DOE OSTI2023

Magnetic phase diagram mapping in Fe 1- x Rh x composition-spread thin films

We have fabricated high-quality polycrystalline Fe 1- x Rh x composition-spread thin films by cosputtering Fe and Rh, and investigated their structural and magnetic transformations as a systematic function of composition. With increasing Rh concentration, Fe 1-x Rh x thin film undergoes from an α' phase to a disordered γ phase and also shows a magnetic transition from a ferromagnetic phase to a paramagnetic phase. Vibrating-sample magnetometry and x-ray magnetic circular dichroism measurements show an antiferromagnetic-ferromagnetic transition in the range of 0.52 < x < 0.58 in the Fe 1- x Rh x composition gradient at room temperature. Based on our structural and magnetic property mapping, we construct a thin-film phase diagram of Fe 1- x Rh x . Compared to reported results in bulk alloys, the antiferromagnetic-ferromagnetic transition in the Fe 1- x Rh x thin films was found to occur at slightly higher Rh concentrations, while the boundary between the pure γ phase and the α'/ γ mixed phase region is shifted to the lower concentration Rh.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Combinatorial Exploration and Mapping of Phase Transformation in a Ni–Ti–Co Thin Film Library

Combinatorial synthesis and high-throughput characterization of a Ni–Ti–Co thin film materials library are reported for exploration of reversible martensitic transformation. The library was prepared by magnetron co-sputtering, annealed in vacuum at 500 °C without atmospheric exposure, and evaluated for shape memory behavior as an indicator of transformation. Composition, structure, and transformation behavior of the 177 pads in the library were characterized using high-throughput wavelength dispersive spectroscopy (WDS), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and four-point probe temperature-dependent resistance (R(T)) measurements. A new, expanded composition space having phase transformation with low thermal hysteresis and Co > 10 at. % is found. Unsupervised machine learning methods of hierarchical clustering were employed to streamline data processing of the large XRD and XPS data sets. Through cluster analysis of XRD data, we identified and mapped the constituent structural phases. Finally, composition–structure–property maps for the ternary system are made to correlate the functional properties to the local microstructure and composition of the Ni–Ti–Co thin film library.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗