Feng, Rui [NETL Site Support Contractor, National Energy Technology Laboratory]

DOE OSTI2025

Process-Microstructure-Property Relationships in Low Heat Input Wire-Arc Additive Manufacturing (WAAM) of Ni-Based Superalloy Haynes 282

Conference presentation on WAAM process optimization on Ni-based superalloy Haynes® 282®. This alloy is targeted for advanced power generation systems for its superior high temperature mechanical properties. Wire-arc additive manufacturing (WAAM) offers attractive cost and materials savings with high deposition rates. Based on initial build process optimization, WAAM blocks were made, and screened for defects using high-throughput CT scanning. The microstructural evolution in arc energy range of 250-700 J/mm was characterized in the as-built and aged conditions, using electron microscopy. Results showed self-consistent microstructure across conditions, with grain size dependence on arc energy, MC and M6C carbides in as-built, and blocky grain boundary M23C6 in as-heat-treated condition. Further reductions in as-built porosity were explored through 20+ combinations of H2 and CO2 additions to shielding gas. Initial results show improved wetting behavior, and bead overlap with up to 1% H2 and up to 0.25% CO2. Combination of experimentally determined datasets provided comprehensive understanding of process-structure-property relationships in WAAM Haynes 282.

Haynes 282↗

DOE OSTI2025

Location-Specific Microstructures and Properties of Haynes 282 Alloy with Laser-Wire DED Processing

In this work, the location-specific microstructures in terms of grain morphology, texture, γ′ precipitates, carbides, and residual strains were investigated in a series of laser-wire direct energy deposition (LW-DED) Haynes 282 alloys with varied processing parameters. A bimodal grain distribution was found in these as-printed and heat-treated alloys with columnar grains within the layers and fine equiaxed grains at the interlayer regions. Dominant <001> texture along the build direction with more obvious <111> orientation preference exists at the bottom layers, compared to the top layers. The gradient γ′-precipitates size distribution contributes predominantly to the observed gradient hardness distribution in the as-printed samples. The heat-treated 282 exhibit comparable yield strengths to those conventionally-processed counterparts, while the observed small deviation in their yield strengths is attributed to the Hall-Petch effect. This work establishes the correlation between location-specific microstructures and mechanical properties, providing valuable insights into future printing parameters and heat-treatment optimization.

Haynes 282↗

DOE OSTI2025

Characterization of Build Parameters and Microstructure in Low Heat Input WAAM of Ni-Based Superalloy Haynes 282

Ni-based superalloy Haynes® 282® is being targeted for various applications in advanced power generation systems for its superior fabricability, weldability, and excellent high temperature creep and corrosion performance. This process optimization study aims to use a low heat-input, high deposition rate, controlled Gas Metal Arc Welding (GMAW) process, Cold Metal Transfer (CMT) by Fronius, attempting to achieve fully dense fabrication and possibly avoid the need for HIP. Twenty-one multilayer blocks (~25x100x40 mm3) were deposited to explore a large set of build parameters variations that focused on varying the travel speed from 14 to 42 inches per minute (ipm) and wire feed speed from 150 to 450 ipm. A strong correlation has been observed between arc energy – controlled primarily by travel and wire feed speed. Initial visual inspection, internal microstructural examination, and computed tomography (CT) have been used to determine the effects of built parameters on evolution of internal porosity and defects. Scanning electron microscopy techniques enabled structural and compositional imaging of heterogeneity and changes in microstructural properties.

additive manufacturing↗

DOE OSTI2025

Characterization of Build Parameters and Microstructure in Low Heat Input WAAM of Ni-Based Superalloy Haynes 282

Ni-based superalloy Haynes® 282® is being targeted for various applications in advanced power generation systems for its superior fabricability, weldability, and excellent high temperature creep and corrosion performance. This process optimization study aims to use a low heat-input, high deposition rate, controlled Gas Metal Arc Welding (GMAW) process, Cold Metal Transfer (CMT) by Fronius, attempting to achieve fully dense fabrication and possibly avoid the need for HIP. Twenty-one multilayer blocks (~25x100x40 mm3) were deposited to explore a large set of build parameters variations that focused on varying the travel speed from 14 to 42 inches per minute (ipm) and wire feed speed from 150 to 450 ipm. A strong correlation has been observed between arc energy – controlled primarily by travel and wire feed speed. Initial visual inspection, internal microstructural examination, and computed tomography (CT) have been used to determine the effects of built parameters on evolution of internal porosity and defects. Scanning electron microscopy techniques enabled structural and compositional imaging of heterogeneity and changes in microstructural properties.

additive manufacturing↗