Engineering topics

George, Jaime L.

Publications and source records attributed to George, Jaime L..

6 records

DOE OSTI2024

Thermo-rheological snapshot of melter feed conversion to glass

Slurry feed charged into an electric melter creates a layer of reacting and melting material (termed cold cap) that floats on the surface of molten glass. The rheological behavior of heated melter feed affects the spreading of slurry at the top of the cold cap and the stability of the primary foam, affecting cold-cap coverage and melter plenum temperatures. The apparent viscosity of a high-alumina high-level waste melter feed was assessed by thermomechanical analysis, high-temperature viscometer, and the hot stage microscopy method, yielding viscosity estimates from ≈10 7.5 Pa s at 550°C to ≈10 2.5 Pa s at 1050°C. As the temperature of feed materials increased, their state changed from rigid solid to dilatant fluid, to pseudoplastic bubbly liquid with dissolving solids, to fully developed foam, and finally to Newtonian glass melt.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2024

Direct Feed High-Level Waste APPS Model Glass Testing (DFHLW APPS) Matrix

This report summarizes the data collected during the batching and melting of the Direct Feed High-Level Waste APPS Model Glass Matrix (DFHLW APPS) to serve as a quality-assured validation of the Aspen Process Performance Simulation (APPS) formulation method. Of 15 glasses tested, 12 satisfied all target property constraints. Two glasses, APPS-05 and -06, formed nepheline on canister centerline cooling heat-treatment and failed the Product Consistency Test response limits. Glass APPS-07-2 formed unacceptably high concentrations of crystals (primarily Na3Nd(PO4)2) when heat treated at 950 °C. All other glasses were found to be satisfactory. The measured property values were compared to predicted values from a set of current models. In many cases the current models were found to be inadequate for design of DFHLW glasses. These models are being adjusted to correct for mispredictions. Other models, e.g., density, toxicity characteristic leaching procedure, and sulfur solubility, are adequate for formulation of DFHLW glasses.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2024

Evaluating Iodine Immobilization Technologies: Cermets, Polycermets, and Polyhalmets

The work in this report documents the efforts conducted to assess the feasibility of some of the ideas documented in Pacific Northwest National Laboratory invention disclosure reports (IDRs) including: 1) Iodine capture in polyacrylonitrile (PAN)-containing composite sorbents (32451-E). In this work, the composites evaluated included Ag0, Bi0, Cu0, Bi2S3, and Cu2S embedded in PAN. 2) Metal iodide removal from these sorbents through dissolution in dimethyl sulfoxide (DMSO) (32729-E). In this work, PAN dissolution was evaluated for multiple types of sorbents including Ag-Pan, Bi-PAN, Cu-PAN, Bi2S3-PAN, and Cu2S-PAN. 3) Using metal-sulfide sorbents for iodine capture (32647-E). In this work, the composites evaluated under this IDR included Ag2S, Bi2S3, and Cu2S embedded in PAN. 4) Using low-melting metals to immobilize (encapsulate) iodine-loaded and polymer-containing sorbents into polymer-ceramic-metal (called polycermet) or polymer-halide-metal (called polyhalmet) composite waste forms (32625-E). In this work, the iodine-loaded PAN composites included AgI-PAN, BiI-PAN, and CuI-PAN. 5) Ceramic-metal composite waste form synthesis of polymer-containing materials using low-melting metals like bismuth, tin, or bismuth-tin alloys (32537-E). In this work, the metals evaluated included Bi, 58Bi-42Sn eutectic. 6) Cermets for immobilizing commercial sorbents loaded with radioiodine (32806-E). In this work, AgIX (iodine-loaded silver faujasite zeolite) was evaluated in cermet form.

38 RADIATION CHEMISTRY, RADIOCHEMISTRY, AND NUCLEA↗

DOE OSTI2024

Viscosity of transient glass-forming melt and its relation to foaming during batch-to-glass conversion

Primary foam, which affects the heat transfer into the glass batch and the final glass quality, occurs when a sufficient quantity of transient glass-forming melt evolves with viscosity low enough to close the open porosity of the reacting glass batch. To better understand how the fraction of transient melt and its viscosity affect the primary foam temperature range, we determined, with x-ray diffraction, the fraction and composition of the transient glass-forming melt in a heated waste glass melter feed as a function of temperature. Then we prepared a set of transient melts that occurred within the foaming temperature interval and measured their viscosities with spindle and falling sphere viscometers. Further, the results agree with the Adam-Gibbs and VFT viscosity-composition models, even for transient melt compositions outside of the models compositional validity range. As silica and other refractory particles dissolved in the predominantly borate transient melt while temperature increased, viscosity increased from the initial value of ~500 Pa s at the onset of foaming (~650°C) to a maximum of ~770 Pa s when silica dissolution was almost complete (~700°C). As temperature increased further, transient melt viscosity decreased to ~220 Pa s (~850°C) when the primary foam collapsed.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Crystalline versus Glassy Nature of Iron Phosphate Waste Forms Subjected to Different Slow Cooling Curves

This report provides experimental details and associated results on the elemental distributions (compositions), crystalline/amorphous phase distributions, and microstructures for iron phosphate reference materials (DPF5-336) made with different cooling curves and starting from different temperatures (i.e., 1050°C and 1200°C). The primary goal of this work was to evaluate the properties of the DPF5- 336 reference material after it was melted and cooled at different rates to simulate the cooling profile of different types of canisters. Crystal fractions across the SCC#2, SCC#3, and SCC#5 samples were all similar ranging in crystal content of 35.66–41.14 mass% with amorphous fractions being the balance (64.34–58.86 mass%, respectively). This shows that the heat treatment profile did not seems to greatly affect either the total crystal content or the phase distributions. The quenched sample was almost completely amorphous (99.55 mass%) with very small peaks identified as Li 3 Fe 2 (PO 4 ) 3 whereas the SCC-treated materials showed peaks for what appear to be ten separate phases present in various concentrations. Another goal of these experiments was to see how the phase distribution affected chemical durability of these waste forms, but that information is being collected at Argonne National Laboratory and will be published in a separate report

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2023

Formulation and testing of a high-tin borosilicate nuclear waste glass for in-can melting

Here, borosilicate waste glasses were successfully developed to immobilize two high-level waste raffinate streams via an in-can melter process with an Inconel 601 canister at 1050 °C. Measured viscosity and crystallinity thermal profiles were within the targeted processing constraints for the in-can melter process. Measured chemical durability of the glass by ASTM C1285–21 (Method A), ranged from normalized loss of boron, NL(B) = 1.44 – 2.65 g•m -2 , and NL(B) decreased with increased waste loading, accompanied by increased SnO 2 crystallinity. Measured corrosion of the in-can melter canister by a glass melt showed that Inconel 601 performed well at 1100 °C for up to 500 hr. Resistance polarization measurements versus time revealed that Inconel 601 corrosion rates in (and by) glass melts decreased from an initial rate of 63 mm•y -1 down to 10.2 mm•y -1 after 137 h with increased duration, which was attributed to formation of an oxide passivation layer (mainly Cr 2 O 3 ) at the alloy-glass interface.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗