Erdewyk, Michael Van | Search NASA

DOE OSTI2022

Molecular Reaction Imaging of a Surface Recombination Process Explains Performance Variation Among Smooth MoS 2 Photoelectrodes

Transition metal dichalcogenides (TMD) such as WSe 2 and MoS 2 are highly efficient and stable light absorbers in TMD∣I − ,I 3 − ∣Pt liquid junction solar cells. It is generally accepted that TMD crystals with a large fraction of exposed edge sites exhibit lower power conversion efficiencies (PCEs) than apparently smooth crystals. However, one open question is why does the PCE vary significantly from one crystal to another? Answering this critical question could lead to robust syntheses for high quality and uniform TMD samples. In this work, we apply nanoscale photoelectrochemical microscopy techniques to study n-type TMD nanoflake∣I − ,I 3 − ∣Pt cells. Using a combination of near-diffraction-limited photocurrent mapping and molecular reaction imaging techniques, we reveal a previously hidden surface recombination process: photogenerated holes in hidden p-type domains travel micron-scale distances parallel to the solid/liquid interface and preferentially react with iodide at step-edges. The overall efficiency of the nanoflake, as evidenced from whole nanoflake-level photoelectrochemical measurements, is dictated by the size, efficiency, and location of n- and p-type domains. Furthermore, these results provide a unifying view of efficiency losses in smooth TMD photoelectrodes and open the possibility to design electrode architectures that leverage the long-range lateral charge transport property for photoelectrocatalysis.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Single Nanoflake Photoelectrochemistry Reveals Intrananoflake Doping Heterogeneity That Explains Ensemble-Level Photoelectrochemical Behavior

Transition metal dichalcogenide (TMD) nanoflake thin films are attractive electrode materials for photoelectrochemical (PEC) solar energy conversion and sensing applications, but their photocurrent quantum yields are generally lower than those of bulk TMD electrodes. The poor PEC performance has been primarily attributed to enhanced charge carrier recombination at exposed defect and edge sites introduced by the exfoliation process. Here, a single nanoflake PEC approach reveals how an alternative effect, doping heterogeneity, limits ensemble-level PEC performance. Photocurrent mapping and local photocurrent–potential (i–E) measurements of MoS 2 nanoflakes exfoliated from naturally occurring bulk crystals revealed the presence of n- and p-type domains within the same nanoflake. Interestingly, the n- and p-type domains in the natural MoS 2 nanoflakes were equally efficient for iodide oxidation and tri-iodide reduction (IQE values exceed 80%). At the single domain-level, the natural MoS 2 nanoflakes were nearly as efficient as nanoflakes exfoliated from synthetic n-type MoS 2 crystals. Single domain-level i–E measurements explain why natural MoS 2 nanoflakes exhibit an n-type to p-type photocurrent switching effect in ensemble-level measurements: the n- and p-type diode currents from individual domains oppose each other upon illuminating the entire nanoflake, resulting in zero photocurrent at the switching potential. Furthermore, the doping heterogeneity effect is likely due to nonideal stoichiometry, where p-type domains are S-rich according to XPS measurements. Although this doping heterogeneity effect limits photoanode or photocathode performance, these findings open the possibility to synthesize efficient TMD nanoflake photocatalysts with well-defined lateral p- and n-type domains for enhanced charge separation.

14 SOLAR ENERGY↗