFe, CoNiVTi, CoNiVTiFe, and CoCrNiVTi—was synthesized and evaluated through tensile testing. The ML model underpredicted YS by approximately 20–30 % and overpredicted ductility by 60–70 % for Ti-containing alloys. Microstructural analysis revealed that Ti segregation at interdendritic regions contributed to early fracture, leading to discrepancies in ductility predictions. Ti segregation at these regions likely drives the increased YS due to segregation strengthening. In contrast, the CoNiVFe alloy showed good agreement with both experimental YS and elongation, with prediction errors of ∼10.2 % and ∼20.7 %, respectively. Microstructural characterization revealed minimal segregation in this alloy, suggesting that the ML model can reliably predict the properties of alloys with little to no segregation. These findings highlight the capability of ML in predicting YS with good accuracy but underscore its limitations in capturing defect-driven failure mechanisms such as segregation-induced embrittlement.

36 MATERIALS SCIENCE↗
DOE OSTI2025

The Path towards Plasma Facing Components: A Review of State-of-the-art in W-Based Refractory High-Entropy Alloys

Developing advanced materials for plasma-facing components (PFCs) in fusion reactors is a crucial aspect for achieving sustained energy production. Tungsten (W) - based refractory high-entropy alloys (RHEAs) have emerged as promising candidates due to their superior radiation tolerance and high-temperature strength. This review paper will focus on recent advancements in W-based RHEA research, particularly emphasizing the key role of modelling using machine learning (ML) in the stage of discovery by predicting properties for each composition and expediting the identification of optimal RHEA compositions with desired properties. Additionally, the application of additive manufacturing (AM) techniques for fabricating W-based RHEAs is explored, highlighting their advantages for rapid prototyping and multi-compositional sample production in a high throughput manner. The review critically evaluates the current understanding of mechanical properties relevant to PFC applications, including high-temperature strength and ductility. Furthermore, the radiation tolerance of W-based RHEAs under irradiated conditions is discussed. Finally, the validity of current AM-manufactured W-based RHEAs as PFC materials is assessed, and key challenges and opportunities for future research are identified. This review aims to provide a comprehensive overview of W-based RHEAs for fusion applications and their potential to guide the development and validation of advanced refractory high entropy alloys.

Hatler, Caleb [University of Wisconsin-Madison]↗
DOE OSTI2024

Complex dislocation loop networks as natural extensions of the sink efficiency of saturated grain boundaries in irradiated metals

The development of radiation-tolerant structural materials is an essential element for the success of advanced nuclear energy concepts. A proven strategy to increase radiation resistance is to create microstructures with a high density of internal defect sinks, such as grain boundaries (GBs). However, as GBs absorb defects, they undergo internal transformations that limit their ability to capture defects indefinitely. Here, we show that, as the sink efficiency of GBs becomes exhausted with increasing irradiation dose, networks of irradiation loops form in the vicinity of saturated or near-saturated GB, maintaining and even increasing their capacity to continue absorbing defects. The formation of these networks fundamentally changes the driving force for defect absorption at GB, from “chemical” to “elastic.” Using thermally-activated dislocation dynamics simulations, we show that these networks are consistent with experimental measurements of defect densities near GB. Our results point to these networks as a natural continuation of the GB once they exhaust their internal defect absorption capacity.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Investigating microstructural evolution in SolidStir™ extruded oxide dispersion strengthened 14YWT alloy fuel cladding tube

Structural components for extreme environments require advanced materials and manufacturing processes. One such advanced material is oxide dispersion strengthened (ODS) Fe–14 wt.%Cr–3W–0.4Ti–0.3Y 2 O 3 (14YWT), which is developed for components to be used in Gen IV and fusion nuclear reactors. However, the conventional manufacturing processes to produce components, such as fuel cladding tubes, either do not retain the desired microstructural attributes or are costly and less efficient. As a result, a more attractive option is a novel manufacturing process developed on the principle of friction stir welding or processing (FSW/P) and commercially referred to as SolidStir™ Extrusion (SSE). Here this study used the SSE technique to study the manufacturing and microstructural evolution of a fuel cladding tube made of ODS 14YWT alloy. The cladding extrusion by the SSE technique involved the use of ball-milled 14YWT powders with Y, Ti, and O in the solid solution and the use of a specially designed W-25Re-Hf tool for consolidation and extrusion of the powders. A scanning electron microscope (SEM), electron backscattered diffraction (EBSD), and transmission electron microscope (TEM) were utilized for microstructural characterization. A Keyence microscope captured macrostructural photographs of the extruded tube. EBSD examination of the extruded tube on both transverse and longitudinal cross-sections showed the presence of dynamically recrystallized grains and revealed that the average grain size of the transverse cross-section was smaller than that of the longitudinal cross-section. The texture was weak and consisted of some amount of shear texture. The presence of nano-oxide clusters or precipitates of Y, Ti, and O (pyrochlores) in the extruded tube was determined by TEM. Aging heat treatment caused the average precipitate size to decrease and the density to increase compared to the as-processed condition. The results indicated that SSE is a viable tool for manufacturing fuel cladding tubes with the desired microstructural attributes.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

A quinary WTaCrVHf nanocrystalline refractory high-entropy alloy withholding extreme irradiation environments

In the quest of new materials that can withstand severe irradiation and mechanical extremes for advanced applications (e.g. fission & fusion reactors, space applications, etc.), design, prediction and control of advanced materials beyond current material designs become paramount. Here, through a combined experimental and simulation methodology, we design a nanocrystalline refractory high entropy alloy (RHEA) system. Compositions assessed under extreme environments and in situ electron-microscopy reveal both high thermal stability and radiation resistance. We observe grain refinement under heavy ion irradiation and resistance to dual-beam irradiation and helium implantation in the form of low defect generation and evolution, as well as no detectable grain growth. The experimental and modeling results—showing a good agreement—can be applied to design and rapidly assess other alloys subjected to extreme environmental conditions.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Effects of helium cavity size and morphology on the strength of pure titanium

In this study, high-purity α-titanium was implanted with helium to observe cavity morphology – size, number density, and form (i.e., bubbles vs. voids) – effects on materials strength. Increasing implantation temperatures lead to an Arrhenius-type (i.e., exponential) increase in cavity size, a transition from spherical bubbles to faceted voids, and a marked increase in strength (~20–50%). Implanted samples deformed uniformly in contrast to nano-compression of unimplanted or alloyed titanium, but pillars with the largest faceted voids developed a type of bulging localized deformation. Affected voids were repeatedly sheared, becoming rough and shrunken. Dislocation-cavity interactions and the role of helium content within cavities are considered.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Void swelling of conventional and composition engineered HT9 alloys after high-dose self-ion irradiation

Ferritic/martensitic (F/M) steels are being considered as potential structural materials for next generation nuclear reactors, and variants of the alloy HT9 are some of the most promising candidates. In this study, two conventional and two composition engineered HT9 alloys were irradiated using 3.5 MeV Fe 2+ up to 600 peak displacement-per-atom (dpa) at 450 °C. Void swelling and microstructure evolution were characterized for each alloy and compared. The two conventional HT9 alloys (INL and ACO3) showed similar void swelling behavior due to their similar elemental composition and processing conditions. The INL HT9 exhibited a maximum of 2.4% swelling and the ACO3 HT9 showed a maximum of 2.8% swelling at 342 and 393 average local dpa, respectively. On the other hand, the two-composition engineered HT9 alloys with varying N contents (10 ppm for low N and 440 ppm for high N) showed disparate swelling behavior. The low N HT9 exhibited a maximum of 4.6% swelling, while the high N HT9 showed a maximum of 0.7% swelling at 342 average local dpa. Changes in the N content also affected Ni/Si rich G-phase formation. The low N HT9 showed a larger size and lower density of G-phase precipitates compared with the high N HT9 after 600 peak dpa irradiation. This study compares the void swelling behavior of the ion irradiated four current HT9 alloys to extremely high doses, with the void swelling data from neutron irradiated HT9 alloys. Furthermore, the comparison lends critical insights into how well these current alloys can withstand high neutron fluxes in future reactors, especially since the low N and high N HT9 alloys have never been exposed to such high doses before.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Characterization of advanced nuclear materials under extreme environments

The performance of materials under extreme environments poses important fundamental questions about the behavior of condensed matter under far-from-equilibrium conditions. These conditions create challenges in materials design, testing and evaluation. One important aspect of advancing nuclear power is the discovery and investigation of new classes of materials able to withstand the harsh environments in nuclear reactors. However, investigating and understanding the performance of these materials requires sophisticated tools and characterization techniques and skills. Furthermore, the goal of this special issue is to present recent research on the characterization of the response of candidate advanced nuclear materials to extreme environments.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Microstructural and micro-mechanical analysis of 14YWT nanostructured Ferritic alloy after varying thermo-mechanical processing paths into tubing

Microstructural analyses and micro-pillar compression were conducted on 14YWT nanostructured ferritic alloy (NFA) to compare different processing pathways: hydrostatic extrusion and Pilger processing with varying annealing temperatures into thin walled tubing, and after hot extrusion and cross-rolling into a plate. Hydrostatic extrusion at 815 °C resulted in the smallest grain sizes and highest yield strength of 1.20 GPa. Pilger processing with annealing at 800 °C had fine grained regions and bands of coarse grains, leading to a large variation in yield strength of 0.9–1.40 GPa. Higher annealing temperatures of 1200 °C after pilger processing significantly increased the grain size and lowered the yield strength to 1.01 GPa. These tubes showed a stronger (111) crystallographic texture in the normal direction and elongated grains in the extrusion direction. Characterization of the nano-oxides using TEM reveals more numerous, smaller oxides present in tubing processed at lower temperatures. Overall, this work shows NFA tubing after hydrostatic extrusion and pilger processing can lead to fine grained microstructures and texturing leading to higher yield strengths at lower annealing temperatures (e.g. 800 °C).

14YWT↗
DOE OSTI2020

Chemical short-range order in derivative Cr–Ta–Ti–V–W high entropy alloys from the first-principles thermodynamic study

The development of high-entropy alloys (HEAs) focuses on exploring compositional regions in multi-component systems with all alloy elements in equal or near-equal atomic concentrations. Initially it was based on the main idea that high mixing configurational entropy contributions to the alloy free energy could promote the formation of a single solid solution phase. By using the ab-initio based Cluster Expansion (CE) Hamiltonian model constructed for the quinary bcc Cr–Ta–Ti–V–W system in combination with Monte Carlo (MC) simulations, we show that the phase stability and chemical short-range order (SRO) of the equiatomic quinary and five sub-quaternary systems, as well as their derivative alloys, can dramatically change the order–disorder transition temperatures (ODTT) as a function of alloy compositions. In particular, it has been found, that the equiatomic quaternary Ta–Ti–V–W and Cr–Ta–Ti–W alloys had the lowest order–disorder transition temperature (500 K) among all the analysed equiatomic compositions. In all investigated alloy systems, the strongest chemical ordering has been observed between Cr and V, which led to the conclusion that decreasing the concentration of either Cr or V might be beneficial in terms of decreasing the ODTT. It also predicts that increasing concentration of Ti significantly decreases the ODTT. Our analysis of chemical SRO as a function of alloy composition allows to understand the microstructure evolution of HEAs as a function of temperature in excellent agreement with available experimental observations. Importantly, our free energy of mixing and SRO calculations predict that the origin of precipitates formed by Cr- and V-rich in the sub-quaternary Cr–Ta–V–W system is driven by the thermodynamics. The modelling results are in an excellent agreement with experimental observation of Cr and V segregation in the W 0.38 Ta 0.36 Cr 0.15 V 0.11 alloy which in turns shows an exceptional radiation resistance.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

Scientific Development of Core Block and Monolith Materials (FY2020 Progress)

This report presents the status of an effort to investigate welding and joining techniques for microreactor monolith structural materials. Previously reported results have demonstrated the potential to tier weld sub-scale components using electron beam welding. Tier welding has been investigated on larger scale test articles, and results indicate that tier welding is not feasible for larger components due to the penetration depth that is required. Additional techniques to produce full length parts have been examined, including diffusion bonding and gundrilling. Evaluations of these techniques are ongoing, and have shown early success on sub-scale components. These results indicate that while issues still exist for manufacturing microreactor structures, these challenges are better understood and solutions are in development.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2020

Revealing the synergistic effects of sequential and simultaneous dual beam irradiations in tungsten via in-situ TEM

Elucidating the synergistic effects of different energetic beams on the radiation response of nuclear materials is critical for developing an improved methodology for their evaluation when exposed to extreme environments. This article describes in-situ sequential (He implantation followed by Kr irradiation and vice-versa) and simultaneous (heavy ion Kr irradiation and He implantation) dual beam irradiations performed on tungsten at 1223 K. Dislocation loop density, average area, and total loop damage as a function of irradiation history and dose/fluence are quantified. The loop Burgers vectors and cavity damage (cavity density, size and total change in volume) are also determined at the final maximum dose for each condition. The loop damage evolution was different in all cases, with the smallest loop damage observed in the simultaneous experiment. Annihilation of Kr generated dislocation loops during He implantation in the Kr + He experiment was an unanticipated observation that may be explained by the dynamic evolution of dislocation loop sink strengths and time-dependent defect fluxes. Dislocation loop raft formation, denuded zones near extended defects, and cavity damage are compared across the different conditions. The phenomena observed and discussed in this work will stimulate further experimental and computational modeling activities leading to improved fundamental understanding of the irradiation response of nuclear materials under reactor-similar environments.

36 MATERIALS SCIENCE↗
DOE OSTI2020

In-Situ Helium Implantation and TEM Investigation of Radiation Tolerance to Helium Bubble Damage in Equiaxed Nanocrystalline Tungsten and Ultrafine Tungsten-TiC Alloy

The use of ultrafine and nanocrystalline materials is a proposed pathway to mitigate irradiation damage in nuclear fusion components. Here, we examine the radiation tolerance of helium bubble formation in 85 nm (average grain size) nanocrystalline-equiaxed-grained tungsten and an ultrafine tungsten-TiC alloy under extreme low energy helium implantation at 1223 K via in-situ transmission electron microscope (TEM). Helium bubble damage evolution in terms of number density, size, and total volume contribution to grain matrices has been determined as a function of He+ implantation fluence. The outputs were compared to previously published results on severe plastically deformed (SPD) tungsten implanted under the same conditions. Large helium bubbles were formed on the grain boundaries and helium bubble damage evolution profiles are shown to differ among the different materials with less overall damage in the nanocrystalline tungsten. Compared to previous works, the results in this work indicate that the nanocrystalline tungsten should possess a fuzz formation threshold more than one order of magnitude higher than coarse-grained tungsten.

36 MATERIALS SCIENCE↗