Effects of processing and microstructure on the oxidation of ZrB2-SiC in CO2
Not Available
Lakusta, Marharyta↗
Engineering topics
Fahrenholtz, William G.
Publications and source records attributed to Fahrenholtz, William G..
Final-stage densification kinetics of direct current–sinteredZrB2
Final-stage sintering was analyzed for nominally phase pure zirconium diboride synthesized by borothermal reduction of high-purity ZrO2. Analysis was conducted on ZrB2 ceramics with relative densities greater than 90% using the Nabarro–Herring stress–directed vacancy diffusion model. Temperatures of 1900°C or above and an applied uniaxial pressure of 50 MPa were required to fully densify ZrB2 ceramics by direct current sintering. Ram travel data were collected and used to determine the relative density of the specimens during sintering. Specimens sintered between 1900 and 2100°C achieved relative densities greater than 97%, whereas specimens sintered below 1900°C failed to reach the final stage of sintering. The average grain size ranged from 1.0 to 14.7 μm. The activation energy was calculated from the slope of an Arrhenius plot that used the Kalish equation. The activation energy was 162 ± 34 kJ/mol, which is consistent with the activation energy for dislocation movement in ZrB2. The diffusion coefficients for dislocation motion that controls densification were 5.1 × 10−6 cm2/s at 1900°C and 5.1 × 10−5 cm2/s at 2100°C, as calculated from activation energy and average grain sizes. This study provides evidence that the dominant mechanism for final-stage sintering of ZrB2 ceramics is dislocation motion.
36 MATERIALS SCIENCE↗
Pressureless sintering of dual-phase, high-entropy boride–carbide ceramics
Here, dual-phase, high-entropy boride–carbide ceramics were densified by pressureless sintering. Relative densities up to approximately 96% were obtained for ceramics containing about 30 vol% high-entropy boride and 70 vol% high-entropy carbide. Isostatic pressing at 200 MPa resulted in higher relative densities of both the green bodies and final ceramics compared to uniaxial pressing. The highest relative density of 96.3% was achieved for a ceramic that was isostatically pressed at 200 MPa and sintered at 2300°C for 2 h. Grain sizes of the resulting ceramics were approximately 2 µm. This is the first report of pressureless sintering of dual-phase, high-entropy boride–carbide ceramics.
36 MATERIALS SCIENCE↗
Mechanical Activation and Cation Site Disorder in MgAl 2 O 4
The synthesis and crystallographic site occupancy were investigated for MgAl 2 O 4 with and without mechanical activation of the precursor powders. Heating to 1200 °C or higher resulted in the formation of a single spinel phase regardless of whether the powders were mechanically activated or not. Neutron diffraction analysis was used to determine cation site occupancy and revealed that mechanical activation resulted in a lower degree of cation site inversion compared to the nonactivated materials, which indicated that the powders were closer to thermodynamic equilibrium. This is the first study to characterize the effects of mechanical activation on crystallographic site occupancy in magnesium aluminate spinel using neutron diffraction.
36 MATERIALS SCIENCE↗
Fusion welding of refractory metals and ZrB 2 -SiC-ZrC ceramics
Molybdenum and a molybdenum alloy were fusion welded to ZrB2-based ceramics to determine if the electrical and thermal properties of the metals and ceramics affected their weldability. Commercial ceramic powders were hot pressed, machined into coupons, and preheated to 1600 °C before joining the ceramics to commercial metals using plasma arc welding. Weldability varied as indicated by the range of porosity observed within the fusion zones. Measured thermal and electrical properties appeared to have little to no effect on the weldability of metal-ceramic welds despite the large range of values measured across each property. Differences in melting temperatures between metal and ceramic coupons did affect weldability by changing the weld penetration depth into ceramic coupons. Finally, future studies on metal-ceramic welds are suggested to investigate the effect that work function, melt viscosity, wetting, or other properties have on weldability.
36 MATERIALS SCIENCE↗
High-entropy boride–carbide ceramics by sequential boro/carbothermal synthesis
We report a dual-phase high-entropy boride/carbide ceramic with fine grain size was synthesized by a sequential boro/carbothermal process. In the first step, a Hf-Nb-Ta-Ti-Zr-containing carbide was synthesized by carbothermal reduction of oxides followed by reaction of the carbide with B4C and ZrH2 to convert part of the carbide to boride. The resulting composition was ~29 vol% high-entropy boride with an average grain size of ~1.1 µm. Solid solution formation occurred at the densification temperature of 1900°C resulting in a relative density higher than 99%. The Vickers’ hardness was 26.5 ± 1.4 GPa. This is the first report of synthesizing dual-phase boride-carbide high-entropy ceramics from carbothermally synthesized, high-entropy carbide powders.
36 MATERIALS SCIENCE↗
Mechanical properties of fusion welded ceramics in the $\mathrm{SiC-ZrB}$ 2 and $\mathrm{SiC-ZrB}$ 2 -$\mathrm{ZrC}$ systems
Mechanical properties of welded SiC-ZrB 2 and SiC-ZrB 2 -ZrC ceramics were measured up to 1700 °C. Commercial powders were hot pressed, machined into coupons, and preheated to 1600 °C before joining the ceramics using either tungsten inert gas welding or plasma arc welding. Toughness of the parent materials was 3–4 MPa*m 1/2 which decreased after welding to 2–2.5 MPa*m 1/2 . Strength of the SiC-ZrB 2 -ZrC parent material was ~700 MPa at 25 °C, ~300 MPa at 1700 °C, and retained 40–60% of this strength once welded. Strength of the SiC-ZrB2 parent material was ~600 MPa at 25 °C and 1700 °C and retained 20–30% of this strength once welded. Griffith analysis indicated that the strength in the parent materials was controlled by the size of SiC clusters while strength of welds was controlled by the size of pores in fusion zones. Therefore, removal of pores in produced fusion zones should be investigated to improve strength of future ceramic welds.
36 MATERIALS SCIENCE↗
Characterization of fusion welded ceramics in the SiC-ZrB 2 -ZrC system
Various SiC-ZrB 2 -ZrC ceramics were joined by fusion welding to determine the maximum silicon carbide content that could be joined. Commercial powders were hot pressed, machined, and preheated to 1450 °C before joining with a tungsten inert gas welding torch at 160–200 A. Resulting welds were cross-sectioned and analyzed to determine which compositions were weldable and to characterize microstructural evolution in welded samples. As compositions approached the ternary eutectic, the welds had smaller SiC grains and exhibited better weldability. Penetration depth of welds was controlled by a combination of current input and welding speed. Here, the ternary eutectic in the system was found at 36.9 ± 1.3 vol% SiC, 42.7 ± 1.5 vol% ZrB 2 , and 20.4 ± 1.9 vol% ZrC and its melting temperature was 2330 ± 23 °C. A ternary phase diagram for the SiC-ZrB 2 -ZrC was constructed and proposed via microstructural analysis of arc melted pellets on binary joins between each binary eutectic and the ternary eutectic in the system.
36 MATERIALS SCIENCE↗