NASA NTRS1991

Processing Bi-Pb-Sr-Ca-Cu-O superconductors from amorphous state

The bismuth based high T sub c superconductors can be processed via an amorphous Bi-Pb-Sr-Ca-Cu oxide. The amorphous oxides were prepared by melting the constituent powders in an alumina crucible at 1200 C in air followed by pouring the liquid onto an aluminum plate, and rapidly pressing with a second plate. In the amorphous state, no crystalline phase was identified in the powder x ray diffraction pattern of the quenched materials. After heat treatment at high temperature the amorphous materials crystallized into a glass ceramic containing a large fraction of the Bi2Sr2Ca2Cu3O(x) phase T sub c = 110 K. The processing method, crystallization, and results of dc electrical resistivity and ac magnetic susceptibility measurements are discussed.

Chiang, C. K.↗

NASA NTRS1990

Processing Bi-Pb-Sr-Ca-Cu-O superconductors from amorphous state

Researchers produced superconducting ceramics of the Bi-Pb-Sr-Ca-Cu-O system started from a glass. To form the glass, the mixed oxide powder was melted at 1200 C in air. The liquid was quenched rapidly by pouring it onto an aluminum plate and rapidly pressing with another plate. The quenched compound was in the form of black amorphous solid, whose x-ray powder pattern has no crystalline peaks. After heat treatment at high temperatures, the glass crystallized into a superconductor. The crystalline phases in the superconductor identified using x-ray diffraction patterns. These phases were that associated with the superconducting phases of T(sub c) = 80 K (Bi2Ca1Sr2Cu2Ox) and of T(sub c) = 110 K (Bi2Ca2Sr2Cu3Ox). The dc resistivity and the ac susceptibility of these superconductors were studied.

Chiang, C. K.↗

NASA NTRS1984

Methods for assessing the structural reliability of brittle materials

Failure from contact-induced surface flaws is considered along with controlled indentation flaws for construction of toughness and fatigue master maps, fatigue properties of ceramics with natural and controlled flaws, and a statistical analysis of size and stress state effects on the strength of an alumina ceramic. Attention is also given to dynamic and static fatigue of a machinable glass ceramic, the effect of multiregion crack growth on proof testing, and a fracture mechanics analysis of defect sizes. Other topics explored are related to the effect of temperature and humidity on delayed failure of optical glass fibers, subthreshold indentation flaws in the study of fatigue properties of ultrahigh-strength glass, the lifetime prediction for hot-pressed silicon nitride at high temperatures, static fatigue in high-performance ceramics, and requirements for flexure testing of brittle materials.

Freiman, S. W.↗