Germanton, Gary | Search NASA

DOE OSTI2024

Insights into Preceramic Polymer-Based Additive Manufacturing Inks via Rheological and Scattering Studies of Preceramic Polymer-Grafted Nanoparticles Suspended in Polycarbosilane

Preceramic polymers (PCPs) offer advantages in producing ceramics due to their processability and ability to tailor the final chemistry of the produced material. However, challenges such as volumetric shrinkage and mass loss during pyrolysis often result in polymer-derived ceramics containing pores and cracks. PCP-grafted ceramic nanoparticles (PCPGNPs) have been proposed and studied as a route to mitigate the shrinkage issues associated with neat PCPs. Prior studies on PCPGNPs have principally focused on the synthesis and characterization of neat materials. Dispersing PCPGNPs in commercial preceramic polymer is another attractive, but underexplored, route to control the rheological and char yield properties of PCP systems. In this work, a systematic rheological study of commercial PCP (SMP-877) and PCPGNP (silica with poly(1,1-dimethylpropylsilane) corona) mixtures was executed to develop design rules for the processing of such systems. A rheological study demonstrated the effect of increasing particle concentration on network formation with percolation occurring between 50 and 60 wt %. Samples above the percolation threshold exhibited higher viscosities and rapid shear thinning thus demonstrating their direct-write printability. X-ray photon correlation spectroscopy (XPCS) corroborated the rheology and showed two diffusive modes when the material was above percolation. Mixtures of PCPGNPs and SMP-877 had synergistically higher char yields upon thermal treatment and pyrolysis. XPCS and rheological measurements during thermal treatment identified thermal jamming of the polymer grafts as a key factor in improving the char yield. In conclusion, with the insights gained here, we expect these mixed systems to provide attractive feedstocks for polymer-derived ceramics, with proof-of-principal application as feedstocks for direct ink write (DIW) additive manufacturing.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Influence of Thermal Treatment on Preceramic Polymer Grafted Nanoparticle Network Formation: Implications for Thermal Protection Systems and Aerospace Propulsion Components

Preceramic polymer grafted nanoparticles (PCP GNPs) offer potential advantages in the production of polymer-derived ceramic composites compared to neat preceramic polymers (PCPs), such as reduced thermal shrinkage and increased char yield. In comparison to traditional composites (particles + free polymer), PCPs avoid issues of compatibility, agglomeration, and phase separation during processing and provide routes to control nanoparticle arrangement. Prior literature has established that the conversion efficiency of PCPs and PCP GNPs to ceramics and ceramic composites is linked to the thermal pretreatment of these precursor polymers (e.g., curing). In this paper, we investigate the material transformations that occur when exposing PCP GNPs to a low-temperature thermal treatment (≤250 °C) prior to pyrolysis. The PCP GNPs explored in this study possessed silica nanoparticle cores but were distinct in their PCP coronas, having poly(1,1-dimethylpropylsilane) (allyl-GNP)- or poly(1,1-dimethylbenzylethylsilane) (styryl-GNP)-grafted polymers. After undergoing low-temperature thermal treatment, these PCP GNPs exhibited increased char yield at 800 °C; however, unlike commercial PCPs (e.g., allylhydridopolycarbosilane (SMP-10)), obvious cross-linkable sites are not present in the PCP corona structure. Differential scanning calorimetry, oscillatory rheology, and X-ray photon correlation spectroscopy were utilized to elucidate the thermally induced material changes in the allyl- and styryl-GNPs. Thermally induced changes to the structure and behavior of the PCP GNPs were determined to be linked to the chemical structure of the grafted polycarbosilane chains. Styryl-GNPs experienced a curing event between 180 and 250 °C, effecting the formation of a network, which contributed to char yield improvement (at 800 °C). The nanoscale dynamics of this material also shows a transition from diffuse behavior to ballistic behavior because of the cross-linking event. Conversely, the allyl-GNPs did not exhibit a curing event under heat treatment but did show an increase in thermally induced physical cross-linking. The allyl-GNP physical network is stronger after the first cycle of thermal treatment, and it is considered that this contributed to the improvement in char yield post thermal treatment. The advancements in the understanding of the cross-linking behavior of these hybrid materials are expected to advance the application of these materials to turbine engine, advanced friction, and heat-shielding components.

36 MATERIALS SCIENCE↗