This article describes the synthesis and catalytic properties of supported, 2-3 nm platinum phosphide (PtP 2 ) nanoparticles (NPs). Depending on the P loading, two PtP 2 structures are formed, that is, a PtP 2 surface on a (metallic) Pt core (Pt@PtP 2 ) and single-phase PtP 2 NPs. The structures were determined using extended X-ray absorption fine structure , in situ synchrotron X-ray diffraction, and scanning transmission electron microscopy. In PtP 2 NPs, Pt 2+ ions are geometrically isolated by P 2 2- ions, at a Pt-Pt distance of 4.02 Å, which is much longer than 2.78 Å in (metallic) Pt NPs. The oxidation state of Pt in PtP 2 NPs was determined by in situ X-ray absorption near-edge structure and in situ X-ray photoelectron spectroscopy and was found to be consistent with Pt 2+ ions even after treatment in H 2 at 550 °C. Unlike Pt NPs, which are highly active for propylene hydrogenation at room temperature, PtP 2 NPs are not active below about 150 °C, suggesting the absence of metallic surface Pt. In contrast to metallic Pt, which is poorly selective for acetylene hydrogenation, PtP 2 NPs display high selectivity toward ethylene. PtP 2 , also has high olefin selectivity for propane dehydrogenation, although the rate per g Pt is about 7 times lower than that of metallic Pt NPs of the same size. In situ resonant inelastic X-ray scattering spectroscopy shows that the energy of the filled Pt 5d valence orbitals is 1.5 eV lower than that of metallic Pt, which leads to weaker adsorbate binding consistent with its catalytic properties. Here, a H 2 -stable Pt 2+ site suggests different catalytic applications for these catalysts as compared to Pt NPs.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2020

Composition Tuning of Ru-Based Phosphide for Enhanced Propane Selective Dehydrogenation

Explore the source record for details and available documents.

Ma, Rui↗

DOE OSTI2020

The effect of strong metal–support interaction (SMSI) on Pt–Ti/SiO 2 and Pt–Nb/SiO 2 catalysts for propane dehydrogenation

In this study, we show how strong metal–support interaction (SMSI) oxides in Pt–Nb/SiO 2 and Pt–Ti/SiO 2 affect the electronic, geometric and catalytic properties for propane dehydrogenation. Transmission electron microscopy (TEM), CO chemisorption, and decrease in the catalytic rates per gram Pt confirm that the Pt nanoparticles were partially covered by the SMSI oxides. X-ray absorption near edge structure (XANES), in situ X-ray photoelectron spectroscopy (XPS), and resonant inelastic X-ray scattering (RIXS) showed little change in the energy of Pt valence orbitals upon interaction with SMSI oxides. The catalytic activity per mol of Pt for ethylene hydrogenation and propane dehydrogenation was lower due to fewer exposed Pt sites, while turnover rates were similar. The SMSI oxides, however, significantly increase the propylene selectivity for the latter reaction compared to Pt/SiO 2 . In the SMSI catalysts, the higher olefin selectivity is suggested to be due to the smaller exposed Pt ensemble sites, which result in suppression of the alkane hydrogenolysis reaction; while the exposed atoms remain active for dehydrogenation.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗