Engineering topics

Finn, Scott R.

Publications and source records attributed to Finn, Scott R..

9 records

NASA NTRS1993

Delaminations in composite plates under transverse static or impact loads - A model

A method is presented for calculating the locations, shapes, and sizes of delaminations which occur in a fiber reinforced composite plate subjected to transverse static or dynamic (impact) loads. The plate may be simply supported, clamped, or free along its edges. A model of the delamination formation was developed. This model was then coupled with a finite element analysis. The model and the finite element analysis were implemented by a computer code which can be used to estimate the load at which damage is initiated as well as the locations, shapes, and sizes of the delaminations.

Finn, Scott R.↗

NASA NTRS1993

Delaminations in composite plates under transverse impact loads - Experimental results

Tests were performed measuring the locations and geometries of delaminations in Fiberite T300/976 graphite/epoxy, Fiberite IM7/977-2 graphite-toughened epoxy, and ICI APC-2 graphite/PEEK plates subjected to transverse impact loads. The data provide specific information on the effects of impactor velocity, impactor mass, material, thickness of back ply group, difference in fiber orientation between adjacent ply groups, plate thickness, and impactor nose radius. The data were compared to the results of the Finn-Springer model. The model was found to describe the data with reasonable accuracy.

Finn, Scott R.↗

NASA NTRS1993

Impact damage resistance of composite fuselage structure, part 2

The strength of laminated composite materials may be significantly reduced by foreign object impact induced damage. An understanding of the damage state is required in order to predict the behavior of structure under operational loads or to optimize the structural configuration. Types of damage typically induced in laminated materials during an impact event include transverse matrix cracking, delamination, and/or fiber breakage. The details of the damage state and its influence on structural behavior depend on the location of the impact. Damage in the skin may act as a soft inclusion or affect panel stability, while damage occurring over a stiffener may include debonding of the stiffener flange from the skin. An experiment to characterize impact damage resistance of fuselage structure as a function of structural configuration and impact threat was performed. A wide range of variables associated with aircraft fuselage structure such as material type and stiffener geometry (termed, intrinsic variables) and variables related to the operating environment such as impactor mass and diameter (termed, extrinsic variables) were studied using a statistically based design-of-experiments technique. The experimental design resulted in thirty-two different 3-stiffener panels. These configured panels were impacted in various locations with a number of impactor configurations, weights, and energies. The results obtained from an examination of impacts in the skin midbay and hail simulation impacts are documented. The current discussion is a continuation of that work with a focus on nondiscrete characterization of the midbay hail simulation impacts and discrete characterization of impact damage for impacts over the stiffener.

Dost, Ernest F.↗

NASA NTRS1992

Delaminations in composite plates under transverse static loads - Experimental results

Tests were performed measuring the damage initiation loads and the locations, shapes, and sizes of delaminations in Fiberite T300/976 graphite/epoxy, Fiberite IM7/977-2 graphite-toughened epoxy, and ICI APC-2 graphite-PEEK plates subjected to transverse static loads. The data were compared to the results of the Finn-Springer model, and good agreements were found between the measured and calculated delamination lengths and widths.

Finn, Scott R.↗

NASA NTRS1992

Compressive strength of damaged and repaired composite plates

Tests were performed assessing the effectiveness of repair in restoring the mechanical properties of damaged, solid composite plates made of Fiberite T300/976 graphite-epoxy. Some (75%) or all (100%) of the damaged zone was cut out, and the plate was repaired by plugging and patching the hole. The effectiveness of the repair was evaluated by measuring the compressive strengths of undamaged plates, damaged plates with no cutout, damaged plates with a cutout, and plates that had been repaired.

Finn, Scott R.↗

NASA NTRS1992

Compressive strength of damaged and repaired composite plates

Tests were performed assessing the effectiveness of repair in restoring the mechanical properties of damaged, solid composite plates made either of Fiberite T300/976 graphite-epoxy, Fiberite IM7/977-2 graphite-toughened epoxy, or ICI APC-2 graphite-PEEK. The plate length, the layup and the amount of damage were also varied. Damage was introduced in the plates either by impacting them with a solid projectile or by applying a transverse static load. Some (75 percent) or all (100 percent) of the damaged zone was then cut out, and the plate was repaired by plugging and patching the hole. The effectiveness of the repair was evaluated by measuring the compressive strengths of undamaged plates, damaged plates with no cutout, damaged plates with a cutout, and repaired plates. The data at an intermediate stage of repair provide information on the effect of each repair step on the compressive strength. The results indicated that for the solid plates used in these tests, the repair methods used herein did not improve the compressive strength of already damaged plates.

Finn, Scott R.↗

NASA NTRS1991

Composite plates impact damage - An atlas

The present volume on impact damage in composite plates presents an extensive compendium of visual and graphic data regarding a variety of material and impactor parameters. The photographs are taken with X-ray and C-scan imaging in conjunction with a dye penetrant to show matrix cracks and delaminations. Impact and static-loading tests are performed on plates of graphite-epoxy, graphite-toughened epoxy, and graphite-PEEK materials. The images are presented to yield specific visual data regarding such parameters as impactor velocity, thickness of the back ply group, impactor nose radius, and the effects of multiple delaminations. The images are grouped in eight subsets that correspond to parameters including plate length, material, and the difference in fiber orientation between adjacent ply groups. This substantial volume represents a systematic effort to study the effects of several material parameters on impact damage.

Finn, Scott R.↗

NASA NTRS1991

Delaminations in composite plates under impact loads

A method is presented for calculating the locations, shapes, and sizes of delaminations which occur in a fiber reinforced composite plate subjected to non-penetrating (low velocity) impact of a solid object. The plate may be simply supported, clamped, or free along its edges. A failure model of the delamination formation was developed. This model was then coupled with a finite element analysis. The model and the finite element analysis were then implemented by a computer code (IMPACT-ST) which can be used to estimate the damage initiation load and the locations, shapes, and sizes of the delaminations. Tests were performed measuring the geometries of the delaminations in graphite-epoxy, graphite-toughened epoxy, and graphite-PEEK plates impacted by a projectile with a spherical tip having masses ranging from 0.355 lbm to 0.963 lbm and velocities from 50 in/sec to 225 in/sec. The data were compared to the results of the model, and good agreements were found between the measured and the calculated delamination lengths and widths.

Finn, Scott R.↗

NASA NTRS1989

Delaminations in composite plates caused by non-penetrating impact

A model is presented for estimating the dimensions of delaminations in continuous fiber reinforced composite plates subjected to non-penetrating (low velocity) impact of a solid object. The model is based on dimensional analysis, and results in two simple, closed form expressions, one providing the delamination length, the other the delamination width. Comparisons of delamination lengths and widths calculated by these expressions with experimental data suggest that the model predicts these dimensions with reasonable accuracy.

Finn, Scott R.↗