Engineering topics

Ghosn, Louis

Publications and source records attributed to Ghosn, Louis.

11 records

NASA NTRS2015

Mechanical Properties of Air Plasma Sprayed Environmental Barrier Coating (EBC) Materials

Development work in Environmental Barrier Coatings (EBCs) for Ceramic Matrix Composites (CMCs) has focused considerably on the identification of materials systems and coating architectures to meet application needs. The evolution of these systems has occurred so quickly that modeling efforts and requisite data for modeling lag considerably behind development. Materials property data exists for many systems in the bulk form, but the effects of deposition on the critical properties of strength and fracture behavior are not well studied. We have plasma sprayed bulk samples of baseline EBC materials (silicon, ytterbium disilicate) and tested the mechanical properties of these materials to elicit differences in strength and toughness. We have also endeavored to assess the mixed-mode fracture resistance, Gc, of silicon in a baseline EBC applied to SiCSiC CMC via four point bend test. These results are compared to previously determined properties of the comparable bulk material.

Ceramic Matrix Composites (CMC's)↗

NASA NTRS2011

Burst Pressure Failure of Titanium Tanks Damaged by Secondary Plumes from Hypervelocity Impacts on Aluminum Shields

Metallic pressure tanks used in space missions are inherently vulnerable to hypervelocity impacts from micrometeoroids and orbital debris; thereby knowledge of impact damage and its effect on the tank integrity is crucial to a spacecraft risk assessment. This paper describes tests that have been performed to assess the effects of hypervelocity impact (HVI) damage on Titanium alloy (Ti-6Al-4V) pressure vessels burst pressure and characteristics. The tests consisted of a pair of HVI impact tests on water-filled Ti-6Al-4V tanks (water being used as a surrogate to the actual propellant) and subsequent burst tests as well as a burst test on an undamaged control tank. The tanks were placed behind Aluminum (Al) shields and then each was impacted with a 7 km/s projectile. The resulting impact debris plumes partially penetrated the Ti-6Al-4V tank surfaces resulting in a distribution of craters. During the burst tests, the tank that failed at a lower burst pressure did appear to have the failure initiating at a crater site with observed spall cracks. A fracture mechanics analysis showed that the tanks failure at the impact location may have been due to a spall crack that formed upon impact of a fragmentation on the Titanium surface. This result was corroborated with a finite element analysis from calculated Von-Mises and hoop stresses.

Nahra, Henry↗

NASA NTRS2009

Environmental Barrier Coatings for Turbine Engines: A Design and Performance Perspective

Ceramic thermal and environmental barrier coatings (TEBC) for SiC-based ceramics will play an increasingly important role in future gas turbine engines because of their ability to effectively protect the engine components and further raise engine temperatures. However, the coating long-term durability remains a major concern with the ever-increasing temperature, strength and stability requirements in engine high heat-flux combustion environments, especially for highly-loaded rotating turbine components. Advanced TEBC systems, including nano-composite based HfO2-aluminosilicate and rare earth silicate coatings are being developed and tested for higher temperature capable SiC/SiC ceramic matrix composite (CMC) turbine blade applications. This paper will emphasize coating composite and multilayer design approach and the resulting performance and durability in simulated engine high heat-flux, high stress and high pressure combustion environments. The advances in the environmental barrier coating development showed promise for future rotating CMC blade applications.

Zhu, Dongming↗

NASA NTRS1997

Characterization of Damage Accumulation in a C/SiC Composite at Elevated Temperatures

This research is part of a program aimed to evaluate and demonstrate the ability of candidate CMC materials for a variety of applications in reusable launch vehicles. The life and durability of these materials in rocket and engine applications are of major concern and there is a need to develop and validate life prediction methodology. In this study, material characterization and mechanical testing was performed in order to identify the failure modes, degradation mechanisms, and progression of damage in a C/SiC composite at elevated temperatures. The motivation for this work is to provide the relevant damage information that will form the basis for the development of a physically based life prediction methodology.

Telesman, Jack↗

NASA NTRS1997

Stress Intensity Factor Solutions for Multiple Edge Cracks in Ceramic Matrix Composites

NASA Lewis Research Center conducted a study to determine the stress intensity factor solutions for periodic arrays of bridged cracks for various crack spacings and crack lengths. Initially, the stress intensity factor of an array of unbridged multiple edge cracks was determined under constant global displacement as well as at a point load along the crack wake. These solutions are expected to contribute toward the development of a damage-based life-prediction methodology for CMC engine components.

Ghosn, Louis↗

NASA NTRS1994

Fracture Behavior of Ceramics Under Displacement Controlled Loading

A Mode I fracture specimen and loading method has been developed which permits the observation of stable crack extension in monolithic and in situ toughened ceramics. The developed technique was used to conduct room temperature tests on commercial grade alumina (Coors' AD-995) and silicon nitride (Norton NC-132). The results of these tests are reported. Crack growth for the alumina remained subcritical throughout testing revealing possible effects of environmental stress corrosion. The crack growth resistance curve for the alumina is presented. The silicon nitride tests displayed a series of stable (slow) crack growth segments interrupted by dynamic (rapid) crack extension. Crack initiation and arrest stress intensity factors, K(sub Ic) and K(sub Ia), for silicon nitride are reported. The evolution of the specimen design through testing is briefly discussed.

Calomino, Anthony↗

NASA NTRS1991

Mode-II-Fracture Specimen And Holder

Test specimen and loading frame developed for fatigue and fracture testing of materials under mode-II (sliding-mode) loading. Assembly placed in compression-testing machine. Loads directed oppositely along centerline cause self-similar crack to propagate. Enables consistently accurate alignment of specimens before insertion of specimen/frame assemblies into compression-testing machine. Makes design attractive for testing in hostile environments in which access to machine or furnace limited. Additional feature, with little or no modification, placed horizontally into impact testing machine and subjected to loading at high speeds.

Buzzard, Robert J.↗

NASA NTRS1991

Fatigue crack growth in a unidirectional SCS-6/Ti-15-3 composite

An investigation was conducted to characterize and model the fatigue crack growth (FCG) behavior of an SCS-6/Ti-15-3 metal matrix composite. Part of the study was conducted using a fatigue loading stage mounted inside a scanning electron microscope (SEM). The results of the study reveal that the fatigue crack growth behavior of the composite is a function of specimen geometry, fiber orientation, and interaction of local stress fields with the highly anisotropic composite. In the case of (0)8 oriented single edge notch specimens and (90)8 oriented compact tension (CT) specimens, the crack growth was normal to the loading direction. However, for the (0)8 CT specimens, the crack grew mostly parallel to the loading and the fiber direction. The unusual fatigue behavior of the (0)8 CT specimens is attributed to the specimen geometry and the associated high tensile bending stresses perpendicular to the fiber direction.

Kantzos, Peter↗

NASA NTRS1989

Fatigue crack growth in a unidirectional SCS-6/Ti-15-3 composite

An investigation was conducted to characterize and model the fatigue crack growth (FCG) behavior of a SCS-6/Ti-15-3 metal matrix composite. Part of the study was conducted using a fatigue loading stage mounted inside a scanning electron microscope (SEM). This unique facility allowed high magnification viewing of the composite fatigue processes and measurement of the near crack tip displacements. The unidirectional composite was tested in the (0)8 (i.e., longitudinal) and (90)8 (i.e., transverse) orientations. For comparison purposes unreinforced matrix material produced by the identical process as the reinforced material was also tested. The results of the study reveal that the fatigue crack growth behavior of the composite is a function of specimen geometry, fiber orientation and the interaction of local stress fields with the highly anisotropic composite. In the case of (0)8 oriented single edge notch (SEN) specimens and (90)8 oriented compact tension (CT) specimens, the crack growth was normal to the loading direction. However, for the (0)8 CT specimens the crack grew mostly parallel to the loading and the fiber direction. The unusual fatigue behavior of the (0)8 CT specimens was attributed to the specimen geometry and the associated high tensile bending stresses perpendicular to the fiber direction. These stresses resulted in preferential cracking in the weak interface region perpendicular to the fiber direction. The interface region, and in particular the carbon coating surrounding the fiber proved to be the composites weakest link. In the (0)8 SEN the crack growth was confined to the matrix leaving behind unbroken fibers which bridged the cracked surfaces. As the crack grew longer, more fibers bridged the crack resulting in a progressive decrease in the crack growth rates and eventual crack arrest. The actual near crack tip displacement measurements were used in a proposed formulation for a bridging-corrected effective crack driving force, delta K(sub eff). This parameter was able to account for most of the experienced bridging and correlated the (0)8 SEN fatigue crack growth data reasonably well.

Kantzos, Peter↗

NASA NTRS1988

Mode 2 fracture mechanics

Current development of high-performance rolling element bearings for aircraft engines (up to 3 million DN, where DN is the product of shaft diameter in millimeters and speed in revolutions per minute) has aroused concern about fatigue crack growth in the inner bearing race that leads to catastrophic failure of the bearing and the engine. A failure sequence was postulated by Srawley, and an analytical program was undertaken to simulate fatigue crack propagation in the inner raceway of such a bearing. A fatigue specimen was developed at NASA by which fatigue data may be obtained relative to the cracking problems. The specimen may be used to obtain either mode 2 data alone or a combination of mixed-mode (1 and 2) data as well and was calibrated in this regard. Mixed-mode fracture data for M-50 bearing steel are presented, and a method for performing reversed-loading tests is described.

Buzzard, Robert J.↗

NASA NTRS1988

Accelerated crack growth rate at low Delta K in a single crystal superalloy

The low Delta K crack growth behavior of a single crystal of the PWA 1480 nickel-based superalloy was investigated. The crystal was tested in the near (100) orientation with the side faces being in the near (001) orientation. Although in the higher Delta K region the fatigue crack growth (FCG) behavior is rather normal, at Delta K of about 8 MPa sq rt m, a transition occurs where the FCG rate appears to be independent of Delta K. This region is found to continue until Delta K of about 2.5 MPa sq rt m, where the FCG rate again decreases with decreasing Delta K.

Telesman, Jack↗