Engineering topics
Fensin, S. J.
Publications and source records attributed to Fensin, S. J..
Quasi-static and dynamic response of a Cu/Nb composite following equal channel angular extrusion
The article presents a study of the plastic properties of a Cu–18%Nb composite following equal channel angular extrusion under both low- and high-strain rate loadings. The microstructures are characterized by optical and scanning electron microscopy as well as electron backscatter diffraction. Comparisons are also made with a Cu–50%Nb laminate made by accumulative roll bonding. Textures obtained within the respective phases in the extruded composite closely mimic those previously reported for the pure components alone (Cu, Nb). Grain sizes of the major phase (Cu) exhibit broad distributions, due largely to partial recrystallization during the extrusion process. Further re-crystallization is obtained within localized deformation bands produced at high strain rates (3 × 10 3 s –1 ). While the degree of anisotropy and the strain rate sensitivity of the composite response are similar to those of pure Cu after extrusion, the strength levels of the composite are somewhat greater, falling broadly between those obtained in the pure components after extrusion to comparable plastic strains. Furthermore, the implications for selection of composite composition and processing for achieving higher strengths are briefly discussed.
Spall and subsequent recompaction of copper under shock loading
Research was undertaken to study spall and subsequent recompaction of oxygen-free high-thermal-conductivity copper using a single-stage large-bore light gas gun capable of planar impacts. Gun experiments were conducted that produced an initial spall in the target with a subsequent recompaction of the spall damage/layer by the use of layered impactors. Symmetric spall experiments at similar conditions were also conducted as a control to the recompaction experiments. Photonic Doppler velocimetry was used to obtain the velocity history of the target’s back surface; these velocity histories were analyzed, and the results were compared to numerical simulations. After recovery of selected samples, the microstructure was analyzed using optical imaging microscopy and electron backscatter diffraction. Recompaction waves were clearly observed in the time-resolved data obtained at the back surface of the targets. Two different series of experiments were performed to understand the effect of damage morphology on the stress required for spall recompaction. In the initial series, the peak pressure of the first shock was systematically increased to alter the amount of damage in the material. While in the second series, the peak pressure of the second shock was increased, keeping the magnitude of the first shock relatively constant to understand the effect of peak stress on the recompaction process. Findings clearly show that recompaction results in a perturbed band of the microstructure at the location of the expected spall plane in all cases except where the peak stress of the second shock is lower than the critical value.
Low-Stress Shock Hugoniot of AM 304L Stainless Steel
Presentation describes research to determine what, if any, differences exist in the shock Hugoniot between AM 304L stainless steel and forged 304L stainless steel.