NASA NTRS1980

Coatings for graphite fibers

Graphite fibers released from composites during burning or an explosion caused shorting of electrical and electronic equipment. Silicon carbide, silica, silicon nitride and boron nitride were coated on graphite fibers to increase their electrical resistances. Resistances as high as three orders of magnitude higher than uncoated fiber were attained without any significant degradation of the substrate fiber. An organo-silicone approach to produce coated fibers with high electrical resistance was also used. Celion 6000 graphite fibers were coated with an organo-silicone compound, followed by hydrolysis and pyrolysis of the coating to a silica-like material. The shear and flexural strengths of composites made from high electrically resistant fibers were considerably lower than the shear and flexural strengths of composites made from the lower electrically resistant fibers. The lower shear strengths of the composites indicated that the coatings on these fibers were weaker than the coating on the fibers which were pyrolyzed at higher temperature.

Galasso, F. S.↗

NASA NTRS1980

Coatings for Graphite Fibers

Several approaches for applying high resistance coatings continuously to graphite yarn were investigated. Two of the most promising approaches involved (1) chemically vapor depositing (CVD) SiC coatings on the surface of the fiber followed by oxidation, and (2) drawing the graphite yarn through an organo-silicone solution followed by heat treatments. In both methods, coated fibers were obtained which exhibited increased electrical resistances over untreated fibers and which were not degraded. This work was conducted in a previous program. In this program, the continuous CVD SiC coating process used on HTS fiber was extended to the coating of HMS, Celion 6000, Celion 12000 and T-300 graphite fiber. Electrical resistances three order of magnitude greater than the uncoated fiber were measured with no significant degradation of the fiber strength. Graphite fibers coated with CVD Si3N4 and BN had resistances greater than 10(exp 6) ohm/cm. Lower pyrolysis temperatures were used in preparing the silica-like coatings also resulting in resistances as high as three orders of magnitude higher than the uncoated fiber. The epoxy matrix composites prepared using these coated fibers had low shear strengths indicating that the coatings were weak.

Galasso, F. S.↗

NASA NTRS1979

Study of high resistance inorganic coatings on graphite fibers

Coatings made of boron, silicon carbide, silica, and silica-like materials were studied to determine their ability to increase resistance of graphite fibers. The most promising results were attained by chemical vapor depositing silicon carbide on graphite fiber followed by oxidation, and drawing graphite fiber through ethyl silicate followed by appropriate heat treatments. In the silicon carbide coating studies, no degradation of the graphite fibers was observed and resistance values as high as three orders of magnitude higher than that of the uncoated fiber was attained. The strength of a composite fabricated from the coated fiber had a strength which compared favorably with those of composites prepared from uncoated fiber. For the silica-like coated fiber prepared by drawing the graphite fiber through an ethyl silicate solution followed by heating, coated fiber resistances about an order of magnitude greater than that of the uncoated fiber were attained. Composites prepared using these fibers had flexural strengths comparable with those prepared using uncoated fibers, but the shear strengths were lower.

Galasso, F. S.↗

NASA NTRS1977

Application of diffusion barriers to high modulus fibers

Barrier layers were coated onto high-modulus fibers, and nickel and titanium layers were overcoated as simulated matrix materials. The objective was to coat the high-strength fibers with unreactive selected materials without degrading the fibers. The fibers were tungsten, niobium, and single-crystal sapphire, while the materials used as barrier coating layers were Al2O3, Y2O3, TiC, ZrC, WC with 14% Co, and HfO2. An ion-plating technique was used to coat the fibers. The fibers were subjected to high-temperature heat treatments to evaluate the effectiveness of the barrier layer in preventing fiber-metal interactions. Results indicate that Al2O3, Y2O3, and HfO2 can be used as barrier layers to minimize the nickel-tungsten interaction. Further investigation, including thermal cycling tests at 1090 C, revealed that HfO2 is probably the best of the three.

Veltri, R. D.↗

NASA NTRS1975

Large diameter carbon-boron fiber

Investigations concerned with a development of large-diameter carbon fibers are considered, taking into account the employment of vapor deposition techniques. In the experiments a carbon monofilament substrate is used together with reacting gases which consist of combinations of hydrogen, methane, and boron trichloride. It is found that the described approach can be used to obtain a large-diameter carbon filament containing boron. The filament has reasonable strength and modulus properties.

Veltri, R. D.↗

NASA NTRS1974

Processing eutectics in space

Experimental work is reported which was directed toward obtaining interface shape control while a numerical thermal analysis program was being made operational. An experimental system was developed in which the solid-liquid interface in a directionally solidified aluminum-nickel eutectic could be made either concave to the melt or convex to the melt. This experimental system provides control over the solid-liquid interface shape and can be used to study the effect of such control on the microstructure. The SINDA thermal analysis program, obtained from Marshall Space Flight Center, was used to evaluate experimental directional solidification systems for the aluminum-nickel and the aluminum-copper eutectics. This program was applied to a three-dimensional ingot, and was used to calculate the thermal profiles in axisymmetric heat flow. The results show that solid-liquid interface shape control can be attained with physically realizable thermal configurations and the magnitudes of the required thermal inputs were indicated.

Douglas, F. C.↗

NASA NTRS1974

Processing eutectics in space

Studies which have been done in an earth-based laboratory environment have generally not yielded specimens with the degree of perfection required of the eutectic microstructure to provide test data to evaluate their nonstructural applications. It has been recognized that the low-g environment of an orbiting space laboratory provides a unique environment to re-examine the process of solidification with the goal of producing better microstructures. The objective of this program is to evaluate the feasibility of using the space environment for producing eutectics with microstructures which can be of value on earth. In carrying out this objective, evaluative investigations were carried out on the technology of solidification in a 1-g environment to provide sound baseline data for planning space laboratory experiments.

Douglas, F. C.↗

NASA NTRS1974

Radial and directional solidification of metallic systems in space

Investigation of the solidification behavior of spherical specimens of Ni-12 wt % Sn and Ni-1 wt % Ag that froze radially from the surface toward the center and cylindrical specimens of Al-33 wt % Cu eutectic that froze directionally under appropriately selected conditions of thermal gradient at the solid-liquid interface and growth rate. Possible effects of vacuum and low gravity conditions, under which the spherical specimens were processed, on observed nucleation and growth phenomena are discussed. A genetic explanation is given of observed microstructures, and the distributions of alloying elements is discussed. In directionally solidified eutectic specimens a comparison is made between statistically evaluated growth defects in Skylab and in ground specimens.

Katamis, T. Z.↗

NASA NTRS1974

Research study on materials processing in space, M566 experiment

Specimens of the aluminum-33 wt% copper eutectic partially melted and resolidified in the low effective gravity of the orbiting Skylab were examined and characterized with respect to microstructural defects and thermal conductivity values. The results obtained were compared with similar evaluations of ground-based simulation melt-resolidification experiments and as-prepared unidirectionally solidified specimens. Thermal conductivity data and electrical resistivity data at temperatures from 25 C to 400 C did not show significant differences between ground and space processed specimens. A methology of evaluating the defects in the Al-Al2Cu structure was implemented. A specimen from Skylab 3 showed signs of instability in growth and several grains were found in the ingot. The specimen from Skylab 4 did not show such marked instability in growth and was found to contain fewer defects than the ground-processed specimens. This agrees with data from Georgia Institute of Technology which showed that there were fewer defects in both their Skylab 3 and 4 specimens than in ground processed specimens.

Douglas, F. C.↗

NASA NTRS1974

Eutectic solidification

The possibilities of using the low-gravity space environment for the processing of directionally solidified materials in order to remove the limitations imposed by the L-g earth environment have led to a careful evaluation of the directional solidification process and the results commonly obtained. Defects in the regularity of the microstructure have been identified as one of the most important areas where present processing technology needs to be improved. One-g environment material processing must also be carefully characterized before it can be determined if zero-g processing will produce significant benefits in eutectic and off-eutectic solidification. It is suggested that a combination of experimental and analytical thermal studies will be required to optimize the solidification process in order to minimize the structural defects which occur due to present processing techniques.

Douglas, F. C.↗