DOE OSTI2022

Correlation of Oxygen Anion Redox Activity to In‐Plane Honeycomb Cation Ordering in Na x Ni y Mn 1− y O 2 Cathodes

Sodium‐ion batteries (SIBs) are one of the most promising next‐generation energy storage systems because of their abundant and low‐cost component materials. However, the lower energy density of SIBs compared with lithium‐ion batteries diminishes their practical value proposition. Among the many sodium‐based cathodes, layered transition metal oxides with high sodium content have energy densities comparable with the lithium‐ion battery technology. When charged above 4.1 V, the sodium‐based cathodes often undergo transformations because the activation of oxygen anion redox causes irreversible oxygen release, transition metal ion migration, lattice distortion, and rapid capacity decay. Here, in situ gas analysis is performed to evaluate the lattice oxygen anion redox activity in Na x Ni y Mn 1− y O 2 cathodes with P2 and O3 structural orderings. Operando X‐ray diffraction and neutron diffraction are performed to assess the structural changes related to lattice oxygen redox and transition metal ion migration in Na x Ni y Mn 1− y O 2 cathodes. The results unveil that in‐plane honeycomb cationic ordering can help suppress oxygen anion redox activity, which is critical for the future design of layered transition metal oxide cathodes that are prone to achieve high‐energy for durable SIBs.

25 ENERGY STORAGE↗

DOE OSTI2022

Critical Barriers to Successful Implementation of Earth-Abundant, Mn-Rich Cathodes for Vehicle Applications and Beyond: The Effect of Particle Morphology

As the search for improved and next-generation cathodes continues, it is clear that a deeper understanding of synthesis–structure–electrochemical property relationships is of critical importance. The effects of primary and secondary particle morphologies on various transition metal oxides have been studied, but new findings are still being reported. To date, few studies have focused on the effects of particle morphologies on Li- and Mn-rich oxides (>50% Mn) and even fewer studies have focused on the influence over key properties such as electrode-level impedance. In this study, we report the effects of particle morphologies on the area-specific-impedance (ASI) and thermal behavior of Li- and Mn-rich oxides. Samples with a fixed, layered–layered–spinel (LLS), composition were synthesized with differing primary morphologies and tested under standardized, full-cell protocols. The results suggest that smaller primary particle size (i.e., higher surface area) leads to lower overall ASI, a delay in the increasing impedance at low states-of-charge (SOCs), and surprisingly, improved thermal behavior.

33 ADVANCED PROPULSION SYSTEMS↗

DOE OSTI2021

Operando Analysis of Gas Evolution in TiNb 2 O 7 (TNO)-Based Anodes for Advanced High-Energy Lithium-Ion Batteries under Fast Charging

TiNb 2 O 7 (TNO) is regarded as one of the promising next-generation anode materials for lithium-ion batteries (LIBs) due to its high rate capabilities, higher theoretical capacity, and higher lithiation voltage. Furthermore, this enables the cycling of TNO-based anodes under extreme fast charging (XFC) conditions with a minimal risk of lithium plating compared to that of graphite anodes. Here, the gas evolution in real time with TNO-based pouch cells is first reported via operando mass spectrometry. The main gases are identified to be CO 2 , C 2 H 4 , and O 2 . A solid–electrolyte interphase is detected on TNO, which continues evolving, forming, and dissolving with the lithiation and delithiation of TNO. The gas evolution can be significantly reduced when a protective coating is applied on the TNO particles, reducing the CO 2 and C 2 H 4 evolution by ~2 and 5 times, respectively, at 0.1C in a half-cell configuration. The reduction on gas generation in full cells is even more pronounced. The surface coating also enables 20% improvement in capacity under XFC conditions.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Anionic redox induced anomalous structural transition in Ni-rich cathodes

Ni-rich cathodes have emerged as one of the most promising candidates for power next generation electric vehicles. However, they often suffer from poor capacity retention when charged to high voltages and the origin of this degradation remains elusive. Here, by using high throughput operando neutron diffraction, a universal four-stage structural evolution of Ni-rich cathodes is revealed during the initial cycle for the first time. Particularly, we discovered a universal structural transition in Ni-rich cathodes at ~75% delithiation irrespective of Ni or substituent contents. This transition is hallmarked by the anomalous increase of average TM–O bond lengths, contradicting the conventional wisdom that TM–O bond lengths decrease during charge (oxidation). This anomaly is induced by the direct oxidation of lattice oxygen ions, which is rooted in the drastic decrease of oxygen-to-TM charge transfer gap at high degrees of delithiation. The onset of this anomalous transition matches very well with the onset of oxygen gas release and severe decline of capacity retention in Ni-rich cathodes, suggesting that this bulk structural transition plays an indispensable role in the degradation process. These findings shed light on the elusive degradation mechanism of Ni-rich cathodes, providing valuable clues to stabilize oxidized oxygen ions for stable cycling of layered oxide cathodes at high voltages.

25 ENERGY STORAGE↗

DOE OSTI2020

Probing Thermal Stability of Li-Ion Battery Ni-Rich Layered Oxide Cathodes by means of Operando Gas Analysis and Neutron Diffraction

Thermal stability is a crucial parameter that must be considered within the overall performance metrics of Ni-rich layered oxide cathodes. While the intrinsic structural stability of the cathode materials under thermal conditions is important, it is also critical to consider their reaction with electrolytes. In this study, operando gas analysis, ex situ neutron diffraction, and differential scanning calorimetry were combined to give a broader picture of the thermal stability of Ni-rich NMC cathodes. Li 1– x Ni 0.8 Mn 0.1 Co 0.1 O 2 (NMC811) composite materials with four different states of charge were investigated with and without the presence of an electrolyte. It has been found that electrolyte can greatly accelerate both the structural and thermal decomposition of the cathode materials. A higher state of charge will also make cathode materials more susceptible to thermal shock. Without an electrolyte, O 2 release inducing a structural change from layered to rock salt was the major observation during thermal runaway. However, all samples retained some levels of layered structure after annealing up to 300 °C without the electrolyte. In comparison, almost all the O3-type layered phase transformed to the rock-salt phase for the cathode materials heated with the electrolyte at the same experimental conditions. Moreover, the amount of CO 2 increased by nearly two orders of magnitude when annealing cathode materials with electrolyte in operando gas analysis experiments. More delithiated NMC811 samples released larger amounts of CO 2 at earlier onset temperatures, resonating well with the differential scanning calorimetry (DSC) results showing that more delithiated samples release more heat during thermal shock.

25 ENERGY STORAGE↗

DOE OSTI2020

A Multidimensional Operando Study Showing the Importance of the Electrode Macrostructure in Lithium Sulfur Batteries

Lithium sulfur batteries are one of the most promising next-generation energy storage technologies, because of their impressive theoretical energy density, low materials cost, and relative safety. However, incomplete understanding of their underlying operation mechanisms has hindered their further development and commercialization. In this work, to gain a better understanding of the operation mechanisms in the lithium sulfur battery, three macroscopically different (woven and nonwoven) and microscopically similar (made from the same carbon fibers) free-standing carbon felts are used as the conductive matrices to show how the macrostructure influences the redox reactions and the electrochemical performance. Additionally, an operando radiography and simultaneous in situ electrochemical impedance spectroscopy study are performed to highlight the differences of the carbon hosts and how they compare electrochemically in a lithium sulfur battery. The electrochemical results show that the carbon host with a more open structure results in increased capacity as well as a higher diffusion coefficient. The operando radiography shows that the open structures are more conducive to efficient redox reactivity in forming solid sulfur species, mostly in the form of elongated needlelike structures identified as β-S8, near the end of charge, which is corroborated by the impedance data. The data also reveal a “breathing” mechanism, where the polysulfides are pushed to the edges during discharge and pulled back during charge. Furthermore, it is also revealed that the “breathing” process is a limiting factor in the high rate performance. Overall, this study shows that there is a close relationship between the macrostructure of the carbon matrix and the electrochemical performance of the sulfur cathode.

25 ENERGY STORAGE↗

DOE OSTI2020

High accuracy in-situ direct gas analysis of Li-ion batteries

Cycling of lithium-ion batteries containing Ni-rich NMC cathodes at high voltage involves intense gas generation. From the safety standpoint, it is critical to understand how different gas species respond to changes of upper cut-off voltages. In this manuscript, we introduce a novel experimental set up for real-time analysis of gas generation in prismatic pouch cells. In a typical experiment, a lithium-ion pouch cell is directly connected to a quadruple mass spectrometer by glass capillary. Pressure difference helps move the generated gases to the mass spectrometer column for full analysis. The gaseous species are probed during both formation cycle and aging cycles in Li-ion pouch cells comprising NMC811 cathode and graphite anode. The gases are generated upon the creation of the solid electrolyte interphase on graphite during the first formation charge. Besides ethylene gas, C 2 H 4 , whose occurrence is related to the decomposition of ethylene carbonate, a minor solvent decomposition happened at a lower voltage is demonstrated to be associated with residue water on the electrode. For aging cycles, three upper cut-off voltages have been selected to investigate the gas evolution behavior upon charging to 4.2, 4.4 and 4.6 V. Higher upper cut-off voltages do not affect the amount of O 2 measured as a part of the generated oxygen could have reacted with electrolytes. Quite similar and low amounts of O 2 remain in the cells upon charging to the selected cut-off voltages. On the other hand, the generation of CO 2 has been found to be very sensitive to upper cut-off voltage. During similar aging cycles, 6167 nmol $g_{NMC}^{-1}$ of CO 2 is generated at 4.6 V, versus 1650 nmol $g_{NMC}^{-1}$ of CO 2 at 4.4 V, versus 91 nmol $g_{NMC}^{-1}$ of CO 2 at 4.2 V.

25 ENERGY STORAGE↗

DOE OSTI2020

Probing the Li 4 Ti 5 O 12 Interface Upon Lithium Uptake by Operando Small Angle Neutron Scattering

The formation of a solid–electrolyte interphase (SEI) on the surface of Li 4 Ti 5 O 12 (LTO) has become a highly controversial topic, with arguments for it and against it. However, prior studies supporting the formation of an SEI layer have typically suggested that a layer forms upon cycling of a cell, although the layer is probed after disassembling. In this study, cubic mesostructured LTO is synthesized with crystallite domain sizes between 3 and 4 nm and uniform pores with diameters ≤8 nm. The mean pore size is controlled between 4–8 nm through the use of a triblock amphipathic copolymer with a tunable hydrophobic block as template and by thermal treatment. The LTO morphology obtained is spherical and evolves upon heat treatment. We report these materials show excellent electrochemical performance, including high rate capability and capacity retention. The LTO material is subjected to operando small-angle neutron scattering and X-ray photoelectron spectroscopy experiments, which reveal that the highly debated SEI forms at potentials as high as 2.2 V, first as a LiF-rich layer and subsequently by the growth of a carbonaceous layer. These SEI products form first on the smaller pores before forming on the mesopores.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2020

Perspectives on the relationship between materials chemistry and roll-to-roll electrode manufacturing for high-energy lithium-ion batteries

As lithium-ion battery (LIB) active material and cell manufacturing costs continue to drop with wider adoption of electric vehicles, electrode and cell processing costs remain too high in terms of reaching the ultimate U.S. Department of Energy (DOE) cell cost target of $80/kWh. This paper primarily covers major materials chemistry advancements made over the last 10 years at Oak Ridge National Laboratory (ORNL) in the space of advanced manufacturing science for LIBs with the aim of simultaneously meeting the ultimate cost target, 500 Wh/kg gravimetric energy density, 10-15-min fast charge times, and 1000 deep discharge cycles. Aqeous electrode processing with a variety of active anode and cathode materials is now a standard procedure at the DOE Battery Manufacturing R&D Facility at ORNL (BMF), including the latest processes developed for Ni-rich cathodes. New results on cobalt-free LiNi 0.8 Fe 0.1 Al 0.1 O 2 (NFA 811) are also included and discussed in an electrode processing advantage context. In addition, colloidal processing advancements have been made for Si/C composite anodes for achieving >600 mA h/g capacities. Optimization of electrode coating parameters and drying protocols have been completed, which has elucidated how key processing variables need to be changed when parameters such as slurry solids loading, solvent type, and wet electrode thickness are changed. ORNL has also increased the line speeds at which thick cathodes can be processed using ultra-fast electron beam (EB) curing and substantially decreased formation cycling times to <1 day. Finally, key details of these advancements are discussed in the context of materials chemistry and process-property-performance relationships.

25 ENERGY STORAGE↗