Halide perovskites as disposable epitaxial templates for the phase-selective synthesis of lead sulfochloride nanocrystals
Colloidal chemistry grants access to a wealth of materials through simple and mild reactions. However, even few elements can combine in a variety of stoichiometries and structures, potentially resulting in impurities or even wrong products. Similar issues have been long addressed in organic chemistry by using reaction-directing groups, that are added to a substrate to promote a specific product and are later removed. Inspired by such approach, we demonstrate the use of CsPbCl 3 perovskite nanocrystals to drive the phase-selective synthesis of two yet unexplored lead sulfochlorides: Pb 3 S 2 Cl 2 and Pb 4 S 3 Cl 2 . When homogeneously nucleated in solution, lead sulfochlorides form Pb 3 S 2 Cl 2 nanocrystals. Conversely, the presence of CsPbCl 3 triggers the formation of Pb 4 S 3 Cl 2 /CsPbCl 3 epitaxial heterostructures. The phase selectivity is guaranteed by the continuity of the cationic subnetwork across the interface, a condition not met in a hypothetical Pb 3 S 2 Cl 2 /CsPbCl 3 heterostructure. The perovskite domain is then etched, delivering phase-pure Pb 4 S 3 Cl 2 nanocrystals that could not be synthesized directly.
Stable CsPbBr 3 Nanoclusters Feature a Disk-like Shape and a Distorted Orthorhombic Structure
CsPbBr 3 nanoclusters have been synthesized by several groups and mostly employed as single-source precursors for the synthesis of anisotropic perovskite nanostructures or perovskite-based heterostructures. Yet, a detailed characterization of such clusters is still lacking due to their high instability. In this work, we were able to stabilize CsPbBr 3 nanoclusters by carefully selecting ad hoc ligands (benzoic acid together with oleylamine) to passivate their surface. The clusters have a narrow absorption peak at 400 nm, a band-edge emission peaked at 410 nm at room temperature, and their composition is identified as CsPbBr 2.3 . Synchrotron X-ray pair distribution function measurements indicate that the clusters exhibit a disk-like shape with a thickness smaller than 2 nm and a diameter of 13 nm, and their crystal structure is a highly distorted orthorhombic CsPbBr 3 . Based on small- and wide-angle X-ray scattering analyses, the clusters tend to form a two-dimensional (2D) hexagonal packing with a short-range order and a lamellar packing with a long-range order.
Multilayer Diffraction Reveals That Colloidal Superlattices Approach the Structural Perfection of Single Crystals
Not Available