Diamagnetic studies on as-processed carbon fibers
The Faraday method has been used to measure the diamagnetic susceptibilities of small bundles of aligned carbon fibers of different types at room temperature. It was found that the tensor trace susceptibility of the fibers varies systematically over the range 0.8-20 (in units of -10 to the -6th emu/g) as a function of precursor type and processing history. The susceptibility increases, in general, with increasing nominal treatment temperature and hot stretching, and with increasing tensile elastic modulus. The anisotropy ratio of fibers increases approximately linearly with tensile elastic modulus for all fibers from about 1 for a modulus of about 70 GN/sq m to about 22 for a modulus of 700 GN/sq m in air, and is quantitatively consistent with the layer-plane orientation textures determined by X-ray diffraction when appropriate values of the crystallite principal susceptibilities are used.