Engineering topics
El-Atwani, O.
Publications and source records attributed to El-Atwani, O..
In-situ radiation response of additively manufactured modified Inconel 718 alloys
Here in this study, a novel alloy of modified Inconel 718 produced by laser powder bed fusion is studied before and after in-situ Kr irradiation up to 3 dpa at 200 and 450 °C. Before irradiation, the microstructure consists of dislocation cells having a misorientation angle less than 5° and with an average size of ~500 nm. There are also second phase particles of MC type carbides, Laves phase and oxides such as Y-O, Y-(Ti)-Al-O. While the microstructure consists of stacking fault tetrahedra, faulted and perfect loops after irradiation at 200 °C, dislocation loops are the primary defects at 450 °C. With increasing dose, the size of the defects remains similar at 200 °C while it increases at 450 °C. This has been attributed to the existence of vacancy type defects at 200 °C and the different defect transport mechanisms at different temperatures. Moreover, matrix and second phase particle compositions seem to be similar after irradiation. The sink strengths of the structures have been calculated and superior radiation resistance of this alloy has been attributed to the existence of fine cell boundaries stabilized by the second phase particles produced by additive manufacturing.
Enhanced mechanical properties of additive manufactured Grade 91 steel
High temperature stability of the mechanical properties, including creep behavior, are important factors to consider in certifying additive manufactured (AM) steels for reactor operation. AM-Grade 91 steel, tested at RT is shown to possess high yield strength, strain hardening and ductility even after high temperature aging for extended hours. Enhanced creep resistance at 650 ⁰C is also evident in the AM Grade 91 steel compared to wrought Grade 91 steel tested at the same conditions. In conclusion, the diverse and complex microstructure of this AM steel allows for both enhanced strength and ductility but increases the ductile-to-brittle transition temperature in these steels.
In-situ observation of nano-oxide and defect evolution in 14YWT alloys
Nanostructured ferritic alloys (NFAs) are considered as candidates for structural components in advanced nuclear reactors due to their excellent radiation resistance as a result of a high density of nano-oxides (NOs) in the microstructure. Therefore, gaining an understanding on the stability of NOs under irradiation is crucial. In this study, we have investigated the evolution of defects and NOs in 14YWT NFAs under in-situ Kr ion irradiation at room temperature (RT) and 450°C up to 10 dpa. It has been found that irradiations at 450°C do not create any changes in the NOs, similar to the bulk irradiations. On the other hand, elemental mapping indicates that NOs dissolve mostly after 10 dpa irradiations at RT. Thus, while defects are both annihilated and pinned by NOs at low doses (before the dissolution of NOs), glissile loops start to escape to the foil surface at high doses (after the dissolution of NOs), justifying the significantly low fraction of (111) loops compared to the literature values. Furthermore, high resolution transmission electron microscopy analysis has shown that the NOs are mostly coherent Y 2 Ti 2 O 7 particles with pyrochlore crystal structure after both RT and 450°C irradiations, similar to those observed before irradiation.
Temperature threshold for preferential bubble formation on grain boundaries in tungsten under in-situ helium irradiation
Understanding a material's radiation tolerance requires examining its performance under different irradiation conditions. In this work, we investigate the radiation tolerance in terms of helium bubble damage in tungsten irradiated in-situ with 16 keV helium at 1073 K and 1223 K. Damage evolution represented by helium bubble density, size and total change in volume in the grain matrices and the grain boundaries are quantified as a function of fluence. Preferential large bubble formation and a higher change in volume on the grain boundaries occurred at 1223 K, suggesting faster migration of certain helium-vacancy complexes as confirmed by a diffusion-reaction model.