Engineering topics

Frimer, Aryeh A.

Publications and source records attributed to Frimer, Aryeh A..

11 records

NASA NTRS2005

Titania Deposition on PMR-15

The formation, degree of crystallinity and adherence of dense titania (TiO2) thin film coatings on a high-temperature polyimide resin (PMR-15) can be influenced by the chemical composition of the polymer surface. Furthermore, solution deposition conditions can be adjusted to provide additional control over the morphology and crystallinity of the titania films. Recipes for solution-based titania deposition that used a slowly-hydrolyzing titanium fluoride salt in the presence of boric acid as a fluoride scavenger allowed growth of films up to 750 nm thick in 22 h. By adjusting solution pH and temperature, either amorphous titania or oriented crystalline anatase films could be formed. Surface sulfonate groups enhance the adhesion of solution-deposited oxide thin film coatings. While most sulfonation procedures severely damaged the PMR-15 surface, the use of chlorosulfonic acid followed by hydrolysis of the installed chlorosulfonyl groups provided effective surface sulfonation without significant surface damage. In some cases, the oxide deposition solution caused partial hydrolysis of the polymer surface, which itself was sufficient to allow adhesion of the titania film through chelation of titanium ions by exposed benzoic acid groups on the polymer surface.

Meador, Mary B.↗

NASA NTRS2005

Tetrahydrophthalic Anhydrides as Addition Curing Polyimide End Caps: Thermal Isomerization of Methylendianiline 3,6-Diphenyltetrahydrophthalic Bisimides

In depth NMR studies confirm that heating a 1:2 mixture of cis, cis, cis 3,6-diphenyltetrahydrophthalic anhydride (end cap 9c) with methylenedianiline at 316 C initially yields the corresponding highly congested cis, cis, cis 3,6-diphenyltetrahydrophthalic bisimide 11, which is converted at this temperature to the observed product, the less hindered trans, cis, trans isomer 12.

Frimer, Aryeh A.↗

NASA NTRS2004

Better End-Cap Processing for Oxidation-Resistant Polyimides

A class of end-cap compounds that increase the thermo-oxidative stab ility of polyimides of the polymerization of monomeric reactants (PM R) type has been extended. In addition, an improved processing proto col for this class of end-cap compounds has been invented.

Meador, Mary Ann B.↗

NASA NTRS2003

New Endcaps for Improved Oxidation Resistance in PMR Polyimides

A polyimide is a polymer composed of alternating units of diamine and dianhydride, linked to each other via an imide bond. PMR polyimides, commonly used in the aerospace industry, are generally capped at each end by an endcap (such as the nadic endcap used in PMR 15) which serves a double function: (1) it limits the number of repeating units and, hence, the average molecular weight of the various polymer chains (oligomers), thereby improving processibility; (2) Upon further treatment (curing), the endcap crosslinks the various oligomer strands into a tough heat-resistant piece. It is this very endcap, so important to processing, that accounts for much of the weight loss in the polymer on aging in air at elevated temperatures. Understanding this degradation provides clues for designing new endcaps to slow down degradation, and prolong the lifetime of the material.

Frimer, Aryeh A.↗

NASA NTRS2003

Reevaluation of Tetrahydrophthalic Anhydride as an End Cap for Improved Oxidation Resistance in Addition Polyimides

Several substituted 1,2,3,6-tetrahydrophthalic anhydride end caps - including the 3-phenyl, 3-methoxy, 3-trimethylsilyloxy, and 3,6-diphenyl analogs - were synthesized via the Diels-Alder condensation of the corresponding butadienes and maleic anhydride. These anhydrides, as well as the commercially available 3-hydro and 4-methyl analogs, were each ground together with methylenedianiline in a 2:1 ratio and heated gradually from 204 C to 371 C, with the thermolysis followed by NMR. Generally speaking, a transformation via monoimide to bisimide was observed in the lower temperature range, followed by competition between crosslinking and aromatization. We believe that this competition produces a substantial percentage of aromatic product, with the concomitant lowering of the relative amount of crosslinking and is responsible for improving both thermal oxidative stability of tetrahydrophthalic end capped polyimides and their substantial frangibility. The thermolysis of the tetrahydrophthalimides under inert atmosphere dramatically lowers the amount of aromatization hence, the mechanism for aromatization is an oxidative one.

Meador, Mary Ann B.↗

NASA NTRS2003

Reevaluation of Tetrahydrophthalic Anydrides as Endcaps for Improved Oxidation Resistance in Addition to Polyimides

Frimer, Aryeh A.↗

NASA NTRS2002

NMR Guided Design of Endcaps With Improved Oxidation Resistance

A polyimide is a polymer composed of alternating units of diamine and dianhydride, linked to each other via an imide bond. PMR polyimides, commonly used in the aerospace industry, are generally capped at each end by a norbornene endcap which serves a double function: (1) It limits the number of repeating units and, hence, the average molecular weight of the various polymer chains (oligomers), thereby improving processibility; (2) Upon further treatment (curing), the endcap crosslinks the various oligomer strands into a tough heat-resistant piece. Norbornenyl-end capped PMR polyimide resins' are widely used as polymer matrix composite materials for aircraft engine applications,2 since they combine ease of processing with good oxidative stability up to 300 C. PMR resins are prepared by a twestep approach involving the initial formation of oligomeric pre-polymers capped at both ends by a latent reactive end cap. The end cap undergoes cross-linking during higher temperature processing, producing the desired low density, high specific strength materials, as shown for PMR-15.

Meador, Mary Ann B.↗

NASA NTRS1999

Approaches to New Endcaps for Improved Oxidation Resistance

Norbornenyl-end capped PMR polyimide resins are widely used as polymer matrix composite materials for aircraft engine applications, since they combine ease of processing with good oxidative stability up to 300 C. PMR resins are prepared by a two-step approach involving the initial formation of oligomeric pre-polymers capped at both ends by a latent reactive end cap. The end cap undergoes cross-linking during higher temperature processing, producing the desired low density, high specific strength materials, for PMR- 15. The end cap facilitates processing by controlling the molecular weight of the oligomer and allowing flow before it cross-links. However, after cross-linking, this very end cap accounts for much of the weight loss in the polymer on aging in air at elevated temperatures. Understanding this degradation provides clues for designing new end caps to slow down degradation, and prolong the lifetime of the material.

Meador, Mary Ann B.↗

NASA NTRS1999

On the Oxidative Degradation of Nadic End-Capped Polyimides: Synthesis and Characterization of Model Compounds for End-Cap Degradation Products - 3

The oxidative degradation of PMR (for polymerization of monomeric reactants) polyimides at elevated temperatures was followed by cross-polarized magic angle spinning (CP-MAS) NMR. Labeling of selected sites in the polymers with C-13 allowed for direct observation of the transformations arising from oxidation processes. The formation of several degradation products has been proposed to be occurring in the cross-links derived from the nadic end caps on oxidation. Model compounds have been synthesized and characterized by CPMAS NMR with both normal and delayed decoupling to distinguish between protonated and unprotonated carbons. Comparison of these spectra to predicted chemical shifts of proposed products for the aged polymer provides further insight to degradation occurring in the cross-linked moieties.

Meador, Mary Ann B.↗

NASA NTRS1997

Oxidative Degradation of Nadic-End-Capped Polyimides: Evidence for Reactions Occurring at High Temperatures - 2

The oxidative degradation of PMR (for polymerization of monomeric reactants) polyimides at elevated temperatures was followed by cross-polarized magic angle spinning (Cp-MAS) NMR. C-13 labeling of selected sites in the polymers allowed for direct observation of the transformations arising from oxidation processes. As opposed to model compound studies, the reactions were followed directly in the polymer. The labeling experiments confirm the previously reported oxidation of the methylene carbon to ketone in the methylenedianiline portion of the polymer chain. They also show the formation of two other oxidized species, acid and ester, from this same carbon. In addition, the technique provides the first evidence of the kind of degradation reactions that are occurring in the nadic end caps. Several PMR formulations containing moieties determined to be present after oxidation, as suggested by the labeling study, were synthesized. Weight loss, FTIR, and natural abundance NMR of these derivatives were followed during aging. In this way, weight loss could be related to the observed transformations.

Meador, Mary Ann B.↗

NASA NTRS1991

New addition curing polyimides

In an attempt to improve the thermal-oxidative stability (TOS) of PMR-type polymers, the use of 1,4-phenylenebis (phenylmaleic anhydride) PPMA, was evaluated. Two series of nadic end-capped addition curing polyimides were prepared by imidizing PPMA with either 4,4'-methylene dianiline or p-phenylenediamine. The first resulted in improved solubility and increased resin flow while the latter yielded a compression molded neat resin sample with a T(sub g) of 408 C, close to 70 C higher than PME-15. The performance of these materials in long term weight loss studies was below that of PMR-15, independent of post-cure conditions. These results can be rationalized in terms of the thermal lability of the pendant phenyl groups and the incomplete imidization of the sterically congested PPMA. The preparation of model compounds as well as future research directions are discussed.

Frimer, Aryeh A.↗