Cation Migration and LSCF/SDC Decomposition Related to Long-Term Operation Mode as Revealed by Electron Microscopy
This study utilized energy dispersive spectroscopy (EDS) in a scanning electron microscope (SEM) and a scanning transmission electron microscope (STEM) in order to track cation migration and related particle decomposition for air electrode components of solid oxide cells. The influence of a Sm-doped ceria (SDC) barrier layers was assessed for three operation modes (fuel cell, electrolysis, reversible) over long time periods (1000-1500 hours). Composition profiles across air electrode/electrolyte interfaces indicated negligible accumulation of La/Sr cations to the yttria-stabilized zirconia (YSZ) electrolyte during operation. Instead, air electrode particles composed of SDC and/or La-Sr-Co-Fe-oxides (LSCF) exhibited decomposition by Sr evaporation and Sm migration to LSCF particle edges.