Role of chemical disorder on radiation-induced defect production and damage evolution in NiFeCoCr

Understanding chemical disorder in many concentrated solid solution alloys (CSAs) at the levels of electrons and atoms has attracted increasing attention as a path forward to reveal and identify underlying mechanisms for extraordinary mechanical properties and improved radiation tolerance. Single-phase NiFeCoCr CSA is a common base for many high-entropy alloys (HEAs) that have shown improved mechanical strength and radiation tolerance. In this study, defect production and damage evolution in NiFeCoCr under ion irradiation at room temperature to dose over 20 dpa are determined using ion channeling technique along both <100> and <110> directions utilizing multiple probing beam energies. The results obtained from the multi-axial and multi-energy channeling analysis are compared with those previously obtained for Ni crystals irradiated under similar conditions. The influence of chemical complexity on defect production and clustering at early-stage under room temperature irradiation up to dose of 1 dpa is discussed based on positron annihilation spectroscopy results. Defect structure evaluation in Ni and NiFeCoCr is also discussed based on transmission electron microscopy results over a prolonged irradiation at both room and elevated temperatures. Compared with chemically complex NiFeCoCr, larger dislocation loops thus less lattice strain are expected to form in pure Ni. Moreover, the role of chemical disorder in this CSA is also investigated based on ab initio calculations using large supercells. Finally, to understand the impact of chemical complexity effect on defect structure evolution, this integrated research effort attempts to link the relatively large charge redistribution due to difference in valence electron counts resulting from alloying different 3d transition metal elements, moderate lattice distortion arising from similar adaptable atomic size, and notable suppressed or delayed damage evolution in NiFeCoCr.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Diffusion-mediated chemical concentration variation and void evolution in ion-irradiated NiCoFeCr high-entropy alloy

High-entropy alloys (HEAs) are proposed as potential structural materials for advanced nuclear systems, but little is known about the response of matrix chemistry in HEAs upon irradiation. Here, we reveal a substantial change of matrix chemical concentration as a function of irradiation damage (depth) in equiatomic NiCoFeCr HEA irradiated by 3 MeV Ni ions. After ion irradiation, the matrix contains more Fe/Cr in depth shallower than ~900–1000 nm but more Ni/Co from ~900–1000 nm to the end of the ion-damaged region due to the preferential diffusion of vacancies through Fe/Cr. Preferential diffusion also facilitates migration of vacancies from high radiation damage region to low radiation damage region, leading to no void formation below ~900–1000 nm and void formation around the end of the ion-damaged region at a fluence of 5 × 10 16 cm -2 (~123 dpa, displacements per atom, peak dose under full cascade mode). As voids grow significantly at an increased fluence (8 × 10 16 cm -2 , 196 dpa), the matrix concentration does not change dramatically due to new voids formed below ~900–1000 nm.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2021

Diffusion-mediated chemical concentration variation and void evolution in ion-irradiated NiCoFeCr high-entropy alloy

High-entropy alloys (HEAs) are proposed as potential structural materials for advanced nuclear systems, but little is known about the response of matrix chemistry in HEAs upon irradiation. Here, we reveal a substantial change of matrix chemical concentration as a function of irradiation damage (depth) in equiatomic NiCoFeCr HEA irradiated by 3 MeV Ni ions. After ion irradiation, the matrix contains more Fe/Cr in depth shallower than ~900–1000 nm but more Ni/Co from ~900–1000 nm to the end of the ion-damaged region due to the preferential diffusion of vacancies through Fe/Cr. Preferential diffusion also facilitates migration of vacancies from high radiation damage region to low radiation damage region, leading to no void formation below ~900–1000 nm and void formation around the end of the ion-damaged region at a fluence of 5 × 10 16 cm –2 (~123 dpa, displacements per atom, peak dose under full cascade mode). As voids grow significantly at an increased fluence (8 × 10 16 cm –2 , 196 dpa), the matrix concentration does not change dramatically due to new voids formed below ~900–1000 nm.

36 MATERIALS SCIENCE↗
DOE OSTI2020

From suppressed void growth to significant void swelling in NiCoFeCr complex concentrated solid-solution alloy

Void swelling can result in dimensional instability and undermine the safe operation of nuclear reactors. Current strategies to inhibit void swelling mainly focus on enhancing defect absorption and recombination by introducing high-density defect sinks. Complex concentrated solid-solution alloys (CSAs), including high-entropy alloys, can withstand severe radiation damage due to their inherent chemical complexity without interfaces. However, the underlying mechanisms for void suppression in CSAs are far from clear. In this research, we studied the void evolution with respect to irradiation depths, doses, and temperatures in equiatomic NiCoFeCr under 3 MeV Ni ion irradiations. At relatively low doses (16 and 54 displacements per atom, dpa), voids form mainly outside of the ion-damaged region, and void formation in the peak damage region is suppressed, leading to negligible swelling. However, with further increase of dose (86 up to 250 dpa), significant void growth occurs in the peak damage region and extended dislocation lines dominate instead of short dislocation lines and loops formed at lower doses. From 500 to 700 °C, the dislocation density decreases while dislocations grow. Although the overall void swelling increases dramatically from 500 to 580 °C at 54 dpa, void growth in the peak damage region is still suppressed. The transition from suppressed void growth to significant void swelling is attributed to dislocation evolution and local chemical inhomogeneity (enrichment of Fe/Cr in the matrix) at higher doses. Our study shows that controlling element diffusion and defect evolution through tuning chemical complexity can further enhance the swelling resistance of CSAs.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Interpreting nanovoids in atom probe tomography data for accurate local compositional measurements

Quantifying chemical compositions around nanovoids is a fundamental task for research and development of various materials. Atom probe tomography (APT) and scanning transmission electron microscopy (STEM) are currently the most suitable tools because of their ability to probe materials at the nanoscale. Both techniques have limitations, particularly APT, because of insufficient understanding of void imaging. Here, we employ a correlative APT and STEM approach to investigate the APT imaging process and reveal that voids can lead to either an increase or a decrease in local atomic densities in the APT reconstruction. Simulated APT experiments demonstrate the local density variations near voids are controlled by the unique ring structures as voids open and the different evaporation fields of the surrounding atoms. We provide a general approach for quantifying chemical segregations near voids within an APT dataset, in which the composition can be directly determined with a higher accuracy than STEM-based techniques.

36 MATERIALS SCIENCE↗