Development of Stable Solid Oxide Electrolysis Cells for Low-Cost Hydrogen Production
The project objective was to demonstrate a solid oxide cell-based steam electrolysis stack that exhibits robustness, reliability, endurance, hydrogen purity, and produces hydrogen at elevated pressure of 2 to 3 bar. Innovative materials and processing methods were evaluated to improve degradation characteristics. Performance improvement focused on nearly all layers involved in the cell and stack assembly. Primary attention was paid to zirconia-ceria interface resistance control via sintering optimization and decrease in degradation from the oxygen electrode by evaluating low strontium (Sr) or Sr-free composition for both the oxygen electrode and current collection layer. Stack robustness was addressed by validating redox tolerance of fuel electrode, confirming capability of cells to survive repeated thermal cycles, studying the effect of pressure on performance and degradation, evaluating the effect of contamination on fuel and oxygen electrode performance and degradation, and identifying mitigation strategies to improve performance. The characterization included evaluation of electrochemical performance and stability followed by microstructural analysis. At the cell level, performance and stability improvements were achieved by incorporating a Sr-free oxygen electrode and a denser oxygen electrode barrier layer. At the stack level, pressurized operation reduces demand on first stage compression, the redox tolerant fuel electrode mitigates risk from service interruptions, and improvements to interconnect coating alleviate chromium (Cr) contamination effects. The denser barrier layer was achieved by adding a sintering aid to the samaria-doped ceria (SDC) composition that reduced sintering temperature by 150 °C. The resulting density was on par with the baseline SDC barrier layer density and the lower sintering temperature resulted in less resistive phase formation during sintering. Button cell tests did not demonstrate a change in performance when exposed to silicon (Si) or manganese (Mn) impurities to the fuel electrode and Cr impurity to the oxygen electrode. More detailed study however is warranted. The project addressed SOEC performance and stability at the cell and stack levels through a systematic approach to known sources of degradation that were combined and tested in three stack tests using an electrolyte supported cell design to allow for evaluation of a variety of fuel and oxygen electrode compositions. STK-82 and STK-83 had identical compositions. STK-100 incorporated the best materials and processing variables developed under this and concurrent projects, and was tested at elevated pressure in steam electrolysis. • STK-82 recovered performance after redox and thermal cycling, demonstrating the robustness of the stack and seals. It exhibited stable performance in testing for 500 hours in SOEC mode, followed by 300 hours of cycling between SOEC and SOFC tests. Degradation during SOEC operation was 1.8 %/ 1,000 hours. • STK-83 generated hydrogen at >80% steam conversion, and oxygen above 98.5 % purity during pressurized operation. Both hydrogen and oxygen were generated at 3 barg pressure without the use of a pressure vessel. In addition to balanced pressure, electrolysis operation at 1 bar differential pressure across anode and cathode was also demonstrated to substantial the robustness of the cell and seal. • STK-100 measured at initial ambient pressure conditions showed an area specific resistance of 1.1 ohm-cm 2 , and STK-83 had 1.3 ohm-cm 2 .