NASA NTRS1992

The interaction of atomic oxygen with thin copper films

A source of thermal, ground-state atomic oxygen has been used to expose thin copper films at a flux of 1.4 x 10 exp 17 atoms/sq cm s for times up to 50 min for each of five temperatures between 140 and 200 C. Rutherford backscattering spectroscopy was used to characterize the oxide formed during exposure. The observations are consistent with the oxide phase Cu2O. The time dependence and the temperature dependence of the oxide layer thickness can be described using oxide film growth theory based on rate limitation by diffusion. Within the time and temperature ranges of this study, the growth of the oxide layers is well described by the equation L(T,t) = 3.6 x 10 to 8th exp(- 1.1/2k sub B T)t exp 1/2, where L,T, and t are measured in angstroms, degrees Kelvin, and minutes, respectively. The deduced activation energy is 1.10 +/- 0.15 eV, with the attendant oxidation rate being greater than that for the corresponding reaction in molecular oxygen.

Gibson, B. C.↗
NASA NTRS1985

Orbital atomic oxygen effects on thermal control and optical materials - STS-8 results

The effects of exposing 23 specimens of optical and thermal control materials to space at 120 km altitude for over 40 hrs during the STS-8 mission are discussed. Ten samples of paint targeted for the Space Telescope (ST) and the Tethered Satellite were exposed, and included polyurethane, oxide, silicone, and glossy black and white samples which were scanned for alterations in the optical properties after being retrieved. Nine mirror-type materials were also investigated, along with silver specimens typical of solar cell interconnects. The oxygen flow at the orbital altitude was 3.5 x 10 to the 20th atoms/cu cm. The exposures caused no degradation of the magnesium fluoride mirror coatings, while the Kapton coating for the ST solar cell panels showed evidence of losing thickness. The Ag solar cell contacts will require coatings to extend their lifetimes. Overcoatings were also proven necessary for inhibiting degradation of painted surfaces.

Whitaker, A. F.↗
NASA NTRS1985

Reaction of metals in lower earth orbit during Space Shuttle flight 41-G

The effects of ambient space environment on metals were studied by exposing specimens of Cu, Ag, Au, Ni, Cr, Al, Pt, and Pd on flight 41-G (STS-17). Data obtained by ellipsometry (ELL), Rutherford backscattering (RBS), and proton-induced X-ray emission (PIXE) before and after flight are summarized. Although the effects of space environment were most pronounced for silver, there were significant changes in the surface properties of the majority of the other metals. The surface optical constants proved to be the most sensitive measure of surface changes. These changes are attributed to the interaction of the metals with atomic oxygen.

Fromhold, A. T., Jr.↗
NASA NTRS1969

Dielectric materials for use in thin-film capacitors

Investigation report presents details of dielectric properties of various metals measured at 300 degrees K for thermally evaporated oxides from 300 to 6000 A in thickness. It is relevant to the medium of integrated circuitry.