A quantitative method to determine the region not influenced by injected interstitial and surface effects during void swelling in ion-irradiated metals

We propose and demonstrate a microstructurally-based experimental method to quantitively determine the depth regions in self-ion-irradiated metals that are affected by the injected interstitial effect and various surface effects, focusing on the choice of safe analysis zones to minimize the impact of these phenomena. The goal is to define the depth ranges where extracted data can be confidently applied to ion-neutron correlations for reactor application. Since ion energies in the range of 1–5 MeV are most frequently employed by the radiation effects community, irradiations were conducted at four energies in this range, all proceeding at 475 °C. The experiment was conducted on relatively pure single crystal iron to focus only on physical phenomena, avoiding the influence of possibly confounding chemical or segregation processes. Care was also taken to minimize the influence of other physical factors such as crystalline orientation. It was shown that, at 475 °C, ion energies of ≤1 MeV were too shallow in penetration and did not yield a safe depth range, but irradiations at 2.5 MeV and above yielded useful safe zones with predicted swelling behavior becoming independent of ion energy. The surface-affected zone width was found to be roughly twice that of the void-denuded zone width and to be independent of accumulated displacement dose. The largest injected-interstitial effect arises from the injected interstitial depression of void nucleation and growth. The interstitial-affected region starts at about one half of the projected range and does not show any “spreading” of its influence in depth as the peak damage level increases from 50 to 100 dpa. This study provides some confidence that enhances the credibility of ion simulation when applied to prediction of void swelling in neutron environments.

36 MATERIALS SCIENCE↗
DOE OSTI2022

LWR Aging Management for Life Beyond 80

While several decades of materials degradation research enabled the current US fleet of Light Water Reactors (LWR) to plan to produce electrical power through extended operations up to 80 years of plant life, it now seems appropriate to evaluate what issues, methods, and timelines need to be considered to meet the expected electric power demands for life beyond eighty (LBE) years. To address these questions, it will be necessary to review the electrical capacity and the projected LWR fleet capacity including new builds and advanced reactors. This effort should begin with a materials degradation assessment focused on known and possible unknown issues using a reduced Expanded Materials Degradation Assessment [1], which was employed to identify knowledge gaps for a second license renewal (60-80 yrs.). The focus of the LBE assessment should include: Establishing a timeline to initiate assessments of possible materials aging issues and to ensure sufficient time to evaluate materials degradation research gaps; assessing components and materials to be evaluated, e.g., metals (reactor pressure vessels and alloys within and outside the pressure boundary), concrete, cables, as well as mitigation methods, advanced monitoring, and validation with ex-service materials; initiating a LBE research plan focused on developing an expanded mechanistic understanding of materials degradation and refined models through Codes and Standards evaluation for use by the nuclear industry; and maintaining and strengthening the nuclear materials human knowledge base to address new and as yet unknown degradation modes.

Chen, Xiang↗
DOE OSTI2022

Microstructural changes of proton irradiated Hastelloy-N and in situ micropillar compression testing of one single grain at different local damage levels

Here, in situ micropillar compression was used to study the deformation of proton-irradiated Hastelloy-N at different damage levels. Multiple pillars were prepared from a single domain along the cross-section of 2.5 MeV proton-irradiated Hastelloy-N. Depending on the location of micropillars, the critical resolved shear stress was obtained as a function of local damage levels. Such an approach eliminates the variation of yield stress due to the difference in the Schmid factor. Microstructural characterization showed that irradiation hardening is contributed by complicated defect structures, including (a) dislocation loops with many in corduroy-like alignments, (2) dislocations pile up, and (3) Cottrell atmosphere. Silicon atoms are found to segregate at dislocation lines and loops and form complicated Cottrell cloud patterns. The critical resolved shear stress, $t_{crss}$, and hardening exponents were both extracted as a function of displacements per atom values up to 2.3. There was a 60% increase in $t_{crss}$ at the highest damage level.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

Orientation-selected micro-pillar compression of additively manufactured 316L stainless steels: Comparison of as-manufactured, annealed, and proton-irradiated variants

In this work, irradiation response and deformation mechanisms of additively manufactured (AM) 316L stainless steel were studied by atomic scale characterization and micro-pillar compression. The AM 316L stainless steels were fabricated by direct energy deposition, a laser-based additive manufacturing process. Irradiation with 2 MeV protons at 360°C was performed to create ~1.8 displacements-per-atom (dpa) damage in AM 316L. Deformation behaviors of the as-manufactured, annealed, and proton-irradiated variants were studied, focusing on the effects of manufacturing-induced pores, residual stress, and irradiation-introduced defects (dislocation loops and voids). Micro-pillars were prepared from grains of pre-selected orientation, avoiding contributions of grain boundaries and allowing determination of resolved shear stress on {111} glide planes. Transmission electron microscopy was used to characterize the pre- and post-deformation microstructure. It was found that in the as-manufactured alloy variant, moving dislocations were the major deformation carrier, with noticeable blocking by fabrication-induced pores, In the annealed variant, hardness was reduced, and deformation was also accomplished by dislocation gliding. In the proton-irradiated variant, significant twinning was observed. Comparing measured resolved shear stress and predicted critical stress for dislocation dissociation, we conclude that irradiation hardening became high enough to activate twinning. Therefore, the deformation mechanism changes from dislocation gliding to twinning. The study is important for both processing optimization and performance evaluation of AM alloys for reactor applications.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Oxide dispersoid coherency of a ferritic-martensitic 12Cr oxide-dispersion-strengthened alloy under self-ion irradiation

Ferritic-martensitic oxide-dispersion-strengthened (ODS) alloy has shown excellent mechanical property and high radiation tolerance. However, the stability of dispersoids during displacive irradiation in the individual ferritic and martensitic phases is unclear. In this work, the correlation among dispersoid coherency, size, density, and matrix phase are studied in dual-phase 12Cr ODS after 100 peak displacements-per-atom (dpa) irradiation at 475°C, using 3.5 MeV Fe 2+ self-ions. The size and density changes of coherent and incoherent dispersoids were analyzed as a function of irradiation depth. The average dispersoid size decreased after irradiation in both phases, and the large incoherent dispersoids in the tempered martensite phase underwent a more dramatic change than those in the ferrite phase. The dispersoid density significantly increased in the ferrite phase within the irradiated region, mostly resulting in an increase in coherent dispersoid density. On the other hand, only a small change in density was observed in the tempered martensite phase for both coherent and incoherent dispersoids. This study shows that dispersoid evolution is dramatically different in ferrite and tempered martensite phases.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Irradiation-induced swelling of pure chromium with 5 MeV Fe ions in the temperature range 450–650 °C

A surface coating using pure chromium has been proposed to increase the accident tolerance of Zircaloy cladding in pressurized water reactors. However, there is not much irradiation experience with Cr alloys and especially pure Cr. In the present study, pure chromium was irradiated with 5 MeV Fe ions to 50 peak dpa (displacements per atom) at temperatures of 450, 500, 550, 600 and 650 °C. Then irradiation at the peak swelling temperature of 550 °C was conducted to 50, 100, 150 peak dpa. Swelling at 50 dpa was observed over the entire temperature range studied, 450–650 °C, but appeared to be decreasing strongly at the temperature boundaries of the experiment. After an initial transient of rapid swelling, chromium was observed to swell at a rate of ~0.03–0.04%/dpa (up to 120 local dpa), which is much lower than pure Fe at 0.2%/dpa. This low swelling rate was found to be relatively insensitive to dpa rate, which varied by a factor of ~2 over the depth of data collection. Here, swelling was observed to begin quickly with an incubation period less than 10 dpa. Self-organization in the form of void ordering was observed to be developing at 50 dpa, becoming better defined with increasing dose. The void alignment direction is determined to be the $\langle$111$\rangle$ axial direction.

36 MATERIALS SCIENCE↗