NASA NTRS1993

Fatigue-environment interactions in a SiC/Ti-15-3 composite

Load-controlled isothermal and nonisothermal fatigue lives of a (0-deg)s SiC/Ti-15-3 were evaluated at temperatures between 150 and 550 C and a target strain range of about 0.45 percent. In nonisothermal fatigue tests, load was first cycled at minimum temperature and then temperature was cycled at zero load. For fatigue tests with peak temperatures at or above 300 C, fatigue life was dramatically reduced compared to that at 150 C. The shortest life was produced by the nonisothermal test with the greatest temperature range (Delta T = 400 C) and highest peak temperature (T(max) = 550 C). Vacuum testing showed that much of the life reduction under isothermal and nonisothermal conditions was related to environmental effects, although the nature of the fatigue-environment interaction was decidedly different for the isothermal and nonisothermal test cycles which were studied.

Gayda, J.↗
NASA NTRS1992

Isothermal fatigue behaviour of a (90 deg)8 SiC/Ti-15-3 composite at 426 C

The transverse fatigue behavior of a unidirectional SiC/Ti-15-3 composite is characterized at 426 C. The fatigue behavior of this composite along the (0 deg)8 fiber direction and that of unreinforced Ti-15-3 alloy is compared. It is found that the (90 deg)8 composite fatigue life is much shorter than that of the (0 deg)8 composite. The (90 deg)8 fatigue life is much lower than that of the unreinforced Ti-15-3 alloy. Results from 1D model and fractographic evidence for the (90 deg)8 fatigue behavior indicate that the short life of the composite in this orientation is caused by weak fiber-matrix bond strength.

Gayda, J.↗
NASA NTRS1991

The effect of matrix mechanical properties on (0)8 unidirectional SiC/Ti composite fatigue resistance

The relationship between constituent and MMC properties in fatigue loading is investigated with low-cycle fatigue-resistance testing of an alloy Ti-15-3 matrix reinforced with SiC SCS-6 fibers. The fabrication of the composite is described, and specimens are generated that are weak and ductile (WD), strong and moderately ductile (SM), or strong and brittle (SB). Strain is measured during MMC fatigue tests at a constant load amplitude with a load-controlled waveform and during matrix-alloy fatigue tests at a constant strain amplitude using a strain-controlled waveform. The fatigue resistance of the (0)8 SiC/Ti-15-3 composite is found to be slightly influenced by matrix mechanical properties, and the composite- and matrix-alloy fatigue lives are not correlated. This finding is suggested to relate to the different crack-initiation and -growth processes in MMCs and matrix alloys.

Gabb, T. P.↗
NASA NTRS1991

The effect of porosity and gamma-gamma-prime eutectic content on the fatigue behavior of hydrogen charged PWA 1480

The study addresses the effect of systematically varying gamma-gamma-prime eutectic content and porosity level on the fatigue life of a hydrogen-charged single crystal PWA 1480 superalloy. Four microstructural variants are produced, and differences in gamma-gamma-prime eutectic morphology among the four processing variants are analyzed. Single valued tensile test data indicate that the tensile and yield strength of the PWA 1480 are degraded by hydrogen charging, with the exception of the material given a eutectic solution treatment. It is shown that the reduction of the fatigue life can be minimized by a duplex thermomechanical treatment consisting of a eutectic solution followed by hot isostatic pressing.

Gayda, J.↗
NASA NTRS1991

A model for predicting high-temperature fatigue failure of a W/Cu composite

The material studied, a tungsten-fiber-reinforced, copper-matrix composite, is a candidate material for rocket nozzle liner applications. It was shown that at high temperatures, fatigue cracks initiate and propagate inside the copper matrix through a process of initiation, growth, and coalescence of grain boundary cavities. The ductile tungsten fibers neck and rupture locally after the surrounding matrix fails, and complete failure of the composite then ensues. A simple fatigue life prediction model is presented for the tungsten/copper composite system.

Verrilli, M. J.↗
NASA NTRS1990

Isothermal and nonisothermal fatigue behavior of a metal matrix composite

The isothermal and nonisothermal fatigue resistance of a metal matrix composite (MMC) consisting of Ti-15V-3Cr-3Al-3Sn (Ti-15-3) matrix reinforced by 33 vol pct continuous SiC fibers was investigated. The fibers were nominally oriented parallel to the specimen axis. Isothermal fatigue tests were performed in air at 300 and 550 C. The MMC had good isothermal fatigue resistance at low cyclic stress, with fatigue cracks initiating from fiber-matrix interfaces and foil laminations. At high cyclic stresses, stress relaxation in the matrix reduced isothermal composite fatigue resistance at 550 C. Nonisothermal fatigue loading substantially degraded composite fatigue resistnce. This degradation was produced by a thermomechanical fatigue damage mechanism associated with the fiber-matrix interfaces.

Gabb, T. P.↗
NASA NTRS1990

The effect of hydrogen on the low cycle fatigue behavior of a single crystal superalloy

The present study compares the room temperature fatigue properties of PWA 1480 single crystals containing either normal or elevated hydrogen levels, giving attention to the effects of various levels of HIPing process-controlled porosity on hydrogen-trapping and fatigue life. Hydrogen charging is found to degrade the fatigue lives of alloy samples by an order of magnitude; the magnitude of this degradation is comparable at both high and low porosity. HIPing accomplished a small beneficial effect on the fatigue life of both the hydrogen-charged and uncharged PWA 1480 samples. Fatigue cracks are noted to have consistently initiated at large, near-surface pores. By reducing the size and frquency of the larger pores, HIPing apparently retarded fatigue-crack initiation.

Gayda, J.↗
NASA NTRS1990

High temperature fatigue behavior of tungsten copper composites

The present study investigates the high-temperature fatigue behavior of a 9-v/o tungsten fiber-reinforced copper matrix composite. Load-controlled isothermal fatigue at 260 and 560 C and thermomechanical fatigue (TMF) experiments, both in-phase and out-of-phase between 260 and 560 C, were performed. The stress-strain response under all conditions displayed considerable inelasticity. Strain ratchetting was observed during all the fatigue experiments. For the isothermal fatigue and in-phase TMF tests, the ratchetting was always in a tensile direction, continuing until failure. The ratchetting during the out-of-phase TMF test shifted from a tensile to a compressive direction. For all cases, the fatigue lives were found to be controlled by the damage of the copper matrix. On a stress basis, TMF loading substantially reduced lives relative to isothermal cycling.

Verrilli, M. J.↗
NASA NTRS1990

The isothermal fatigue behavior of a unidirectional SiC/Ti composite and the Ti alloy matrix

The high temperature fatigue behavior of a metal matrix composite (MMC) consisting of Ti-15V-3Cr-3Al-3Sn(Ti-15-3) matrix reinforced by 33 volume percent of continuous unidirectional SiC fibers was experimentally and analytically evaluated. Isothermal MMC fatigue tests with constant amplitude loading parallel to the fiber direction were performed at 300 and 550 C. Comparative fatigue tests of the Ti-15-3 matrix alloy were also performed. Composite fatigue behavior and the in situ stress state of the fiber and matrix were analyzed with a micromechanical model, the Concentric Cylinder Model (CCM). The cyclic stress-strain response of the composite was stable at 300 C. However, an increase in cyclic mean strain foreshortened MMC fatigue life at high strain ranges at 550 C. Fatigue tests of the matrix alloy and CCM analyses indicated this response was associated with stress relaxation of the matrix in the composite and subsequent load shedding to the fibers.

Gayda, John↗
NASA NTRS1989

The high temperature deformation in cyclic loading of a single crystal nickel-base superalloy

The high temperature cyclic stress softening response of the single crystal nickel-base superalloy PWA 1480 was investigated. Specimens oriented near the 001- and 111-lines were tested at 1050 C in low-cycle fatigue and then microstructurally evaluated. The 001- and 111-line specimens had dissimilar flow behavior in monotonic tensile tests, but comparable softening in low-cycle fatigue. This softening was accompanied by rapid generation of dislocation networks at the gamma-gamma-prime interfaces and by a slower time-dependent coarsening of gamma-prime precipitates. Due to the rapid formation of a dislocation substructure at the gamma-gamma-prime interfaces, the cyclic stress softening could be modeled with an existing theory which related cyclic stress to the evolving microstructure and dislocation structure.

Gabb, T. P.↗
NASA NTRS1989

The low cycle fatigue deformation response of a single-crystal superalloy at 650 C

The cyclic stress-strain response and the associated deformation structure of the single crystal nickel-base superalloy PWA 1480 were investigated. Specimens of various crystallographic orientations were tested in low-cycle fatigue (LCF) at 650 C, resulting in a significant tension-compression anisotropy in initial yield strength associated with the shearing of gamma-prime precipitates by dislocation pairs, and a LCF cyclic hardening of the crystals associated with dislocation interactions occurring in the gamma phase. In specimens deforming by slip on a single slip system, dislocations of the primary slip system accumulated in the gamma matrix and formed seesile entanglements. In specimens deforming by slip on several slip systems, the dislocations of the different operative slip systems intersected in the gamma matrix and formed sessile arrangements.

Gabb, T. P.↗
NASA NTRS1989

The role of interfacial dislocation networks in high temperature creep of superalloys

The dislocation networks generated during high-temperature creep of several single-crystal nickel-based superalloys are analyzed. The networks continually evolve during creep at relatively low temperatures or eventually reach a more stable configuration at high temperatures. Specifically, the role of these networks in directional coarsening processes are studied, along with their formation kinetics, characteristics, and stability during creep. The results of this study combined with previous findings suggest that the directional coarsening process is strongly influenced by elastic strain energy. The dislocation networks formed during primary creep are found to be stable during all subsequent creep stages. Aspects of these dislocation networks are determined to be a product of both the applied creep stress and coherency strains.

Gabb, T. P.↗
NASA NTRS1988

Isothermal and bithermal thermomechanical fatigue behavior of a NiCoCrAlY-coated single crystal superalloy

Specimens of single crystal PWA 1480 with group of zone axes (100) orientation, bare, or with NiCoCrAlY coating PWA 276, were tested in low cycle fatigue (LCF) at 650, 870, and 1050 C, and in simplified bithermal thermomechanical fatigue (TMF) tests between these temperatures. These tests were examined as a bridge between isothermal LCF and general TMF. In the bithermal test, an inelastic strain is applied at one temperature, T sub max, and reversed at T sub min. The out-of-phase (OP) test type imposing tension at T sub min and compression at T sub max received most study, since it was more damaging than the in-phase type. Specifically investigated were the effects of: inelastic strain range, the coating, delta T, T sub max, T sub min, and the environment.

Gayda, J.↗
NASA NTRS1988

Fatigue crack propagation of nickel-base superalloys at 650 deg C

The 650 C fatigue crack propagation behavior of two nickel-base superalloys, Rene 95 and Waspaloy, is studied with particular emphasis placed on understanding the roles of creep, environment, and two key grain boundary alloying additions, boron and zirconium. Comparison of air and vacuum data shows the air environment to be detrimental over a wide range of frequencies for both alloys. More in-depth analysis on Rene 95 shows at lower frequencies, such as 0.02 Hz, failure in air occurs by intergranular, environmentally-assisted creep crack growth, while at higher frequencies, up to 5.0 Hz, environmental interaction are still evident but creep effects are minimized. The effect of B and Zr in Waspaloy is found to be important where environmental and/or creep interactions are presented. In those instances, removal of B and Zr dramatically increases crack growth and it is therefore plausible that effective dilution of these elements may explain a previously observed trend in which crack growth rates increase with decreasing grain size.

Gayda, J.↗
NASA NTRS1988

Isothermal and 'bithermal' thermomechanical fatigue behavior of a NiCoCrAlY-coated single crystal superalloy

Specimens of single crystal PWA 1480 with group of zone axes (100) orientation, bare, or with NiCoCrAlY coating PWA 276, were tested in low cycle fatigue (LCF) at 650, 870, and 1050 C, and in simplified bithermal thermomechanical fatigue (TMF) tests between these temperatures. These tests were examined as a bridge between isothermal LCF and general TMF. In the bithermal test, and inelastic strain is applied at one temperature, T sub max, and reversed at T sub min. The out-of-phase (OP) test type imposing tension at T sub min and compression at T sub max received most study, since it was more damaging than the in-phase type. Specifically investigated were the effects of: inelastic strain range, the coating, delta T, T sub max, T sub min, and the environment.

Gayda, J.↗
NASA NTRS1987

The characteristics of gamma-prime dislocation pairs in a nickel-base superalloy

The gamma-prime dislocation pairs of a single crystal nickel-base superalloy, PWA 1480, after tensile and fatigue loading at 650 C are analyzed. The existence and extent of cube cross slip in octahedral slip, and the nature of gamma-prime dislocation pairs in primary cube slip are investigated. It is observed that the PWA 1480 specimens oriented near (001) and (-3 6 10) line directions deform by octahedral slip and specimens oriented near (-1 1 1) and (-2 3 4) lines deform by primary cube slip. It is determined that the overall dislocation distributions are more homogeneous in low cycle fatigue (LCF) loading than in monotonic tensile loading; however, the gamma-prime dislocation pair characteristics are similar for tensile and LCF test specimens. The data reveal that the gamma-prime dislocation pairs of octahedral slip specimens are near-screw and on the cube cross slip plane and for the cube slip specimens, the dislocation pairs are of various characters and on the primary cube slip plane.

Gabb, T. P.↗
NASA NTRS1987

Bithermal Low-Cycle Fatigue Behavior of a NiCoCrAlY-Coated Single Crystal Superalloy

Specimens of a single crystal superalloy, PWA 1480, both bare and coated with a NiCoCrAlY alloy, PWA 276, were tested in low-cycle fatigue at 650 and 1050 C, and in bithermal thermomechanical fatigue tests. In the two bithermal test types, tensile strain was imposed at one of the two temperatures and reversed in compression at the other. In the high-strain regime, lives for both bithermal test types approached that for the 650 C isothermal test on an inelastic strain basis, all being controlled by the low ductility of the superalloy at 650 C. In the low-strain regime, coating cracking reduced life in the 650 C isothermal test. The bithermal test imposing tension at 650 C, termed out-of-phase, also produced rapid surface cracking, but in both coated and bare specimens. Increased crack growth rates also occurred for the out-of-phase test. Increased lives in vacuum suggested that there is a large environmental contribution to damage in the out-of-phase test due to the 1050 C exposure followed by tensile straining at the low temperature.

Gayda, J.↗
NASA NTRS1987

Bithermal low-cycle fatigue behavior of a NiCoCrAlY-coated single crystal superalloy

Specimens of a single crystal superalloy, PWA 1480, both bare and coated with a NiCoCrAlY alloy, PWA 276, were tested in low-cycle fatigue at 650 and 1050 C, and in bithermal thermomechanical fatigue tests. In the two bithermal test types, tensile strain was imposed at one of the two temperatures and reversed in compression at the other. In the high-strain regime, lives for both bithermal test types approached that for the 650 C isothermal test on an inelastic strain basis, all being controlled by the low ductility of the superalloy at 650 C. In the low-strain regime, coating cracking reduced life in the 650 C isothermal test. The bithermal test imposing tension at 650 C, termed out-of-phase, also produced rapid surface cracking, but in both coated and bare specimens. Increased crack growth rates also occurred for the out-of-phase test. Increased lives in vacuum suggested that there is a large environmental contribution to damage in the out-of-phase test due to the 1050 C exposure followed by tensile straining at the low temperature.

Gayda, J.↗