Search NASA⌕ Search

Engineering topics

Ettenberg, M.

Publications and source records attributed to Ettenberg, M..

16 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1991

Improving the Reliability and Modal Stability of High Power 870 nm AlGaAs CSP Laser Diodes for Applications to Free Space Communication Systems

The operating characteristics (power-current, beam divergence, etc.) and reliability assessment of high-power CSP lasers is discussed. The emission wavelength of these lasers was optimized at 860 to 880 nm. The operational characteristics of a new laser, the inverse channel substrate planar (ICSP) laser, grown by metalorganic chemical vapor deposition (MOCVD), is discussed and the reliability assessment of this laser is reported. The highlights of this study include a reduction in the threshold current value for the laser to 15 mA and a degradation rate of less than 2 kW/hr for the lasers operating at 60 mW of peak output power.

Connolly, J. C.↗
NASA NTRS1989

High-power single spatial mode AlGaAs channeled-substrate-planar semiconductor diode lasers for spaceborne communications

A high power single spatial mode channeled substrate planar AlGaAs semiconductor diode laser was developed. The emission wavelength was optimized at 860 to 880 nm. The operating characteristics (power current, single spatial mode behavior, far field radiation patterns, and spectral behavior) and results of computer modeling studies on the performance of the laser are discussed. Reliability assessment at high output levels is included. Performance results on a new type of channeled substrate planar diode laser incorporating current blocking layers, grown by metalorganic chemical vapor deposition, to more effectively focus the operational current to the lasing region was demonstrated. The optoelectronic behavior and fabrication procedures for this new diode laser are discussed. The highlights include single spatial mode devices with up to 160 mW output at 8600 A, and quantum efficiencies of 70 percent (1 W/amp) with demonstrated operating lifetimes of 10,000 h at 50 mW.

Connolly, J. C.↗
NASA NTRS1988

High-power AlGaAs channeled substrate planar diode lasers for spaceborne communications

A high power channeled substrate planar AlGaAs diode laser with an emission wavelength of 8600 to 8800 A was developed. The optoelectronic behavior (power current, single spatial and spectral behavior, far field characteristics, modulation, and astigmatism properties) and results of computer modeling studies on the performance of the laser are discussed. Lifetest data on these devices at high output power levels is also included. In addition, a new type of channeled substrate planar laser utilizing a Bragg grating to stabilize the longitudinal mode was demonstrated. The fabrication procedures and optoelectronic properties of this new diode laser are described.

Connolly, J. C.↗
NASA NTRS1988

AlGaAs heterojunction lasers

The characterization of 8300 A lasers was broadened, especially in the area of beam quality. Modulation rates up to 2 Gbit/sec at output powers of 20 mW were observed, waveform fidelity was fully adequate for low BER data transmission, and wavefront measurements showed that phase aberrations were less than lamda/50. Also, individually addressable arrays of up to ten contiguous diode lasers were fabricated and tested. Each laser operates at powers up to 30 mW CW in single spatial mode. Shifting the operating wavelength of the basic CSP laser from 8300 A to 8650 A was accomplished by the addition of Si to the active region. Output power has reached 100 mW single mode, with excellent far field wave front properties. Operating life is currently approx. 1000 hrs at 35 mW CW. In addition, laser reliability, for operation at both 8300 A and 8650 A, has profited significantly from several developments in the processing procedures.

Goldstein, B.↗
NASA NTRS1985

Coupled-mode analysis of gain and wavelength oscillation characteristics of diode laser phased arrays

The lasing wavelengths and gain characteristics of the modes of phase-locked arrays of channel-substrate-planar (CSP) lasers are presented. The gain values for the array modes are determined from complex coupling coefficients calculated using the fields of neighboring elements of the array. The computations show that, for index guided lasers which have nearly planar phase fronts, the highest order array mode will be preferred. The 'in-phase' or fundamental mode, which produces only one major lobe in the far-field radiation pattern, has the lowest modal gain of all array modes. The modal gain differential between the highest order and fundamental modes is less than 10/cm for weak coupling between the elements.

Butler, J. K.↗
NASA NTRS1983

Reliability of constricted double-heterojunction AlGaAs diode lasers

Constricted double-heterojunction diode lasers have been life tested at 70 C heatsink temperature and 3-4 mW/facet in CW operation. A median life of 7800 h is obtained at 70 C, which extrapolates to 400,000 h median life at room temperature. The extrapolated mean time to failure at room temperature is in excess of 1,000,000 h. Single-longitudinal-mode CW operation is maintained after 10,000 h of accelerated aging at 70 C.

Botez, D.↗
NASA NTRS1981

Very low threshold-current temperature sensitivity in constricted double-heterojunction AlGaAs lasers

The temperature dependence of threshold currents in constricted double-heterojunction diode lasers with strong lateral mode confinement is found to be significantly milder than for other types of lasers. The threshold-current relative variations with ambient temperature are typically two to three times less than for other devices of CW-operation capability. Over the interval 10-70 C the threshold currents fit the empirical exponential law exp/(T2-T1)/T0/ with T0 values in the 240-375 C range in pulsed operation, and in the 200-310 C range in CW operation. The external differential quantum efficiency and the mode far-field pattern near threshold are virtually invariant with temperature. The possible causes of high-T0 behavior are analyzed, and a new phenomenon - temperature-dependent current focusing - is presented to explain the results.

Botez, D.↗
NASA NTRS1980

SPS design with solid-state transmitter

The replacement of the klystrons in the microwave transmitter in the SPS leads to major redesign considerations. Several curves are presented which show the interrelations of the major design features, the power level and the transmitting and receiving dimensions.

Ettenberg, M.↗
NASA NTRS1979

Analysis of S-band solid-state transmitters for the solar power satellite

The possibility of replacing the Reference System antenna in which thermionic devices are used for the dc-to-microwave conversion, with solid-state elements was explored. System, device, and antenna module tradeoff investigations strongly point toward the desirability of changing the transmitter concept to a distributed array of relatively low power elements, deriving their dc power directly from the solar cell array and whose microwave power outputs are combined in space. The approach eliminates the thermal, weight, and dc-voltage distribution problems of a system in which high power tubes are simply replaced with clusters of solid state amplifiers. The proposed approach retains the important advantages of a solid state system: greatly enhanced reliability and graceful degradation of the system.

Belohoubek, E. F.↗
NASA NTRS1978

Accelerated step-temperature aging of Al/x/Ga/1-x/As heterojunction laser diodes

Double-heterojunction A2(0.3)Ga(0.7)As/Al(0.08)Ga(0.92)As lasers (oxide-striped and Al2O3 facet coated) were subjected to step-temperature aging from 60 to 100 C. The change in threshold current and spontaneous output was monitored at 22 C. The average time required for a 20% pulsed threshold current increase ranges from about 500 h, when operating at 100 C, to about 5000 h at a 70 C ambience. At 22 C, the extrapolated time is about 1 million h. The time needed for a 50% spontaneous emission reduction is of the same order of magnitude. The resulting activation energies are approximately 0.95 eV for laser degradation and approximately 1.1 eV for the spontaneous output decrease

Kressel, H.↗
NASA NTRS1977

Al2O3 half-wave films for long-life CW lasers

Long-term operating-life data are reported for (AlGa)As CW laser diodes. The use of half-wave Al2O3 facet coatings is shown to eliminate facet erosion, allowing stable diode operation at constant current for periods in excess of 10,000 h.

Ladany, I.↗
NASA NTRS1976

Interfacial recombination at /AlGa/As/GaAs heterojunction structures

Experiments were conducted to determine the interfacial recombination velocity at Al0.25Ga0.75As/GaAs and Al0.5Ga0.5As/GaAs heterojunctions. The recombination velocity was derived from a study of the injected minority-carrier lifetime as a function of the junction spacing. It is found that for heterojunction spacings in excess of about 1 micron, the interfacial recombination can be characterized by a surface recombination velocity of 4,000 and 8,000 cm/sec for the two types of heterojunctions, respectively. For double-heterojunction spacings below 1 micron, the constancy of the minority-carrier lifetime suggests that the interfacial recombination velocity decreases effectively. This effect is technologically very important since it makes it possible to construct very low-threshold injection lasers. No such effect is observed in single-heterojunction diodes.

Ettenberg, M.↗
NASA NTRS1970

Thermal expansion of AlAs

Lattice parameter and thermal expansion of AlAs as function of temperature, indicating lattice match at 900 C with GaAs

Ettenberg, M.↗