Much of the experimental work on vapor phase lubrication has employed certain organo phosphorous compounds as the vapor phase lubricant. Graham and Klaus, for instance, used tricresyl phosphate (TCP) and tributyl phosphate to vapor phase lubricate a four-ball wear tester using M50 steel balls at 370 C. Makki and Graham were able to vapor phase lubricate a reciprocating pin on plate tribometer using 1018 steel at 280 C with TCP vapor. Although a few organo phosphorous compounds, such as TCP, have been successfully used as vapor phase lubricants in many laboratory experiments, many problems remain unsolved. Two areas of concern relate to the 'durability' of phosphate deposited films and to the ability of the lubricating system to "self-recover" when vapor phase lubricated with an organo phosphorous compound. Durability refers to the ability of the deposited film to provide effective lubrication, for a period of time, after the vapor flow to the lubricating surfaces has been interrupted. Vapor phase lubrication tests, conducted at Cleveland State University with their high temperature tribometer, revealed that when TCP vapor flow to the lubricating surfaces was interrupted the frictional coefficient of the system rapidly increased from a value less than 0.1 to a value of 0.3 which was selected as our failure point. Self-recovery means the ability of the vapor phase lubricant to reduce the frictional coefficient of the lubricating system back down to value less than 0.1 after startup of the interrupted vapor flow. Lubrication tests conducted at Cleveland State University revealed that the high temperature tribometer could not self-recover after startup of the interrupted TCP vapor flow.