Faur, Maria

Publications and source records attributed to Faur, Maria.

At least 19 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS2005

Novel Passivating/Antireflective Coatings for Space Solar Cells

We are developing a novel process to grow passivating/antireflective (AR) coatings for terrestrial and space solar cells. Our approach involves a Room Temperature Wet Chemical Growth (RTWCG) process, which was pioneered, and is under development at SPECMAT, Inc., under a Reimbursable Space Act Agreement with NASA Glenn Research Center. The RTWCG passivating/AR coatings with graded index of refraction are applied in one easy step on finished (bare) cells. The RTWCG coatings grown on planar, textured and porous Si, as well as on poly-Si, CuInSe2, and III-V substrates, show excellent uniformity irrespective of surface topography, crystal orientation, size and shape. In this paper we present some preliminary results of the RTWCG coatings on Si and III-V substrates that show very good potential for use as a passivation/AR coating for space solar cell applications. Compared to coatings grown using conventional techniques, the RTWCG coatings have the potential to reduce reflection losses and improve current collection near the illuminated surface of space solar cells, while reducing the fabrication costs.

Faur, Mircea↗
NASA NTRS2004

Passivating Window/First Layer AR Coating for Space Solar Cells

Chemically grown oxides, if well designed, offer excellent surface passivation of the emitter surface of space solar cells and can be used as effective passivating window/first layer AR coating. In this paper, we demonstrate the effectiveness of using a simple room temperature wet chemical technique to grow cost effective passivating layers on solar cell front surfaces after the front grid metallization step. These passivating layers can be grown both on planar and porous surfaces. Our results show that these oxide layers: (i) can effectively passivate the from the surface, (ii) can serve as an effective optical window/first layer AR coating, (iii) are chemically, thermally and UV stable, and (iv) have the potential of improving the BOL and especially the EOL efficiency of space solar cells. The potential of using this concept to simplify the III-V based space cell heterostructures while increasing their BOL and EOL efficiency is also discussed.

Faur, Mircea↗
NASA NTRS1997

Ultra-Low-Cost Room Temperature SiC Thin Films

The research group at CSU has conducted theoretical and experimental research on 'Ultra-Low-Cost Room Temperature SiC Thin Films. The effectiveness of a ultra-low-cost room temperature thin film SiC growth technique on Silicon and Germanium substrates and structures with applications to space solar sells, ThermoPhotoVoltaic (TPV) cells and microelectronic and optoelectronic devices was investigated and the main result of this effort are summarized.

Faur, Maria↗
NASA NTRS1995

Theoretical and experimental research in space photovoltaics

Theoretical and experimental research is outlined for indium phosphide solar cells, other solar cells for space applications, fabrication and performance measurements of shallow homojunction InP solar cells for space applications, improved processing steps and InP material characterization with applications to fabrication of high efficiency radiation resistant InP solar cells and other opto-electronic InP devices, InP solar cells fabricated by thermal diffusion, experiment-based predicted high efficiency solar cells fabricated by closed-ampoule thermal diffusion, radiation resistance of diffused junction InP solar cells, chemical and electrochemical characterization and processing of InP diffused structures and solar cells, and progress in p(+)n InP diffused solar cells.

Faur, Mircea↗
NASA NTRS1995

Design of a Three-Layer Antireflection Coating for High Efficiency Indium Phosphide Solar Cells Using a Chemical Oxide as First Layer

It is well known that the behavior of III-V compound based solar cells is largely controlled by their surface, since the majority of light generated carriers (63% for GaAs and 79% for InP) are created within 0.2 microns of the illuminated surface of the cell. Consequently, the always observed high surface recombination velocity (SRV) on these cells is a serious limiting factor for their high efficiency performance, especially for those with the p-n junction made by either thermal diffusion or ion implantation. A good surface passivation layer, ideally, a grown oxide as opposed to a deposited one, will cause a significant reduction in the SRV without adding interface problems, thus improving the performance of III-V compound based solar cells. Another significant benefit to the overall performance of the solar cells can be achieved by a substantial reduction of their large surface optical reflection by the use of a well designed antireflection (AR) coating. In this paper, we demonstrate the effectiveness of using a chemically grown, thermally and chemically stable oxide, not only for surface passivation but also as an integral part of a 3- layer AR coating for thermally diffused p(+)n InP solar cells. A phosphorus-rich interfacial oxide, In(PO3)3, is grown at the surface of the p(+) emitter using an etchant based on HNO3, o-H3PO4 and H2O2. This oxide has the unique properties of passivating the surface as well as serving as a fairly efficient antireflective layer yielding a measured record high AM0, 25 C, open-circuit voltage of 890.3 mV on a thermally diffused InP(Cd,S) solar cell. Unlike conventional single layer AR coatings such as ZnS, Sb2O3, SiO or double layer AR coatings such as ZnS/MgF2 deposited by e-beam or resistive evaporation, this oxide preserves the stoichiometry of the InP surface. We show that it is possible to design a three-layer AR coating for a thermally diffused InP solar cell using the In(PO3)3 grown oxide as the first layer and Al2O3, MgF2 or ZnS, MgF2 as the second and third layers respectively, so as to yield an overall theoretical reflectance of less than 2%. Since chemical oxides are readily grown on III-V semiconductor materials, the technique of using the grown oxide layer to both passivate the surface as well as serve as the first of a multilayer AR coating, should work well for essentially all III-V compound-based solar cells.

Moulot, Jacques↗
NASA NTRS1994

Electrochemical Characterization of InP and GaAs Based Structures for Space Solar Cell Applications.

In this paper the emphasis is on accurate majority carrier concentration EC-V profiling of structures based on Indium Phosphide and Gallium Arsenide, using a newly developed electrolyte based on Hydrogen Flouride, Acetic Acid, Phosphoric Acid, 1-phenyl-2-propanamine and Ammonia Diflouride. Some preliminary data on the use of this electrolyte for determining the energy distribution of surface and deep states of these structures, applicable to fabrication process optimization and radiation induced defects studies of solar cells, are also provided.

Faur, Maria↗
NASA NTRS1994

Status of diffused junction p+n InP solar cells for space applications

Recently, we have succeeded in fabricating diffused junction p(sup +)n(Cd,S) InP solar cells with measured AMO, 25 C open circuit voltage (V(sub OC)) of 887.6 mV, which, to the best of our knowledge, is higher than previously reported V(sub OC) values for any InP homojunction solar cells. The experiment-based projected achievable efficiency of these cells using LEC grown substrates is 21.3 percent. The maximum AMO, 25 C internal losses due to date on bare cells is, however, only 13.2 percent. This is because of large external and internal losses due to non-optimized front grid design, antireflection (AR) coating and emitter thickness. This paper summarizes recent advances in the technology of fabrication of p(sup +)n InP diffused structures and solar cells, resulted from a study undertaken in an effort to increase the cell efficiency. The topics discussed in this paper include advances in: (1) the formation on thin p(sup +) InP:Cd emitter layers, (2) electroplated front contacts, (3) surface passivation and (4) the design of a new native oxide/Al2O3/MgF2 tree layer AR coating using a chemically-grown P-rich passivating oxide as a first layer. Based on the high radiation resistance and the excellent post-irradiation annealing and recovery demonstrated in the early tests done to date, as well as the projected high efficiency and low-cost high-volume fabricability, these cells show a very good potential for space photovoltaic applications.

Faur, Mircea↗
NASA NTRS1994

Status of Diffused Junction p(+)n InP Solar Cells for Space Applications

Recently, we have succeeded in fabricating diffused junction p(+)n(Cd,S) InP solar cells with measured AMO, 25 C open circuit voltage (V(sub OC)) of 887.6 mV, which, to the best of our knowledge, is higher than previously reported V(sub OC) values for any InP homojunction solar cells. The experiment-based projected achievable efficiency of these cells using LEC grown substrates is 21.3%. The maximum AMO, 25 C efficiency recorded to date on bare cells is, however, only 13.2%. This is because of large external and internal losses due to non-optimized front grid design, antireflection (AR) coating and emitter thickness. This paper summarizes recent advances in the technology of fabrication of p(+)n InP diffused structures and solar cells, resulted from a study undertaken in an effort to increase the cell efficiency. The topics discussed in this paper include advances in: 1) the formation of thin p(+) InP:Cd emitter layers, 2) electroplated front contacts, 3) surface passivation and 4) the design of a new native oxide/AI203/MgF2 three layer AR coating using a chemically-grown P-rich passivating oxide as a first layer. Based on the high radiation resistance and the excellent post-irradiation annealing and recovery demonstrated in the early tests done to date, as well as the projected high efficiency and low-cost high-volume fabricability, these cells show a very good potential for space photovoltaic applications.

Faur, Mircea↗
NASA NTRS1993

Progress in p(+)n InP solar cells fabricated by thermal diffusion

The performance results of our most recently thermally diffused InP solar cells using the p(+)n (Cd,S) structures are presented. We have succeeded in fabricating cells with measured AMO, 25 C V(sub oc) exceeding 880 mV (bare cells) which to the best of our knowledge is higher than previously reported V(sub oc) values for any InP homojunction solar cells. The cells were fabricated by thinning the emitter, after Au-Zn front contacting, from its initial thickness of about 4.5 microns to about 0.6 microns. After thinning, the exposed surface of the emitter was passivated by a thin (approximately 50A) P-rich oxide. Based on the measured EQY and J(sub sc)-V(sub oc) characteristics of our experimental high V(sub oc) p(+)n InP solar cells, we project that reducing the emitter thickness to 0.3 microns, using an optimized AR coating, maintaining the surface hole concentration of 3 x 10(exp 18)cm(sup -3), reducing the grid shadowing from actual 10.55 percent to 6 percent and reducing the contact resistance will increase the actual measured 12.57 percent AMO 25 C efficiency to about 20.1 percent. By using our state-of-the-art p(+)n structures which have a surface hole concentration of 4 x 10(exp 18)cm(sup -3) and slightly improving the front surface passivation, an even higher practically achievable AMO, 25 C efficiency of 21.3 percent is projected.

Flood, D. J.↗
NASA NTRS1993

Electrochemical characterization of p(+)n and n(+)p diffused InP structures

The relatively well documented and widely used electrolytes for characterization and processing of Si and GaAs-related materials and structures by electrochemical methods are of little or no use with InP because the electrolytes presently used either dissolve the surface preferentially at the defect areas or form residual oxides and introduce a large density of surface states. Using an electrolyte which was newly developed for anodic dissolution of InP, and was named the 'FAP' electrolyte, accurate characterization of InP related structures including nature and density of surface states, defect density, and net majority carrier concentration, all as functions of depth was performed. A step-by-step optimization of n(+)p and p(+)n InP structures made by thermal diffusion was done using the electrochemical techniques, and resulted in high performance homojunction InP structures.

Wilt, David M.↗
NASA NTRS1992

Closed-ampoule diffusion of sulfur into Cd-doped InP substrates - Dependence of S profiles on diffusion temperature and time

In order to optimize the fabrication of n(+)-p InP solar cells made by closed-ampoule diffusion of sulfur into p-InP:Cd substrates, we have investigated the influence of diffusion conditions on sulfur diffusion profiles. We show that S diffusion in InP is dominated by the P vacancy mechanism and is not characterized by a complementary error function as expected for an infinite source diffusion. The S diffusion mechanism in p-InP is qualitatively explained by examining the depth profiles of S, P, and In in the emitter layer and by taking into account the presence and composition of different compounds found to form in the In-P-S-O-Cd system as a result of diffusion.

Faur, Mircea↗
NASA NTRS1992

Progress in p(+)n InP solar cells fabricated by thermal diffusion

In SPRAT XI, we proposed that p(sup +)n diffused junction InP solar cells should exhibit a higher conversion efficiency than their n(sup +)p counterparts. This was mainly due to the fact that our p(sup +)n (Cd,S) cell structures consistently showed higher V (sub OC) values than our n(sup +)p (S,Cd) structures. The highest V(sub OC) obtained with the p(sup +)n (Cd,S) cell configuration was 860 mV, as compared to the highest V(sub OC) 840 mV obtained with the n(sup +)p (S,Cd) configuration (AMO, 25 C). In this work, we present the performance results of our most recent thermally diffused cells using the p(sup +)n (Cd,S) structure. We have been able to fabricate cells with V(sub OC) values approaching 880 mV. Our best cell with an unoptimized front contact grid design (GS greater than or equal to 10%) showed a conversion efficiency of 13.4% (AMO, 25 C) without an AR coating layer. The emitter surface was passivated by a -50A P rich oxide. Achievement of such high V(sub OC) values was primarily due to the fabrication of emitter surfaces, having EPD densities as low as 2E2 cm(sup -2) and N(sub a)N(sub d) of about 3E18 cm (sup -3). In addition, our preliminary investigation of p(sup +)n structures seem to suggest that Cd-doped emitter cells are more radiation resistant than Zn-doped emitter cells against both high energy electron and proton irradiation.

Faur, Mircea↗
NASA NTRS1992

Electrochemical characterization of InP structures

Electrochemical (EC) techniques represent a simple and yet accurate method to characterize InP and related materials structures. With EC techniques, uncertainties in the measurements arising from factors such as surface effects, the composition and thickness of a front dead layer, the contacts, etc., can be significantly reduced when both a suitable electrolyte is used and the measuring conditions are carefully selected. In this work, the use of photoelectrochemical techniques with InP structures is reported. The work focuses on both the characterization and the optimization of structures grown by thermal diffusion and by epitaxial methods. Characterization of the structures is done by studying the variation in the density of surface states, number of defects, and net majority carrier concentration as a function of material removed. A step-by-step optimization process of n(sup +)p and p(sup+)n InP structures is also described. This involves the passivation and subsequent removal of damaged layers in order to extract the performance parameters of solar cells fabricated with these structures.

Faur, Maria↗
NASA NTRS1991

High resolution electrolyte for thinning InP by anodic dissolution and its applications to EC-V profiling, defect revealing and surface passivation

An extensive experimental study was conducted using various electrolytes in an effort to find an appropriate electrolyte for anodic dissolution of InP. From the analysis of electrochemical characteristics in the dark and under different illumination levels, x ray photoelectron spectroscopy and SEM/Nomarski inspection of the surfaces, it was determined that the anodic dissolution of InP front surface layers by FAP electrolyte is a very good choice for rendering smooth surfaces, free of oxides and contaminants and with good electrical characteristics. The FAP electrolyte, based on HF, CH3COOH, and H2O2 appears to be inherently superior to previously reported electrolytes for performing accurate EC-V profiling of InP at current densities of up to 0.3 mA/sq cm. It can also be used for accurate electrochemical revealing of either precipitates or dislocation density with application to EPD mapping as a function of depth, and for defect revealing of multilayer InP structures at any depth and/or at the interfaces.

Faur, Maria↗
NASA NTRS1991

Investigation of anodic and chemical oxides grown on p-type InP with applications to surface passivation for n(+)-p solar cell fabrication

Most of the previously reported InP anodic oxides were grown on a n-type InP with applications to fabrication of MISFET structures and were described as a mixture of In2O3 and P2O5 stoichiometric compounds or nonstoichiometric phases which have properties similar to crystalline compounds In(OH)3, InPO4, and In(PO3)3. Details of the compositional change of the anodic oxides grown under different anodization conditions were previously reported. The use of P-rich oxides grown either by anodic or chemical oxidation are investigated for surface passivation of p-type InP and as a protective cap during junction formation by closed-ampoule sulfur diffusion. The investigation is based on but not limited to correlations between PL intensity and X-ray photoelectron spectroscopy (XPS) chemical composition data.

Faur, Maria↗
NASA NTRS1991

A comparative study of performance parameters of n(+)-p InP solar cells made by closed-ampoule sulfur diffusion into Cd- and Zn-doped p-type InP substrates

Preliminary results indicate that Cd-doped substrates are better candidates for achieving high efficiency solar cells fabricated by closed-ampoule sulfur (S) diffusion than Zn-doped substrates. The differences in performance parameters (i.e., 14.3 percent efficiency for Cd-doped vs. 11.83 percent in the case of Zn-doped substrates of comparable doping and etch pit densities) were explained in terms of a large increase in dislocation density as a result of S diffusion in the case of Zn-doped as compared to Cd-doped substrates. The In(x)S(y) and probably Zn(S) precipitates in the case of Zn-doped substrates, produce a dead layer which extends deep below the surface and strongly affects the performance parameters. It should be noted that the cells had an unoptimized single layer antireflective coating of SiO, a grid shadowing of 6.25 percent, and somewhat poor contacts, all contributing to a reduction in efficiency. It is believed that by reducing the external losses and further improvement in cell design, efficiencies approaching 17 percent at 1 AMO, 25 degrees should be possible for cells fabricated on these relatively high defect density Cd-doped substrates. Even higher efficiencies, 18 to 19 percent should be possible by using long-lifetime substrates and further improving front surface passivation. If solar cells fabricated on Cd-doped substrates turn out to have comparable radiation tolerance as those reported in the case of cells fabricated on Zn-doped substrates, then for certain space missions 18 to 19 percent efficient cells made by this method of fabrication would be viable.

Faur, Mircea↗
NASA NTRS1991

High performance etchant for thinning p(+)-InP and its application to p(+)n InP solar cell fabrication

An etchant, namely (o-H3PO4)u: (HNO3)v: (H2O2)t: (H2O)1-(u+v+t) is developed for thinning, after contacting, the p(+) emitter layer of p(+)n InP structures made by thermal diffusion. Varying u, v, and t, reproducible etch rates of 5 to 110 nm/min are obtained. After thinning the 0.6- to 2.5-micron thick p(+) InP layer down to 60-250 nm, specular surfaces are obtained at up to 80 nm/min etch rate. Due to its intrinsic qualities the resisual P-rich oxide after thinning the emitter layer provides surface passivation of p(+) InP surfaces and can also serve as a first-layer AR coating.

Faur, Maria↗