NASA NTRS1974

Temperature, illumination, and fluence dependence of current and voltage in electron irradiated solar cells

Empirical equations have been derived from measurements of solar cell photovoltaic characteristics relating light-generated current and open circuit voltage to cell temperature, intensity of illumination and 1-MeV electron fluence. Both 2-ohm-cm and 10-ohm-cm cells were tested over the temperature range from 120 to 470 K, the illumination intensity range from 5 to 1830 mW/sq cm, and the electron fluence range from 1 x 10 to the 13th to 1 x 10 to the 16th electrons/sq cm. The normalized temperature coefficient of the light generated current varies as the 0.18 power of the fluence for temperatures above approximately 273 K and is independent of fluence at lower temperatures. At 140 mW/sq cm, a power law expression was derived which shows that the light-generated current decreases at a rate proportional to the 0.153 power of the fluence for both resistivities. The coefficient of the expression is larger for 2-ohm-cm cells; consequently, the advantage for 10-ohm-cm cells increased with increasing fluence.

Faith, T. J.↗

NASA NTRS1973

Temperature, illumination and fluence dependence of current and voltage in electron irradiated solar cells

Emperical equations have been derived from measurements of solar cell photovoltaic characteristics relating light generated current, IL, and open circuit voltage, VO, to cell temperature, T, intensity of illumination, W, and 1 Mev electron fluence, phi both 2 ohm-cm and 10 ohm-cm cells were tested. The temperature dependency of IL is similar for both resistivities at 140mw/sq cm; at high temperature the coefficient varies with fluence as phi 0.18, while at low temperatures the coefficient is relatively independent of fluence. Fluence dependent degration causes a decrease in IL at a rate proportional to phi 0.153 for both resistivities. At all intensities other than 560 mw/sq cm, a linear dependence of IL on illumination was found. The temperature coefficient of voltage was, to a good approximation, independent of both temperature and illumination for both resistivities. Illumination dependence of VOC was logarithmic, while the decrease with fluence of VOC varied as phi 0.25 for both resistivities.

Obenschain, A. F.↗

NASA NTRS1973

Temperature dependence of damage coefficient in electron irradiated solar cells

Measurements of light-generated current vs cell temperature on electron-irradiated n/p silicon solar cells show the temperature coefficient of this current to increase with increasing fluence for both 10-ohm and 20-ohm cells. A relationship between minority-carrier diffusion length and light-generated current was derived by combining measurements of these two parameters: vs fluence at room temperature, and vs cell temperature in cells irradiated to a fluence of 1 x 10 to the 15th power e/sq cm. This relationship was used, together with the light-generated current data, to calculate the temperature dependence of the diffusion-length damage coefficient. The results show a strong decrease in the damage coefficient with increasing temperature in the range experienced by solar panels in synchronous earth orbit.

Faith, T. J.↗

NASA NTRS1973

Solar array synthesis computer program

Photovoltaic characteristics have been measured on solar cells irradiated by 1 MeV electrons to fluences ranging from 1 x 10 to the 13th power e/sq cm to 1 x 10 to the 16th power e/sq cm, for cell temperatures ranging from 123 K to 473 K and for illumination intensities ranging from 5m W/sq cm to 1830m W/sq cm. Empirical equations have been derived from these measurements to describe the behavior of light generated current, open circuit voltage and I-V curve shape over various portions of these temperature/illumination ranges. Both 10 ohms/cm and 17 ohms/cm n-p silicon solar cells were tested, and similar analytical expressions were formulated for easy comparison between the two resistivities.

Faith, T. J.↗

NASA NTRS1972

Voltage and power relationships in lithium-containing solar cells.

Photovoltaic characteristics have been measured on a large number of crucible-grown lithium-containing solar cells irradiated by 1-MeV electrons to fluences ranging from 3 x 10 to the 13th power to 3 x 10 to the 15th power electrons per sq cm. These measurements have established empirical relationships between cell photovoltaic parameters and lithium donor density gradient. Short-circuit current and maximum power measured immediately after irradiation decrease logarithmically with lithium gradient. Open-circuit voltage increases logarithmically with lithium gradient both immediately after irradiation and after recovery, the degree of recovery being strongly gradient-dependent at high fluence. As a result, the maximum power and the power at 0.43 V after recovery from 3 x 10 to the 15th power electrons per sq cm increase with increasing lithium gradient.

Faith, T. J.↗

NASA NTRS1971

Study to determine and improve design for lithium-doped solar cells

Solar cell experiments show that a single lithium density parameter, the lithium density gradient, calculated from nondestructive capacitance measurements, provides the basis for accurate predictions of lithium cell behavior in a 1-MeV electron environment for fluences ranging between 3 X 10 to the 13th power e/sq cm and 3 X 10 to the 15th power/e sq cm. The oxygen-rich (quartz crucible) lithium cell with phosphorous starting dopant and lithium gradient between approximately 5 X 10 to the 18th power and 1.5 x 10 to the 19th power/cm to the 4th power was found superior in performance to the commercial 10 ohm-cm n/p control cells. Post-recovery stability of oxygen-rich cells was satisfactory. An average post-recovery current drop of approximately 1 mA was observed for 70 crucible cells after 1 year-equivalent storage time at 80 C. In contrast the oxygen-poor (float zone and Lopex) lithium cells displayed spotty initial performance and stability problems at room temperature.

Brucker, G.↗

NASA NTRS1971

Damage and recovery characteristics of lithium-containing solar cells.

Damage and recovery characteristics were measured on lithium-containing solar cells irradiated by 1-MeV electrons. Empirical expressions for cell recovery time, diffusion-length damage coefficient immediately after irradiation, and diffusion-length damage coefficient after recovery were derived using results of short-circuit current, diffusion-length, and reverse-bias capacitance measurements. The damage coefficients were expressed in terms of a single lithium density parameter, the lithium gradient. A fluence dependence was also established, this dependence being the same for both the immediate-post-irradiation and post-recovery cases. Cell recovery rates were found to increase linearly with lithium gradient.

Faith, T. J.↗

NASA NTRS1971

Density and fluence dependence of lithium cell damage and recovery characteristics

Experimental results on lithium-containing solar cells point toward the lithium donor density gradient dN sub L/dw as being the crucial parameter in the prediction of cell behavior after irradiation by electrons. Recovery measurements on a large number of oxygen-rich and oxygen-lean lithium cells have confirmed that cell recovery speed is directly proportional to the value of the lithium gradient for electron fluences. Gradient measurements have also been correlated with lithium diffusion schedules. Results have shown that long diffusion times (25 h) with a paint-on source result in large cell-to-cell variations in gradient, probably due to a loss of the lithium source with time.