Engineering topics
Fu, Zhenyu
Publications and source records attributed to Fu, Zhenyu.
Advanced Electron Microscopy of TRISO coated Particles: FY2021 Overview
Objectives: Understanding Effects of Irradiation on TRISO layers Fission product chemistry and behavior in UCO kernel Identify and Understand Fission Product Transport Mechanisms in TRISO Coated Particles
Microstructural and Micro-Chemical Evolutions in the Irradiated UCO Fuel Kernels of AGR-1 and AGR-2 TRISO Fuel Particles
AGR-1 and AGR-2 TRISO fuel particles were fabricated with slightly different fuel kernel chemical compositions, modified fabrication processes, different fuel kernel diameters, and changed 235U enrichments. To correlate those differences with the fuel kernel responses to neutron irradiations in terms of irradiated fuel microstructure, fission products chemical and physical states, and fission gas bubble evolutions, extensive microstructural and analytical characterizations were conducted. The studies used a state of art transmission electron microscopy (TEM) equipped with Energy-dispersive X-ray spectroscopy (EDS) of four silicon solid-state detectors which have super sensitivity and fast speed. The TEM specimens were prepared from selected AGR-1 and AGR-2 irradiated fuel kernels exposed to safety testing after irradiation. The particles were chosen to represent a representative irradiation conditions with a fuel burnup within the range from 10.8 to 18.6% FIMA, and the time-average volume-average temperatures vary from 1070 to 1287°C. The 235U enrichment was 19.74 wt.% for the AGR1 fuel kernels and 14.03 wt.% for the AGR-2 fuel kernels. The TEM results show that there were significant microstructural reconstructions in the irradiated fuel kernels for both the AGR-1 and AGR-2 fuels. There are four major phases including fuel matrix of UO2 and UC, U2RuC2, and UMoC2 in the irradiated AGR2 fuel kernel. Zr and Nb form solid solution in the UC phase. UMoC2 phase often shows a detectable concentration of Tc. Pd was found to mainly locate in the buffer layer or to be associated with fission gas bubble within the UMoC2 phase. The EDS maps qualitatively show that the rare-earth fission products (Nb, et al.) preferentially reside in the UO2 phase. In contrast, in the irradiated AGR1 fuel kernel, no U2RuC2 or UMoC2 precipitates were positively identified. Instead, there is a high number of rod-shape precipitates enriched with Ru, Tc, Rh, and Pd observed in the fuel kernel center and edge zone. The difference of microstructural and micro-chemical evolutions in irradiated fuel kernels between the AGR-1 and AGR-2 TRISO fuel particle may result from a combined factor of irradiation temperature, fuel geometry and chemical composition. However, the irradiation temperature probably play a more deterministic role. Limited electron energy loss spectroscopy (EELS) characterizations on the AGR2 fuel kernel show that there is nearly no carbon in the UO2 phase while a small fraction of oxygen was detected in the UC/UMoC2 phase.
Advanced Microscopy Report on UCO Fuel Kernels from Selected AGR-1 and AGR-2 Experiments
A variety of neutron irradiation experiments were completed at Idaho National Laboratory (INL) on tristructural isotropic (TRISO) coated particles contained in a graphitic matrix as part of the Advanced Gas Reactor (AGR) fuel development and qualification program. Although the initial advanced microscopy and microanalysis studies on AGR-1 particles focused predominantly on the SiC layer?s role as the main fission-product containment, studies were further expanded to evaluate UCO kernels of selected AGR-1 and AGR-2 coated particles. Fuel kernels tested in the AGR-1 and AGR-2 experiments is composed of a mixture of UO2 and UC, with a nominal as-fabricated stoichiometry of UO1.37 C0.35 and UO1.43 C0.39, respectively. These as-fabricated kernel-stoichiometry values are determined at the completion of kernel fabrication and do not account for any changes that will occur during the subsequent coating and compacting processes.
Advanced Electron Microscope and Micro Analysis of TRISO coated Particles: FY2020 Overview
Objectives Understanding Effects of Irradiation on TRISO layers Fission product chemistry and behavior in UCO kernel Identify and Understand Fission Product Transport Mechanisms in TRISO Coated Particles Outcomes and Impact Impact on Performance Improve Predictive Behavior Modeling Kernel Behavior: Release from kernel; release from whole particle Known Fission Product Transport Mechanisms