DOE OSTI2017

Probing and controlling terahertz-driven structural dynamics with surface sensitivity

Intense, single-cycle terahertz (THz) pulses are powerful tools to understand and control material properties through low-energy resonances, such as phonons. Combining this with optical second harmonic generation (SHG) makes it possible to observe the resulting ultrafast structural changes with surface sensitivity. This makes SHG an ideal method to probe phonon dynamics in topological insulators (TI), materials with unique surface transport properties. Here, we resonantly excite a phonon mode in the TI Bi 2 Se 3 with THz pulses and use SHG to separate the resulting symmetry changes at the surface from the bulk. Furthermore, we coherently control the lattice vibrations with a pair of THz pulses. Lastly, our work demonstrates a versatile, table-top tool to probe and control phonon dynamics in a range of systems, particularly at surfaces and interfaces.

36 MATERIALS SCIENCE↗

DOE OSTI2016

Influence of the carrier mobility distribution on the Hall and the Nernst effect measurements in n-type InSb

In this study, we report magneto-resistance measurements on an n-doped InSb film, to separate the contributions of the electrical currents from the heat currents. We have demonstrated a prototype for a magnetic field sensor which is powered by heat currents and does not require any electrical current. We fabricated two Hall bars, where a low frequency (f = 0.05 Hz) AC current, was applied between the two contacts in one of the Hall bars. Separating the f and 2f components of the voltage measured across the second Hall bar was used to distinguish between the electrical and the heat contributions to the electron currents. Our observations can be modeled using a Gaussian distribution of mobility within the sample.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗

DOE OSTI2014

Effect of catalyst diameter on vapour-liquid-solid growth of GaAs nanowires

GaAs nanowires were grown on (111)B GaAs substrates using the vapour-liquid-solid mechanism. The Au/Pt nanodots used to catalyse wire growth were defined lithographically and had varying diameter and separation. An in-depth statistical analysis of the resulting nanowires, which had a cone-like shape, was carried out. This revealed that there were two categories of nanowire present, with differing height and tapering angle. The bimodal nature of wire shape was found to depend critically on the diameter of the Au-Ga droplet atop the nanowire. Transmission electron microscopy analysis also revealed that the density of stacking faults in the wires varied considerably between the two categories of wire. It is believed that the cause of the distinction in terms of shape and crystal structure is related to the contact angle between the droplet and the solid-liquid interface. The dependency of droplet diameter on contact angle is likely related to line-tension, which is a correction to Young's equation for the contact angle of a droplet upon a surface. The fact that contact angle may influence resulting wire structure and shape has important implications for the planning of growth conditions and the preparation of wires for use in proposed devices.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗