Comparative Mechanical Properties Analysis of Triple Ion-Beam Irradiated and Neutron Irradiated Potential Plasma Facing Components

Abstract Several classes of materials are being proposed for use in fusion reactors including oxide dispersion strengthened (ODS) and reduced activation ferritic-martensitic (RAF/M) steels to withstand the severe and harsh conditions. In this work, the mechanical properties of a Fe-16Cr-4Al-2W-0.3Ti-0.3Y 2 O 3 (K3) (ODS) ferritic steel and a Fe-8.9Cr-1.1W-0.47Mn-0.2V-0.14Ta-0.11C (Eurofer 97) (RAF/M) steel) after triple ion beam irradiation were locally evaluated utilizing in-situ micro-pillar compression tests, and continuous stiffness/quasi-static nanoindentation. No change in mechanical properties was observed in the K3 ODS steel. However, the Eurofer 97 RAF/M steel exhibited radiation-induced effects via increases in yield strength. Micro-pillar techniques were expanded to neutron-irradiated materials via an in-situ testing technique employing lift-out methods on Fe-14Cr-0.9Ti-0.3Mo-0.25Y 2 O 3 (MA957) ODS ferritic steel. Both the non-irradiated and irradiated compressive yield stresses of the MA 957 micro-pillars were in good agreement with bulk yield stress values reported in the literature, suggesting that the lift-out micro-pillar compression testing technique is a promising method. The demonstration of these techniques on ion beam and neutron irradiated ODS steels and ion beam RAF/M steels gives information to inform models of the material degradation during use in a fusion device.

alloys↗
DOE OSTI2021

Electron microscopy characterization of the fuel-cladding interaction in medium burnup annular fast reactor MOX

In this work, we present electron microscopy data focused on the fuel-cladding interaction layer in annular fast reactor MOX with HT-9 cladding at medium burnup. In agreement with previous literature data, the volatile fission products Cs, Te and I have migrated radially into the extreme fuel periphery and partially interacted with the cladding. The accumulation of Cs has occurred in the outermost rim of the fuel pellet, where grain recrystallization has also been observed. Significant amounts of Pd have been found in the interaction zone, particularly in the sample taken from the upper half of the fissile column where the cladding temperatures are higher. At this axial location, Cr has been enriched at the cladding inner surface and diffused into the fuel. Furthermore, chromium remains mainly in metallic form, but locally formed oxides. The fission products Cs, Te and I are found, with variable composition, in form of nanocrystalline regions dispersed in the metallic Cr-rich layer. The morphology and chemical characteristics of the layer suggest a non-oxidative corrosion mechanism as principal cladding degradation phenomenon occurring in this sample, with local onset of Cr oxidation within the nanocrystalline precipitates.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Cryogenic Stress-Driven Grain Growth Observed via Microcompression with in situ Electron Backscatter Diffraction

The deformation of materials at cryogenic temperature is of interest for space, arctic, and fundamental science applications. In this work, a custom-built cooling system attached to a commercial picoindenter was used for in situ cryogenic microcompression testing of equal-channel angular-pressed copper with real-time electron backscatter diffraction. Stress-driven grain growth at cryogenic temperatures was observed during a series of elastic and plastic deformations. Finally, these results provide direct evidence for the previously predicted phenomenon, whereas previous ex situ examinations demonstrated coarsening after cryogenic loading when samples were not maintained at cryogenic temperatures between deformation and characterization.