An additively manufactured near-eutectic Al-Ce-Ni-Mn-Zr alloy with high creep resistance

A new additively manufactured (AM) Al-7.5Ce-4.5Ni-0.4Mn-0.7Zr (wt.%) near-eutectic alloy is reported, which shows unprecedented creep resistance up to 400 °C (a homologous temperature of 0.72). The eutectic solidification microstructure comprises ~ 27 vol% of coarsening-resistant second phase network with an ultrafine (<100 nm) inter-phase spacing. Both Mn and Zr contribute to creep resistance of the alloy. Small amount of Mn addition promotes selection of coarsening resistant phases without compromising the alloy processability. Zr not only improves hot-tearing resistance, but further enhances the second phase coarsening resistance resulting in improved creep resistance. Neutron diffraction performed during creep deformation reveals that the underlying mechanism for creep resistance in this alloy is impedance to dislocation motion stemming from the ultrafine eutectic solidification microstructure, whereas load transfer strengthening becomes less effective as the creep temperature increases. The second phase forms a continuous network in the as-fabricated condition, which is maintained during long-term creep at 300 °C. However, this network is fragmented into fine dispersoids at higher temperatures. It is proposed that the rate-limiting deformation mechanism at 300–400 °C is (i) dislocation climb for the alloy with fragmented second phase dispersoids and (ii) Orowan looping for the alloy with a continuous second phase network. In conclusion, the present design of an AM-processable multicomponent eutectic alloy with high creep resistance can be applied to other metallic systems exhibiting eutectic reactions, with expected extreme creep resistance.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Grain Structure Evolution in Fe-6Si During Directed Energy Deposition

The purpose of this study is to explore the effect of additive manufacturing (AM) process variables on the grain structure of Fe-6Si, a soft-magnetic alloy used in electrical machine and grid applications. Samples were fabricated with laser engineered net shaping (LENS) with varying inter-pass timing and numbers of unidirectional passes. Here the results show that the grain structure was affected by both solidification and solid-state grain growth mechanisms. A model of the LENS process suggests that, although shorter inter-pass times encourage greater nucleation of new grains and therefore grain refinement during solidification, these conditions also help maintain high solid-state temperatures that allow for grain boundary motion to keep pace with the build rate. Grains formed under these conditions may span multiple layers, and the high-temperature gradient promotes directional growth. This new understanding of these microstructure evolution mechanisms will aid in using process conditions to control the competition between solidification and solid-state grain growth to create grain structures that may not be possible with conventional processing.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Improved Productivity with Multilaser Rotary Powder Bed Fusion Additive Manufacturing

Laser powder bed fusion (LPBF) enables the fabrication of intricate, geometrically complex structures with a sufficiently fine surface finish for many engineering applications with a diversity of available feedstock metals. However, the production rate of LPBF systems is not well suited for mass production in comparison to traditional manufacturing methods. LPBF systems measure their deposition rates in 100's of grams per hour, while other processes measure in kilograms per hour or even in the case of processes such as forming, stamping, and casting, 100's of kilograms per hour. To be widely adopted in industry for mass production, LPBF requires a new scalable architecture that enables many orders of magnitude improvement in deposition rate, while maintaining the geometry freedom of additive manufacturing. This article explores concepts that could achieve as much as four orders of magnitude increase in the production rate through the application of (1) rotary table kinematic arrangements; (2) a dramatic number of simultaneously operating lasers; (3) reductions of laser optic size; (4) improved scanning techniques; and (5) an optimization of toroidal build plate size. To theoretically demonstrate the possibilities of production improvements, a productivity analysis is proposed for synchronous reluctance motors with relevance to the electric vehicle industry, given the recent increase in the diversity of printable soft magnetic alloys. The analysis provides insights into the impact of the architecture and process parameters necessary to optimize rotary powder bed fusion for mass production.

36 MATERIALS SCIENCE↗

DOE OSTI2023

The high intensity diffractometer for residual stress analysis (HIDRA), a third generation residual stress mapping neutron diffractometer at the high flux isotope reactor

This paper describes the hardware and software upgrades, operation, and performance of the high intensity diffractometer for residual stress analysis (HIDRA) instrument, a residual stress mapping neutron diffractometer located at the High Flux Isotope Reactor at Oak Ridge National Laboratory in Oak Ridge Tennessee, USA. Following a major upgrade in 2018, the new instrument has a single 3 He multiwire 2D 30 × 30 cm 2 position sensitive detector, yielding a field of view of 17° 2θ. Further, the increase in the field of view (from 4° 2θ) from the previous model instrument has contributed to the tremendous improvement in the out of plane solid angle such that the 3D count rate could be obtained easily. Accordingly, the hardware, software, Data Acquisition System (DAS), and so on have also been updated. Finally, all these enhanced features of HIDRA have been ably demonstrated by conducting multi directional diffraction measurements in the quenched 750-T74 aluminum, and the evolved and improved strain/stress mappings are presented.

3D printing↗

DOE OSTI2022

Load shuffling during creep deformation of an additively manufactured AlCuMnZr alloy

Here, the high-temperature deformation behavior of an additively manufactured Al-Cu-Mn-Zr alloy is evaluated in the as-fabricated and heat-treated states using traditional ex-situ and in-situ neutron diffraction creep experiments performed at 300 °C. The dominant reinforcement phase in the alloy, θ-Al 2 Cu, despite its high volume fraction of ~10%, does not provide load transfer strengthening during creep deformation. Instead, the lattice strain evolution suggests a new mechanism we term “load shuffling” wherein the initial load is transferred away from precipitate-free zones along the grain boundaries where most of the θ-Al 2 Cu particles are located to precipitate-strengthened grain interiors. Notwithstanding the lack of load transfer strengthening, the as-fabricated AM Al-Cu-Mn-Zr alloy still possesses improved creep resistance at 300 °C relative to a cast alloy with similar composition. The proposed load shuffling mechanism explains the lack of observed L1 2 -Al 3 Zr strengthening at 300 °C and helps identify several strategies for improvement of elevated-temperature mechanical response of AM Al alloys.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Quantitative texture analysis at the WAND 2 and HIDRA diffractometers

Data collection and analysis strategies have been developed for efficient and reliable crystallographic texture measurements at two recently upgraded neutron diffractometers: the Wide Angle Neutron Diffractometer Squared (WAND 2 ) and the High Intensity Diffractometer for Residual Stress Analysis (HIDRA) at the High Flux Isotope Reactor located at Oak Ridge National Laboratory. These methods are demonstrated using measurements on a variety of textured samples, including multi-phase steel composites and polycrystalline calcite (CaCO 3 ). Reference measurements were also made at VULCAN, the engineering diffractometer located at the Spallation Neutron Source. The texture data obtained on the different instruments are in agreement, and WAND 2 is more time efficient than HIDRA. Two analysis methods were investigated, single-peak fitting to obtain individual pole figures for inversion and Rietveld texture analysis using MAUD. Here, the impact of the differences between the various textures obtained was evaluated through the calculation of diffraction elastic constants, which is one application of the texture data collected. Both instruments were found to provide texture data that are suitable for complementing other analyses, such as residual stress mapping.

47 OTHER INSTRUMENTATION↗