NASA NTRS1994

Nondestructive evaluation of fatigue damage in aluminum 2024 by x-ray diffraction

Aluminum alloys are widely used in the automobile and aerospace industries. This is due to their attractive low density-high modulus and low density-high strength characteristics. Unfortunately, cyclic stress-strain deformations alter the microstructure of aluminum alloys when they are placed into service. These structural changes can lead to fatigue damage and ultimately service failure. Since x-ray diffraction analysis is known to be a sensitive nondestructive indicator of structural changes due to deformations, this technique is being used to evaluate changes in the microstructure of cycled aluminum 2024 commercial alloys. Line shapes, widths, and positions in an x-ray diffraction pattern depend on microstructural properties such as grain size, grain orientation, residual stress, microstrain, etc. Changes in the microstructure due to fatigue will appear as changes in the diffraction pattern. One parameter used to characterize a reflection in a diffraction pattern is the full width at half maximum (FWHM). Preliminary x-ray diffraction results on cycled Al 2024 indicate that the (111) and (222) reflections of the matrix phase do not show any variations in the FWHM due to an increase in the fatigue cycles. However, the FWHM of the (200) and (400) reflections of the same phase unexpectedly showed a dramatic decrease. These results can be interpreted as due to the relaxation of some initial nonuniform residual stresses in the matrix phase lattice. Further work is in progress to evaluate the FWHM of the second phase of the cycled alloys.

Ferguson, Milton W.↗

NASA NTRS1993

An experimental investigation of fatigue damage in aluminum 2024-T3 alloys

Aluminum alloys are finding increasing use in the aerospace and automobile industries due to their attractive low density-high modulus and low density-high strength characteristics. Unfortunately, cyclic stress-strain deformation alters the microstructure of the material. These structural changes can lead to fatigue damage and ultimately service failure. Therefore, in order to assess the integrity of the alloy, a correlation between fatigue damage and a measurable microstructural property is needed. Aluminum 2024-T3, a commonly used commercial alloy, contains many grains (individual crystals) of various orientations. The sizes and orientations of these grains are known to affect the strength, hardness, and magnetic permeability of polycrystalline alloys and metals; therefore, perhaps a relationship between a grain property and the fatigue state can be established. Tension-compression cycling in aluminum alloys can also induce changes in their dislocation densities. These changes can be studied from measurements of the electrical resistivities of the materials. Consequently, the goals of this investigation were: to study the grain orientation of aluminum 2024-T3 and to seek a correlation between the grain orientation and the fatigue state of the material; and to measure the electrical resistivities of fatigued samples of aluminum 2024-T3 and to interpret the findings.

Ferguson, Milton W.↗

NASA NTRS1992

Fatigue damage study in aluminum-2024 T3 alloys

The grain structure of aluminum 2024, a commonly used commercial alloy is investigated, and these findings are correlated with the fatigue property of the material. Samples of aluminum 2024 were polished and etched in different reagents. Optical micrographs (at 500X) of samples etched in Keller's reagent revealed grain boundaries as well as some particles present in the microstructure. Normal x-ray scans of samples etched for different intervals of time in Keller's reagent indicate no significant variations in diffraction peak positions; however, the width of the rocking curve increased with the time of etching. These results are consistent with the direct dependence of the width of the rocking curve on the range of grain orientation. Etching removes the preferred orientation layer of the sample produced by polishing; thereby, causing the width to increase.

Ferguson, Milton W.↗

NASA NTRS1991

Experimental determination of residual stress

Residual stresses in finished parts have often been regarded as factors contributing to premature part failure and geometric distortions. Currently, residual stresses in welded structures and railroad components are being investigated. High residual stresses formed in welded structures due primarily to the differential contractions of the weld material as it cools and solidifies can have a profound effect on the surface performance of the structure. In railroad wheels, repeated use of the brakes causes high residual stresses in the rims which may lead to wheel failure and possible derailment. The goals of the study were: (1) to develop strategies for using x-ray diffraction to measure residual stress; (2) to subject samples of Inconel 718 to various mechanical and heat treatments and to measure the resulting stress using x-ray diffraction; and (3) to measure residual stresses in ferromagnetic alloys using magnetoacoustics.

Ferguson, Milton W.↗

NASA NTRS1989

A (13)C NMR analysis of the effects of electron radiation on graphite/polyetherimide composites

Initial investigations have been made into the use of high resolution nuclear magnetic resonance (NMR) for the characterization of radiation effects in graphite and Kevlar fibers, polymers, and the fiber/matrix interface in graphite/polyetherimide composites. Sample preparation techniques were refined. Essential equipment has been procured. A new NMR probe was constructed to increase the proton signal-to-noise ratio. Problem areas have been identified and plans developed to resolve them.

Ferguson, Milton W.↗