Impact of degradation mechanisms at the cathode/electrolyte interface of garnet-based all-solid-state batteries
Not Available
Clausnitzer, Moritz (ORCID:0009000047434947)↗
Engineering topics
Fattakhova-Rohlfing, Dina
Publications and source records attributed to Fattakhova-Rohlfing, Dina.
The Riddle of Dark LLZO: Cobalt Diffusion in Garnet Separators of Solid‐State Lithium Batteries
Abstract Solid‐state batteries (SSBs) with a Li 7 La 3 Zr 2 O 12 (LLZO) garnet electrolyte are attracting much attention as robust and safe alternative to conventional lithium‐ion batteries. Technical challenges in the practical implementation of garnet SSBs are related to the need for high‐temperature sintering, which often leads to undesirable chemical reactions with the cathode material. While these reactions are well understood for composite cathodes, very little is known about similar processes between cathode and separator during battery fabrication. This work focuses on understanding the processes between the composite LiCoO 2 ‐LLZO cathode and the LLZO separator and how they affect the battery performance. The extensive diffusion of Co‐ions within LLZO, which leads to the often‐observed LLZO darkening, is shown to have a significant impact on ionic conductivity, electronic conductivity, and dendrite stability of the separator. Experimental data coupled with large‐scale molecular dynamics simulations uncover the diffusion mechanism for Co‐ions and identify secondary phases that form during these interactions. In addition to extensive Co‐ion diffusion within the grains, a non‐uniform segregation of Co‐ions at grain boundaries is found leading to the formation of three distinct Co‐containing phases. This work offers a general approach to studying the fundamental ion diffusion processes that occur during the fabrication of oxide SSBs.
electrochemical properties↗
The effects of aluminum concentration on the microstructural and electrochemical properties of lithium lanthanum zirconium oxide
Cubic lithium lanthanum zirconium oxide (Li 7-x Al x La 3 Zr 2 O 12 , LLZO) garnet has gained attention as a promising next-generation electrolyte for lithium batteries due to its high ionic conductivity and chemical stability with lithium metal. The high conductivity can be achieved through doping over a range of aluminum concentrations. In this study, we hot-pressed samples to achieve <2% nominal porosity with aluminum concentrations from x = 0.25–0.55 mol to understand the effect of aluminum on microstructure and electrochemistry. It was observed that beyond the aluminum solubility limit (x = ~0.40), resistive secondary phases formed at the grain boundaries. As a result, the percent grain boundary resistance increased from 17.6 to 41.2% for x = 0.25 and x = 0.55, respectively. Both the grain boundary and bulk activation energies remained relatively constant as the aluminum concentrations increased (~0.44 eV and ~0.39 eV, respectively). It was, therefore, surmised that the mobility term of the Nernst–Einstein equation was roughly independent of aluminum concentration and the major variable controlling bulk conductivity was the number of lithium charge carriers. As a result, as the aluminum concentration increased from x = 0.25 to x = 0.55 the bulk conductivity decreased from 0.56 to 0.15 mS cm -1 . Following these trends of increasing grain boundary resistance and decreasing bulk conductivity with increasing aluminum concentration, x = 0.25 had the highest total conductivity (0.46 mS cm -1 ). We demonstrated that aluminum concentration has a significant effect on the microstructure and electrochemical properties of LLZO. In conclusion, we believe this work could help understand how to link processing, microstructure, and electrochemical properties to guide the manufacturing of LLZO for use in solid-state batteries.
25 ENERGY STORAGE↗
Digestion processes and elemental analysis of oxide and sulfide solid electrolytes
Detailed elemental analysis is essential for a successful development and optimization of material systems and synthesis methods. This is especially relevant for Li- and Na-containing compounds, found in state-of-the-art and next-generation battery systems. Their materials’ properties and thus the final device performance strongly depend on the crystal structure, the stoichiometry, and defect chemistry, e.g., influencing charge carrier concentration and activation energies for vacancy transport. However, a detailed quantitative analysis of light elements in a heavy matrix, featuring a broad range of solubilities and vapor pressures, is often difficult and associated with large uncertainties and thus neglected in favor of just reporting the stoichiometry as “weighed in.” Here, in this work, we report several approaches to digest and dissolve various oxide and sulfide-based materials, used in next-generation Li batteries, for elemental analysis via optical emission spectroscopy. These include the most common solid electrolytes Li-La-Ti–O, a perovskite material (LLTO), and Li-La-Zr-O which has garnet structure (LLZO). Additionally, a facile thermal digestion process is reported for a surrogate sulfide solid electrolyte (Na 2 S). The digestion procedures reported here are suitable for almost any laboratory environment and, when applied, will improve understanding of the synthesis-structure–property correlations needed to advanced batteries with all solid-state configurations.