Engineering topics
Publications and source records attributed to Espitia, Jose Ali.
A product includes a solid state electrolyte particle coated with a coating consisting essentially of metal oxide. A method includes depositing a coating on a solid state electrolyte particle by atomic layer deposition. A method includes fabricating a product using a plurality of solid state electrolyte particles coated with a coating consisting essentially of metal oxide.
Garnet-type solid electrolytes, such as Li 6.4 La 3 Zr 1.4 Ta 0.6 O 12 (LLZTO), are promising materials for solid-state batteries, but processing remains a challenge, in part due to the high sintering temperature required for densification. Additionally, this temperature can be lowered by decreasing the initial particle size via solvent-assisted ball milling, but the relationship between solvent choice, particle properties, sintering behavior, and ionic conductivity is not well understood. In this work, we systematically explore these parameters, showing that milling in commonly used protic solvents, such as alcohols, effectively decreases the particle size but results in lithium loss (through Li + /H + exchange) that leads to poor sintering. By contrast, milling in aprotic solvents with surfactant reduces the particle size to ~220 nm without lithium loss, enabling the fabrication of dense samples (5.1 g/cm 3 ) with good ionic conductivity (0.43 mS/cm at 25 °C) at a lower sintering temperature (1000 °C). We compare ionic conductivities and activation energies for samples prepared with different particle sizes and sintering temperatures and use multiphase-field simulations to identify the mass transport and microstructural mechanisms responsible for the observed sintering dependence on particle size. These results further clarify the relationship between processing parameters and performance and represent important progress toward overcoming fabrication challenges for these materials.
Lithium ion batteries have become a common use in most electronic devices and transportation. However, the use of liquid electrolytes poses a serious safe hazard due to their high flammability. The narrow operating temperature and voltage windows also limit further improvement of the energy density.Solid-state lithium batteries with the use of more stable and safer solid electrolyte have garnered much attention and could be the future choice for battery technology. A promising potential candidate for the solid electrolyte component is the garnet type Li 7 La 3 Zr 2 O 12 (LLZO) ceramic material since it possesses high ionic conductivity at room temperature and enables the use of high capacity lithium anode and high voltage/capacity cathodes.However, to form the stable cubic phase of LLZO and high densification,high sintering temperatures above 1100°C is typically required, which causes Lithium loss of the system.Many studieshave been taken to dop LLZO with various precursors such as Ga, Ta, and Al to stabilize the cubic structure and reduce calcination temperature, while the doping effect on sintering densification is still unclear. In this study Al doping along with ball milling were explored to stabilize the cubic phase of LLZO and improve densification, while reducing the amount of impurity phases. Samples were synthesized from the precursors Li 2 CO 3 , Al 2 O 3 , La 2 O 3 , and ZrO 2 by ball milling followed by heat treatment for 12 hours at 1000°C. XRD with Rietveld fitting was used to determine the two phases of LLZO (cubic, tetragonal) and other possible secondary phases. Furthermore,SEM with top and cross sectional views was conducted to investigate the morphology and microstructure of sintered pellets.