Optimizing Active Sites for High CO Selectivity during CO 2 Hydrogenation over Supported Nickel Catalysts
The undesired formation of CH 4 during the hydrogenation of CO 2 remains a great challenge with direct impact on selectivity towards CO or CH 3 OH. In this study, the selectivity of a supported Ni catalyst prepared by traditional impregnation method was found to change after a first CO 2 hydrogenation reaction cycle from 100 to 800 °C. The usually high CH 4 formation was suppressed leading to full selectivity towards CO. This behavior was also observed after the catalyst was treated under methane or propane atmospheres at elevated temperatures. In-situ spectroscopic studies revealed that the accumulation of carbon species on the catalyst surface at high temperature leads to a nickel carbide-like phase. The catalyst regains its high selectivity to CH 4 production after carbon depletion from the surface of the Ni particles by oxidation. However, the selectivity readily shifts back towards CO formation after a new temperature programmed CO 2 hydrogenation cycle. The fraction of weakly adsorbed CO species increases on the carbide-like surface when compared to a clean nickel surface, explaining the higher selectivity towards CO formation. This easy protocol of changing the surface of a common Ni catalyst to gain selectivity represents an important step for the commercial use of CO 2 hydrogenation to CO process together with Fischer-Tropsch applications.