Boron and Zirconium from Crucible Refractories in a Complex Heat-Resistant Alloy

In a laboratory study of the factors involved in the influence of induction vacuum melting on 55ni-20cr-15co-4mo-3ti-3al heat resistant alloy, it was found that the major factor was the type of ceramic used as the crucible. The study concluded that trace amounts of boron or zirconium derived from reaction of the melt with the crucible refactories improved creep-rupture properties at 1,600 degrees F. Boron was most effective and, in addition, markedly improved hot-workability.

Decker, R F↗
NASA NTRS1957

Effect of Overheating on Creep-rupture Properties of S-816 Alloy at 1,500 F

The effects of overheats to temperatures of 1650, 1800, 1900, and 2000 F were evaluated in terms of the changes in creep-rupture characteristics at 1500 F of S-816 alloy under stresses within the range of rupture strengths of the alloy for 100 to 1000 hours. Overheat periods were predominantly of 2-minute duration and were applied cyclically at approximately 5- or 12-hour intervals. The possible damage from overheating was believed to include internal metal structure changes induced by exposure to the higher temperatures and loss of life by creep if stress was present during the overheats.

ALLOYS, HEAT-RESISTING↗
NASA NTRS1957

Abnormal Grain Growth in M-252 and S-816 Alloys

An experimental investigation was carried out on air- and vacuum-melted M-252 and S-816 alloys to find conditions of heating and hot-working which resulted in abnormal grain growth. The experiments were mainly limited to normal conditions of heating for hot-working and heat treatment and normal temperatures of solution treatment were used to allow grain growth after susceptibility to abnormal grain growth was developed by various experimental conditions. Results indicated that small reductions of essentially strain-free metal were the basic cause of such grain growth.

MATERIALS, PROPERTIES - STRUCTURE↗
NASA NTRS1957

Influence of Crucible Materials on High-temperature Properties of Vacuum-melted Nickel-chromium-cobalt Alloy

A study of the effect of induction-vacuum-melting procedure on the high-temperature properties of a titanium-and-aluminum-hardened nickel-base alloy revealed that a major variable was the type of ceramic used as a crucible. Reactions between the melt and magnesia or zirconia crucibles apparently increased high-temperature properties by introducing small amounts of boron or zirconium into the melts. Heats melted in alumina crucibles had relatively low rupture life and ductility at 1,600 F and cracked during hot-working as a result of deriving no boron or zirconium from the crucible.

MATERIALS, PROPERTIES - STRESS-RUPTURE↗
NASA NTRS1957

Influence of Hot-Working Conditions on High-Temperature Properties of a Heat-Resistant Alloy

The relationships between conditions of hot-working and properties at high temperatures and the influence of the hot-working on response to heat treatment were investigated for an alloy containing nominally 20 percent molybdenum, 2 percent tungsten, and 1 percent columbium. Commercially produced bar stock was solution-treated at 2,200 degrees F. to minimize prior-history effects and then rolled at temperatures of 2,200 degrees, 2,100 degrees, 2,000 degrees, 1,800 degrees, and 1,600 degrees F. Working was carried out at constant temperature and with incremental decreases in temperature simulating a falling temperature during hot-working. In addition, a few special repeated cyclic conditions involving a small reduction at high temperature followed by a small reduction at a low temperature were used to study the possibility of inducing very low strengths by the extensive precipitation accompanying such properties. Most of the rolling was done in open passes with a few check tests being made with closed passes. Heat treatments at both 2,050 degrees and 2,200 degrees F. subsequent to working were used to study the influence on response to heat treatment.

Ewing, John F↗