An Atomic-Scale Understanding of UO 2 Surface Evolution during Anoxic Dissolution

Our present understanding of surface dissolution of nuclear fuels such as uranium dioxide (UO 2 ) is limited by the use of non-local characterization techniques. In this paper, we discuss the use of state-of-the-art scanning transmission electron microscopy (STEM) to reveal atomic–scale changes occurring to UO 2 thin films subjected to anoxic dissolution in deionised water. No amorphisation of the UO 2 film surface during dissolution is observed, and dissolution occurs preferentially at surface reactive sites that present as surface pits which increase in size as the dissolution proceeds. Using a combination of STEM imaging modes, energy-dispersive X-ray spectroscopy (STEM-EDS), and electron energy loss spectroscopy (STEM-EELS), we investigate structural defects and oxygen passivation of the surface that originates from the filling of the octahedral interstitial site in the centre of the unit cells and its associated lattice contraction. Taken together, our results reveal complex pathways for both the dissolution and infiltration of solutions into UO 2 surfaces.

38 RADIATION CHEMISTRY, RADIOCHEMISTRY, AND NUCLEA↗

DOE OSTI2020

An investigation of the long-range and local structure of sub-stoichiometric zirconium carbide sintered at different temperatures

ZrC 1-x (sub-stoichiometric zirconium carbide), a group IV transition metal carbide, is being considered for various high temperature applications. Departure from stoichiometry changes the thermo-physical response of the material. Reported thermo-physical properties exhibit, in some cases, a degree of scatter with one likely contributor to this being the uncertainty in the C/Zr ratio of the samples produced. Conventional, methods for assigning C/Zr to samples are determined either by nominal stochiometric ratios or combustion carbon analysis. In this study, a range of stoichiometries of hot-pressed ZrC 1-x were examined by SEM, XRD, Raman spectroscopy and static 13 C NMR spectroscopy and used as a basis to correct the C/Zr. Graphite, amorphous, and ZrC 1-x carbon signatures are observed in the 13 C NMR spectra of samples and are determined to vary in intensity with sintering temperature and stoichiometry. In this study a method is outlined to quantify the stoichiometry of ZrC 1-x and free carbon phases, providing an improvement over the sole use and reliance of widely adopted bulk carbon combustion analysis. We report significantly lower C/Zr values determined by 13 C NMR analysis compared with carbon analyser and nominal methods. Furthermore, the location of carbon disassociated from the ZrC 1-x structure is analysed using SEM and Raman spectroscopy.

36 MATERIALS SCIENCE↗