Engineering topics
Ellis, Megan E.
Publications and source records attributed to Ellis, Megan E..
Unlocking Larger Scales and Aspect Ratios in 3D Printed Glass: Coupling Active Mixing and UV Curing for Advanced Printability and Crack Resistance
Recent developments in additive manufacturing (AM) of glass via silica-filled inks have facilitated fabrication of previously unattainable geometries and compositions. However, the maximum processable size of 15 mm limits the use of these prints in applications such as optics. A key limitation lies in the trade-off between material printability and green strength: increasing silica content in the feedstock improves crack resistance and reduces shrinkage but results in dramatic changes in viscoelastic properties that hinder flowability. Here, this paper presents a novel approach that offers expanded versatility in processable size, feedstock formulation, and printing. Described here is a direct ink writing (DIW) system coupled with an active high-shear micromixer and UV light source, capable of simultaneously printing multiple inks with a wide range of rheological properties. Choice of silica sourc, solvent, UV-curable binder, and dispersant is used to tune the ink rheology and improve printability and mechanical properties. Imparting high shear with the micromixer while UV-curing the extrudate allows for increased ink viscosities and reduced nozzle diameters, enabling printing finer feature sizes. With these advances, thin-walled high-aspect ratio structures and a crack-free glass disk measuring 44 mm in diameter are demonstrated, an increase of 3× in the greatest dimension compared to current state-of-the-art.
3D printing of void-free glass monoliths: rheological and geometric considerations
Direct ink writing (DIW) is a versatile additive manufacturing technique capable of printing 3D architectures from a broad range of materials. The key advantage of DIW is the ability to spatially control both the architecture and the composition of the printed part, which enables the production of components with previously unachievable combinations of functionalities. One emergent application space for DIW has been in additively manufactured glass optics, where a “green body” is patterned layer-by-layer by extruding a silica-based slurry through a microfluidic nozzle and then thermally consolidated to transparent glass. A critical aspect of the process is ensuring that the printed part is completely free of voids that can occur in the interstitial spaces between the extruded filaments. This outcome is governed by the interplay between ink rheology and strains imposed by the printing process and geometric packing of the filaments. Here, we explore the strain- and rate-dependent deformation events in the DIW process to determine conditions that enable the printing of void-free monoliths without sacrificing shape fidelity. We focus on yield stress fluids consisting of fumed silica nanoparticles dispersed in organic solvents at varied volume fractions to control the rheological properties. We investigate the printability of these ink materials as a function of print process variables and devise the appropriate dimensionless parameters that capture the geometry-dependent and rate-dependent effects on the deformation of the extruded ink. Lastly, we use these scaling arguments to construct a phase diagram for void-free monolith printability.
3D-Printable Fluoropolymer Gas Diffusion Layers for CO 2 Electroreduction
The electrosynthesis of value-added multicarbon products from CO 2 is a promising strategy to shift chemical production away from fossil fuels. Particularly important is the rational design of gas diffusion electrode (GDE) assemblies to react selectively, at scale, and at high rates. However, the understanding of the gas diffusion layer (GDL) in these assemblies is limited for the CO 2 reduction reaction (CO 2 RR): particularly important, but incompletely understood, is how the GDL modulates product distributions of catalysts operating in high current density regimes > 300 mA cm -2 . Here, 3D-printable fluoropolymer GDLs with tunable microporosity and structure are reported and probe the effects of permeance, microstructural porosity, macrostructure, and surface morphology. Under a given choice of applied electrochemical potential and electrolyte, a 100× increase in the C 2 H 4 :CO ratio due to GDL surface morphology design over a homogeneously porous equivalent and a 1.8× increase in the C 2 H 4 partial current density due to a pyramidal macrostructure are observed. Overall, these findings offer routes to improve CO 2 RR GDEs as a platform for 3D catalyst design.