Effect of processing parameters and build orientation on microstructure and performance of AISI stainless steel 304L made with selective laser melting under different strain rates
Selective laser melting (SLM) process brings diverse potentials on geometry flexibility; therefore, it is more and more widespread to be employed in fabrication metal alloys served for industries. Nonetheless, a material characterization study is desired to carry on for better understanding the correlation among process, structure, microstructure, and performance. In the current study, the SLM fabricated AISI stainless steel 304L was fabricated with different process parameters and built orientations (horizontal, inclined, and vertical. The tensile behavior was evaluated under different strain rates (0.0001 /s, 0.001 /s, 0.01 /s, and 0.1 /s) and compared to the commercial cold-rolled and annealed counterpart. Grain structures, tensile strength, elongation-to-failure, strain rate sensitivity, work hardening, and fractographic analysis were evaluated in terms of the effect of energy density, build orientation, and strain rate. The output indicates the tensile strength increases with increasing strain rates. On the contrary, the elongation-to-failure shows a decreasing trend with strain rates. Tensile properties of specimens built in the horizontal and inclined orientations are more sensitive to strain rates due to the smaller dimension of grain structures. Tensile anisotropy depends on the energy input, where a high energy density could yield a strong build orientation-dependent anisotropy. Hall-Petch relationship is validated to explain the mechanical anisotropy in different built orientations for SLM alloys. The strain hardening exponent and work hardening rate are demonstrated to be positively correlated, and they increase with smaller grain sizes. The fine dimple features indicate the ductile fracture mode regardless of strain rates. The size of the ductile dimples seems to depend on the strain rates and build orientations.