Community Data Contribution to M.E.T.A. with ATF-relevant Hydrided Zr cladding (Coated and Uncoated)

Since the aftermath of the Fukushima Daiichi loss-of-coolant accident, accident-tolerant fuel (ATF) claddings have been developed to improve the coping times in such events. However, the mechanical performance of ATF cladding is crucial in ensuring that it does not negatively impact the mechanical integrity during all other stages of the nuclear fuel cycle, and the validity of the existing safe operating margins must be verified. However, due to the cladding’s tube geometry and textured anisotropy, determination of apparent mechanical properties under certain deformation paths is challenging. In the uniaxial hoop direction, for instance, the measured mechanical stresses include frictional forces caused by loading mandrels or varying deformation paths in the sample during traditional ring tensile testing. This experimental difficulty is exacerbated by the specimen size. However, addressing these challenges enables irradiation separate-effects investigations in which the materials can be inserted in reactors like the High Flux Isotope Reactor, and reducing the material consumption of commercially irradiated material allows for further post-irradiation examinations. Despite the advantages of reduced-scale mechanical testing, any drawbacks from new specimen geometries must be evaluated, and uncertainties from specimen preparation, setup, and analysis methodologies must be understood.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Hydrogen Effects on Cladding Performance during Simulated Loss of Coolant Accident Testing

Fresh Zircaloy cladding segments were charged with hydrogen and subjected to simulated Loss of Coolant Accident (LOCA) conditions to assess the impact of hydrogen on the cladding mechanical performance and rupture resistance. The cladding rupture temperature decreased by 10 °C for every 100 wppm H added into the system for two different internal pressurization cases. Post-test analysis showed a loss of ductility with increasing hydrogen content, evident through decreased balloon sizes, smaller rupture openings, and sharper rupture interfaces. Digital image correlation was used to map the cladding strain in situ for two cladding segments. An elevated intermediate temperature uniform strain was visible for the hydride cladding, occurring prior to the decreased ductility during balloon and rupture determined from posttest fractography and microscopy. The thermal stability of Zr alloys as a function of hydrogen concentration and the thermal stability of Zr hydride as a function of temperature are likely responsible for the uniform deformation behavior at intermediate temperatures. The present framework for rapid assessment of hydrogen effects on cladding rupture can be utilized as an initial comparison to high burnup cladding thermomechanical response to a LOCA, where local regions may contain high concentrations of precipitated Zr hydride phase.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Hydrogen Effects on Cladding Performance during Simulated Loss of Coolant Accident Testing

Fresh Zircaloy cladding segments were charged with hydrogen and subjected to simulated Loss of Coolant Accident (LOCA) conditions to assess the impact of hydrogen on the cladding mechanical performance and rupture resistance. The cladding rupture temperature decreased by 10 °C for every 100 wppm H added into the system for two different internal pressurization cases. Post-test analysis showed a loss of ductility with increasing hydrogen content, evident through decreased balloon sizes, smaller rupture openings, and sharper rupture interfaces. Digital image correlation was used to map the cladding strain in situ for two cladding segments. An elevated intermediate temperature uniform strain was visible for the hydride cladding, occurring prior to the decreased ductility during balloon and rupture determined from posttest fractography and microscopy. The thermal stability of Zr alloys as a function of hydrogen concentration and the thermal stability of Zr hydride as a function of temperature are likely responsible for the uniform deformation behavior at intermediate temperatures. The present framework for rapid assessment of hydrogen effects on cladding rupture can be utilized as an initial comparison to high burnup cladding thermomechanical response to a LOCA, where local regions may contain high concentrations of precipitated Zr hydride phase.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Sister Rod Destructive Examinations (FY22) Appendix E: Mechanical Testing

As a part of the DOE NE High Burnup Spent Fuel Data Project, Oak Ridge National Laboratory (ORNL) is performing destructive examinations (DEs) of high burnup (HBU) (>45 GWd/MTU) spent nuclear fuel (SNF) rods from the North Anna Nuclear Power Station operated by Dominion Energy. The SNF rods, called sister rods or sibling rods, are all HBU and include four different kinds of fuel rod cladding: standard Zircaloy-4 (Zirc-4), low-tin Zirc-4, ZIRLO, and M5. The DEs are being conducted to obtain a baseline of the HBU rod’s condition before dry storage and are focused on understanding overall SNF rod strength and durability. Composite fuel and defueled cladding will be tested to derive material properties. Although the data generated can be used for multiple purposes, one primary goal for obtaining the post-irradiation examination data and the associated measured mechanical properties is to support SNF dry storage licensing and relicensing activities by (1) addressing identified knowledge gaps and (2) enhancing the technical basis for post-storage transportation, handling, and subsequent disposition.This appendix documents the status of the ORNL Phase 1 DE activities related to the mechanical testing of selected sister rods in Phase 1 of the sister rod test program.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗