The clean activation of methane at low temperatures remains an eminent challenge and a field of competitive research. In particular, on late transition metal surfaces such as Pt(111) or Ni(111), higher temperatures are necessary to activate the hydrocarbon molecule, but a massive deposition of carbon makes the metal surface useless for catalytic activity. However, on very low-loaded M/CeO 2 (M = Pt, Ni, or Co) surfaces, the dissociation of methane occurs at room temperature, which is unexpected considering simple linear scaling relationships. This intriguing phenomenon has been studied using a combination of experimental techniques (ambient-pressure X-ray photoelectron spectroscopy, time-resolved X-ray diffraction, and X-ray absorption spectroscopy) and density functional theory-based calculations. The experimental and theoretical studies show that the size and morphology of the supported nanoparticles together with strong metal–support interactions are behind the deviations from the scaling relations. These findings point toward a possible strategy for circumventing scaling relations, producing active and stable catalysts that can be employed for methane activation and conversion.

03 NATURAL GAS↗

DOE OSTI2020

Ni Nanoparticles on CeO 2 (111): Energetics, Electron Transfer, and Structure by Ni Adsorption Calorimetry, Spectroscopies, and Density Functional Theory

The morphology, interfacial bonding energetics and charge transfer of Ni clusters and nanoparticles on slightly-reduced CeO 2-x (111) surfaces at 100 to 300 K have been studied using single crystal adsorption calorimetry (SCAC), low-energy ion scattering spectroscopy (LEIS), Xray photoelectron spectroscopy (XPS), low energy electron diffraction (LEED) and density functional theory (DFT). The initial heat of adsorption of Ni vapor decreased with the extent of pre-reduction (x) of the CeO 2-x (111), showing that stoichiometric ceria adsorbs Ni more strongly than oxygen vacancies. On CeO 1.95 (111) at 300 K, the heat dropped quickly with coverage in the first 0.1 ML, attributed to nucleation of Ni clusters on stoichiometric steps, followed by the Ni particles spreading onto less favorable terrace sites. At 100 K, the clusters nucleate on terraces due to slower diffusion. Adsorbed Ni monomers are in the +2 oxidation state, and they bind by ~45 kJ/mol more strongly to step sites than terraces. The measured heat of adsorption versus average particle size on terraces is favorably compared to DFT calculations. The Ce 3d XPS lineshape showed an increase in Ce 3+ /Ce 4+ ratio with Ni coverage, providing the number of electrons donated to the ceria per Ni atom. The charge transferred per Ni is initially large but strongly decreases with increasing cluster size for both experiments and DFT, and shows large differences between clusters at steps versus terraces. This charge is localized on the interfacial Ni and Ce atoms in their atomic layers closest to the interface. This knowledge is crucial to understanding the nature of the active sites on the surface of Ni-CeO 2 catalysts for which metal-oxide interactions play a very important role in the activation of O-H and C-H bonds. In conclusion, the changes in these interactions with Ni particle size (metal loading) and the extent of reduction of the ceria help to explain how previously reported catalytic activity and selectivity change with these same structural details.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗