Górnicka, K. | Search NASA

DOE OSTI2022

Ferromagnetism in Pr-rich binary Pr 7 Ru 3 intermetallic compound

We present the synthesis and experimental characterization of the binary intermetallic compound Pr 7 Ru 3 . The polycrystalline sample was prepared by arc melting pure Pr and Ru, followed by homogenization at 500 °C and 600 °C for 48 and 89 h, respectively. Powder x-ray diffraction confirms that Pr 7 Ru 3 crystallizes in an orthorhombic crystal structure (Pnma, space group no. 62) with the lattice parameters: a = 7.3606(7) Å, b = 23.120(1) Å and c = 6.5959(5) Å. Magnetization, resistivity, and heat capacity measurements reveal a ferromagnetic transition in Pr 7 Ru 3 with the Curie temperature T C ~ 24.5 K. The bulk transition is confirmed by a large λ-shape anomaly observed in the specific heat measurement. The magnetic susceptibility above the transition obeys the modified Curie-Weiss law with a positive Curie-Weiss temperature $\ominus$ CW = 30(1) K and an effective magnetic moment of 3.39(1) μ B /Pr. Resistivity data for Pr 7 Ru 3 reveals metallic-like behavior with a clear anomaly at the transition temperature which is smeared by an applied magnetic field. We also synthesized high-quality nonmagnetic analog La 7 Ru 3 for which superconducting transition is observed with T c = 1.95 K, in agreement with the literature.

36 MATERIALS SCIENCE↗

DOE OSTI2021

MgPd 2 Sb : A Mg-based Heusler-type superconductor

Here, we report the synthesis and physical properties of a full Heusler compound, MgPd 2 Sb, which we found to show superconductivity below T c = 2.2 K . MgPd 2 Sb was obtained by a two-step solid-state reaction method and its purity and cubic crystal structure [Fm-3m, a = 6.4523(1) Å ] were confirmed by powder x-ray diffraction. Normal and superconducting states were studied by electrical resistivity, magnetic susceptibility, and heat capacity measurements. The results show that MgPd 2 Sb is a type-II, weak coupling superconductor ( λ e-p = 0.53 ). The observed pressure dependence of T c (ΔT c /p ≈ -0.23 K / GPa ) is one of the strongest reported for a superconducting Heusler compound. The electronic structure, phonons, and electron-phonon coupling in MgPd 2 Sb were theoretically investigated. The obtained results are in agreement with the experiment, confirming the electron-phonon coupling mechanism of superconductivity. We compare the superconducting parameters to those of all reported Heusler-type superconductors.

36 MATERIALS SCIENCE↗