Commissioning of a two-target DC cylindrical magnetron sputter coater for depositing Nb 3 Sn film on Nb superconducting radiofrequency cavities

A DC cylindrical magnetron sputter coater was commissioned and used to coat Nb 2.6 GHz superconducting radiofrequency (SRF) cavity with Nb 3 Sn. The sputter coater has two identical cylindrical magnetrons that can move, with a controlled speed, along the axis of the SRF cavity to coat the inside surface of the cavity. The design of the sputter coater is discussed, along with its performance. Initially, a sample holder that allows coating on flat substrates at positions similar to the equator and beam tubes of a 2.6 GHz SRF cavity was used to test conditions for fabricating Nb 3 Sn layers. Multilayers of Nb and Sn were sequentially sputtered on flat Nb and sapphire substrates mounted on the equivalent positions of the cavity's beam tubes and the equator using the two identical cylindrical magnetrons. Then, the Nb/Sn multilayers were annealed at 950 °C for 3 h. Here, the ~1.2 μm thick Nb 3 Sn film did not show any other Nb–Sn compounds and had a superconducting transition temperature of 17.61–17.76 K. The 2.6 GHz SRF cavity was coated using similar conditions as flat samples. Cryogenic RF testing of the Nb 3 Sn-coated cavity demonstrated a quality factor of 3.2 × 10 8 at an accelerating gradient of 5 MV/m at 4.4 K.

43 PARTICLE ACCELERATORS↗
DOE OSTI2023

Selective thermal evolution of native oxide layer in Nb and Nb$_3$Sn-coated SRF grade Nb: An in-situ angular XPS study

This contribution discusses the results of an in-situ angular XPS study on the thermal evolution of the native oxide layer on Nb3Sn and pure Nb. XPS data were recorded with conventional spectrometers using an AlK(alpha) X-ray source for spectra collected up to 600 C, and an MgK(Alpha) X-rays source for temperatures above 600 C. The effect of the thickness, composition, and thermal stability of that oxide layer is relevant to understanding the functional properties of superconducting radiofrequency (SRF) cavities used in particle accelerators. There is a consensus that oxide plays a role in surface resistance (Rs). The focus of this study is Nb3Sn, which is a promising material that is used in the manufacturing of superconducting radiofrequency (SRF) cavities as well as in quantum sensing, and pure Nb, which was included in the study for comparison. The thermal evolution of the oxide layer in these two materials is found to be quite different, which is ascribed to the influence of the Sn atom on the reactivity of the Nb atom in Nb3Sn films. Nb and Sn atoms in this intermetallic solid have different electronegativity, and the Sn atom can reduce electron density around neighbouring Nb atoms in the solid, thus reducing their reactivity for oxygen. This is shown in the thickness, composition, and thermal stability of the oxide layer formed on Nb3Sn. The XPS spectra were complemented by grazing incident XRD patterns collected using the ESRF synchrotron radiation facility. The results discussed herein shed light on oxide evolution in the Nb3Sn compound and guide its processing for potential applications of the Nb3Sn-based SRF cavities in accelerators and other superconducting devices.

Cano, Arely↗
DOE OSTI2023

Fabrication of superconducting Nb 3 Sn film by Co-sputtering

High-efficiency SRF cavities are the key technology to construct cost-effective CW SRF accelerators. Improvements in the efficiency of SRF cavities are realized by using novel materials, such as niobium-tin. Advances in niobium-tin coatings on the inner surface of SRF cavities showed the potential for this material to increase the operating temperature of the SRF cavity to above 4 K, leading to significant reduction of the capital and operating cost of SRF accelerators. Among the techniques used to apply the niobium-tin coating to the surface of the SRF cavity is sputtering. Old Dominion University, Jefferson Lab, and Fermilab are collaborating on developing an optimized niobium-tin coating of the inside surface of niobium SRF cavities using a recently-developed cylindrical sputtering system. This research will result in optimized sputtering coating techniques leading to high efficiency SRF structures.

42 ENGINEERING↗
DOE OSTI2022

Effect of substrate temperature on the growth of Nb 3 Sn film on Nb by multilayer sputtering

Here, we report on the fabrication of niobium tin (Nb 3 Sn) films by multilayer sequential sputtering on niobium at substrate temperatures ranging from room temperature to 250 °C. The multilayers were then annealed inside a separate vacuum furnace at 950 °C for 3 h. The material properties of the films were characterized by X-ray diffraction, scanning electron microscopy, energy-dispersive X-ray spectroscopy, atomic force microscopy, and transmission electron microscopy. The superconducting properties of the films were studied by four-point probe resistivity measurements from room temperature to below the superconducting critical temperature T c . The highest film T c was 17.76 K, obtained when the multilayers were deposited at room temperature. When the deposition temperature was raised to 250 °C, a significant reduction in voids was achieved while the film's T c was 17.58 K.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Effect of substrate temperature on the growth of Nb$_3$Sn film on Nb by multilayer sputtering

Nb3Sn films were fabricated by multilayer sequential sputtering on Nb substrates at substrate temperatures ranging from room temperature to 250 °C. The film material properties were characterized by X-ray diffraction, scanning electron microscopy, energy-dispersive X-ray spectroscopy, atomic force microscopy, and transmission electron microscopy. The films’ superconducting properties were studied by four-point probe resistivity measurements from room temperature to below the superconducting critical temperature Tc. The highest Tc was17.76 K, when the multilayers were deposited at room temperature. A superconducting Nb3Sn thin film with a smoother surface morphology but a lower Tc of 17.58 K was obtained on the film deposited at a substrate temperature of 250 °C.

Sayeed, Md. Nizam↗
DOE OSTI2021

Investigations Towards Ultra-Low Cost Nb 3 Sn SRF Fabrication via Melt Casted Bronze Route Processing

Here, a novel approach to fabricating Nb 3 Sn SRF cavities and other RF components using an ultra-low-cost melt casting fabrication process has been investigated. This simple, low cost melt casting technique has the potential to be used to fabricate nearly any superconducting Nb3Sn structure using either the Bronze Route (BR), Internal Tin (IT), External Tin (ET) processes as well as normal conducting pure copper (Cu) cavities. Most of the heat treated samples that were examined using SEM/EDX seemed to show a reasonable correlation of T c onset and transition width (ΔT c ) of the ingots initial/starting Sn content to the desired stoichiometric Nb 3 Sn phase, where the lower starting Sn content coupons resulted in lower T c 's with broader transition widths and the higher starting Sn coupons resulted in higher T c 's with narrower ΔT c ’s. The best samples had T c onsets ~17-18 K and ΔT c 's < 2 K. Two samples were further tested for RF surface resistance (R s ) and Quality Factor (Q) at JLAB. Here, these RF measurements were performed at 7.4 GHz using a calorimetric technique and showed two transitions, one at ~ 8 K and another at ~ 14 K; values of R s were at least two orders of magnitude higher than similar high quality Nb 3 Sn films directly deposited substrates by JLAB and with another superconducting transition close to the superconducting transition temperature of niobium. Substantial improvements in the processing variables ranging from higher quality of the initial ingots with higher Sn content, to better electropolishing and reaction heat treatment regimens will be necessary to realize improved RF performance metrics.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
DOE OSTI2021

Properties of Nb3Sn films fabricated by magnetron sputtering from a single target

Superconducting Nb3Sn films were fabricated on sapphire and fine grain Nb substrates by magnetron sputtering from a single stoichiometric Nb3Sn target. The structural, morphological and superconducting properties of the films annealed for 24 h at temperatures of 800-1000 {\deg}C were investigated. The effect of the annealing time at 1000 {\deg}C was examined for 1, 12, and 24 h. The film properties were characterized by X-ray diffraction, scanning electron microscopy, atomic force microscopy, energy dispersive X-ray spectroscopy, and Raman spectroscopy. The DC superconducting properties of the films were characterized by a four-point probe measurement down to cryogenic temperatures. The RF surface resistance of films was measured over a temperature range of 6-23 K using a 7.4 GHz sapphire-loaded Nb cavity. As-deposited Nb3Sn films on sapphire had a superconducting critical temperature of 17.21 K, which improved to 17.83 K when the film was annealed at 800 {\deg}C for 24 h. For the films annealed at 1000 {\deg}C, the surface Sn content was reduced to ~11.3 % for an annealing time of 12 h and to ~4.1 % for an annealing time of 24 h. The Raman spectra of the films confirmed the microstructural evolution after annealing. The RF superconducting critical temperature of the as-deposited Nb3Sn films on Nb was 16.02 K, which increased to 17.44 K when the film was annealed at 800 {\deg}C for 24 h.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
DOE OSTI2021

Microstructural and Superconducting Radiofrequency Properties of Multilayer Sequentially Sputtered Nb 3 Sn films

Nb 3 Sn is considered as a potential candidate for superconducting radiofrequency cavities for particle acceleration due to its higher transition temperature of 18.3 K and higher superheating field of 400 mT. Nb 3 Sn films can be grown inside the surface of a Nb cavity by sequentially sputtering multiple layers of Nb and Sn thin films followed by annealing at 950 °C for 3 h. We report on the properties of Nb 3 Sn films grown on Nb substrates by magnetron sputtering. The films’ crystal structure, surface morphology, and composition were characterized by X-ray diffraction, scanning electron microscopy, and energy-dispersive X-ray spectroscopy. The films had a polycrystalline Nb 3 Sn structure with a fine-grain surface and an atomic Sn composition of ~23%. The RF surface resistance of the films was measured for different temperatures at 7.4 GHz to understand the feasibility of this method for the SRF application. The RF surface resistance of the films was 5 mΩ at 12 K, which is about 2 orders of magnitude higher than 60 μΩ previously measured in Nb 3 Sn films grown by Sn vapor diffusion. Finally, the sputtered film had a superconducting transition at 17.2 K, which is also lower than 17.9 K observed in Nb 3 Sn film prepared by vapor diffusion.

43 PARTICLE ACCELERATORS↗
DOE OSTI2020

β = 0.61 & 0.92 Systems for PIP-II

State-of-the-art surface treatments for SRF cavities (EP/BCP, 120C baking, 75-120C baking, N-doping) applied to 650 MHz cavities

43 PARTICLE ACCELERATORS↗