DOE OSTI2024

Materials Characterization, Prediction, and Control Project: Summary Report on Material Characterization, Part 1

The Pacific Northwest National Laboratory (PNNL) undertook the Materials Characterization, Prediction, and Control (MCPC) Laboratory Directed Research and Development Project to advance understanding of nuclear material processing and enable multifold acceleration in the development and qualification of new material systems in national security and advanced energy applications (Smith 2021). The MCPC Project executed research across three scientific vertices—material characterization, predictive modeling, and data analytics—with extensive support by a data curation and management team. The central technical objective in the MCPC Project was to improve the prediction and characterization of the process-structure-property relationships within the microstructurally refined region of stainless-steel samples prepared utilizing friction stir processing (FSP). Application of the FSP technique is well established at PNNL within the Solid Phase Processing capability through many years of investment across a range of materials and applications (PNNL 2024). Three distinct rounds of FSP experiments were performed by the experimental team, producing replicate samples utilizing across different nominal processing conditions (Condition IDs) listed in Table 1. The starting material on which FSP was applied was commercially available unprocessed stainless-steel type 316L material. Chosen processing conditions were very diverse, and some were intentionally chosen to produce defects. Several samples experienced tool breakage during experimentation, so a full set of three replicates was not produced for every nominal processing condition.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Decoupling of strain and temperature effects on microstructural evolution during high shear strain deformation

The interplay between defect generation by shear strain and defect annihilation by local heating is difficult to predict in shear-assisted processing techniques. In this study, we decoupled the effects of high shear strain and external heating in an immiscible Cu-Nb alloy using a pin-on-disk tribometer to mimic the microstructural evolution of material during solid-phase processing. The change in sub-surface deformation, strain distribution, and redistribution of the second phase as a function of temperature were examined using transmission electron microscopy and atom probe tomography. Zener-Hollomon parameter is used to semi-quantify the deformation of Cu-Nb alloys as a function of strain and temperature.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Thermal Stability and Mechanical Properties of Cold-Sprayed Nickel-Yttria Coating

The microstructural evolution under the extreme environments imposed during cold spray deposition of cermet coatings and the microstructural recovery during post-processing annealing treatments is rather complex and not well understood. Here, Ni-Yttria cermet coatings on an SS304 substrate were produced using cold spray technique, resulting in a bimodal grain structure. The grain growth, phase stability, hardness, and wear properties are observed in as-deposited and annealed (at 400 °C) Ni-Yttria and pure Ni coatings. A multimodal microstructural characterization using electron microscopy, and atom probe tomography shows the structural and compositional stability of yttria particles and Ni grains. A fragmentation of Y-rich particles and dispersion in Ni was observed, however, no forced mixing/dissolution of Y in Ni is detected. Nano-yttria dispersed within the Ni grains slowed the grain growth during annealing. After annealing, Yttria reinforced coating was 1.5 times harder and showed better thermal and mechanical stability compared to the Ni coating.

Gwalani, Bharat↗

DOE OSTI2022

A Finite Difference Analysis of the Effect of Graphene Additions on the Electrical Conductivity of Polycrystalline Copper

A finite-difference method was used to explore the effect of graphene on the bulk electrical conductivity of copper-graphene composites. In this capacity, grain orientation information from pure copper and copper-graphene composites were used to generate synthetic 3D microstructures. The electrical conductivity of these microstructures were calculated using the finite difference method assuming different average grain sizes. From these calculations, we demonstrate that when high-conductivity grain boundaries are present within the microstructure arising from the presence of graphene, an increase in the bulk electrical conductivity is observed. On the other hand, the difference in textures between copper and copper-graphene composites may not account for a significant difference in bulk electrical conductivity. In comparison, the copper grain size has a considerably larger effect on electrical conductivity as previously anticipated. This is one of the first demonstrations of a physical basis for enhanced conductivity composites and presents pathways for further investigations on the effects of composite microstructural features, material interfaces and graphene content on electrical performance.

Frazier, William E.↗

DOE OSTI2021

Extrusion of Unhomogenized Castings of 7075 Aluminum via ShAPE

Extrusion of unhomogenized castings of 7075 aluminum (Al) alloy has been accomplished using shear assisted processing and extrusion (ShAPE). The simultaneous plastic deformation and heat generation during ShAPE rapidly fracture and dissolve interdendritic and intragranular secondary phases of Al-Zn-Mg-Cu, accomplishing homogenization in seconds rather than many hours in a furnace prior to extrusion. ShAPE thereby eliminates the energy-intensive and time-consuming homogenization step required to prepare as-cast microstructures for conventional extrusion. Concurrently, extensive grain refinement occurs due to gradient activation of dynamic recrystallization during ShAPE, which facilitates a threefold increase in extrusion speed compared to the conventional extrusion method. Evident enhancement of the mechanical properties of ShAPE+T6 samples is achieved, compared to the ASTM standard values for conventional extrusion products. The microstructural evolution pathway, involving the processes of grain refinement and secondary particle dissolution, is explained using scanning and transmission electron microscopy.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Multimodal Analysis of Spatially Heterogeneous Microstructural Refinement and Softening Mechanisms in Three-Pass Friction Stir Processed Al4Si Alloy

Multiple thermally and thermomechanically induced microstructural refinement mechanisms can be activated in metallic alloys when subjected to solid phase processing methods such as friction stir processing (FSP). In this work, we provide detailed descriptions of the relationship between region-specific microstructural refinement mechanisms and the variation in microhardness, through a systematic and multimodal microstructural characterization of an FSP-processed 75% cold-rolled Al-4 at.% Si model binary alloy. Spatially resolved high-energy synchrotron X-ray diffraction, electron backscattered diffraction, and scanning transmission electron microscopy were used to understand the spatially heterogeneous microstructural evolution due to FSP. Results provide insights into how mechanisms such as static recovery, static recrystallization, dynamic recovery and recrystallization, geometric and continuous dynamic recrystallization, and particle-stimulated static or dynamic grain nucleation may occur heterogeneously in the microstructure as a function of the distance from the stir zone in processed alloys, directly influencing the degree of softening. The systematic analysis of microstructures and hardness in the FSP-processed model binary alloy given in this work highlights the rich microstructural domains that can be uniquely harnessed through solid phase processing of metallic alloys.

Al4Si, Friction Stir Processing, Geometric Dynamic↗

DOE OSTI2021

Shear Assisted Processing and Extrusion (ShAPE) of Aluminum Alloy 7075, 2024, and Al-12.4TM

The most common aluminum alloys utilized in the aerospace industry are 7075 and 2024 due to their high strength-to-weight ratio compared to advanced high strength steels and other aluminum alloys. Despite excellent performance, these aluminum alloys have seen limited use outside of the aerospace industry due in part to high cost. If high-performance aluminum extrusions could be made more cost effectively by eliminating energy intensive process steps typical of conventional extrusion, then numerous opportunities exist for more widespread adoption. A key reason for the high cost of 7075 and 2024 extrusions (25-75% higher than 6061) is their slow extrusion speed. 7075 and 2024 are limited to 2 m/min and 3.5 m/min respectively, in contrast to 6061 which can be extruded at 20–80 m/min. In addition to slow speed, aluminum alloys require numerous thermal treatments throughout the extrusion process including homogenization and pre-heating prior to extrusion, and solution heat treating and artificial aging after extrusion. Each of these steps contribute to the total energy consumed during manufacturing of extruded components. This project investigates the use of ShAPE to improve extrusion speed and reduce, or even eliminate, the typical thermal treatments for high strength aluminum alloys, all while improving material performance. The overarching goal of this project was to demonstrate that Shear Assisted Processing and Extrusion (ShAPE) can manufacture high-performance aluminum alloy tubing with lower manufacturing energy and improved mechanical properties compared to conventional extrusion. Unlike conventional extrusion where the billet is rammed against a stationary die using a strictly linear motion, the ShAPE process superimposes a rotational shear force by spinning the die while the billet is plunged. Compared to conventional linear extrusion, the ShAPE process imparts significantly more strain into the feedstock material, which enables the formation of novel microstructures. These microstructures manifest an array of property and process improvements for extrusion of high-performance aluminum alloys. The following accomplishments were achieved for this project: Extrusion of 7075 at 12.2 meters/min compared to 2 meters/min for conventional extrusion; Elimination of 7075 billet homogenization (430 °C for 20 hours) which is required prior to conventional extrusion; Elimination of 7075 billet pre-heating (400 °C for 1 hour) in a separate furnace which is required prior to conventional extrusion; Achieved 7075-T6with yield strength = 595 MPa, ultimate tensile strength = 531MPa, and elongation = 17.4% for extrusions made from unhomogenized billets. Exceeds the ASTM and ASM standard, and typical industry values; Achieved 7075-T5 (i.e., no solution heat treatment) with yield strength = 588 MPa, ultimate tensile strength = 535 MPa, and elongation = 14.8% for extrusions made from homogenized billets; Extrusion of 2024 at 7.4 meters/min compared to 3.5 meters/min for conventional extrusion; Achieved 2024-T8510 yield strength = 522 MPa, ultimate strength = 510MPa, and elongation = 7.1% for extrusions made from wrought billets. Exceeds the ASTM and ASM standard, and typical industry values; Extrusion of Al-12.4TM high-performance aluminum powder directly into tubing, in a single step, which eliminates process steps typical of powder metallurgy extrusion.

36 MATERIALS SCIENCE↗